防水用聚脲绝缘涂料的制备及性能研究

doi:10.11896/j.issn.1005-023X.2018.16.004

Abstract
Figure/Table
References
Related Citation (9)

Download:

Full Text ( PDF ) (3162KB)
Export: BibTeX | EndNote (RIS)

Abstract A polyurea waterproof coating were prepared from HDI trimer, modified D2000 and chain extender such as E300 as raw materials. By adjusting the molar ratio of modified D2000 and chain extender, the optimum synthesis process were studied. The FT-IR results have showed the modification mechanism of amino terminated polyether and molecular structure of polyurea coating. It was found that the polyurea coating had excellent water resistance and waterproof performance by comparing the volume resistivity of the coating before and after immersion in 50 ℃ water and after drying. The breakdown voltage, hardness and tensile strength test showed that the insulation performance and mechanical strength of the polyurea coating were increased with the increasing of hard content, and the polyurea of E300 as the chain extender were better on comprehensive performance than others. Combing with the elongation at break test found that when the molar fraction of E300 is 86%, the coating has good ductility and the elongation at break is 28.72%. At this time, the volume resistivity of coating film is 8.2×10¹⁰ Ω·m, breakdown field strength of coating film is 96.73 kV/mm, Shore hardness of coating film is 52.

Key words： polyurea coatings water resistance insulation performance mechanical behavior

Published: 18 September 2018

CLC number:

TM215.3

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	LUO Xueyu
	LIU Lizhu

Cite this article:

LUO Xueyu,LIU Lizhu. Preparation of Polyurea Insulation Coating for Waterproofing and Its Properties[J]. Materials Reports, 2018, 32(16): 2723-2727.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2018.16.004 OR http://www.mater-rep.com/EN/Y2018/V32/I16/2723

1 Wang Y, Zhang D L. The new concept of thermal endurance of electrical insulation system [J]. Large Electric Machine and Hydraulic Turbine,2009(4):30(in Chinese).
王洋,张东林.电气绝缘系统及绝缘材料耐热性的新概念[J].大电机技术,2009(4):30.
2 Haung Y, Li Y X. Aqueous impregnating varnishes for insulation [J]. Insulating Material,2003(3):46(in Chinese).
黄愔,李耀星.水基绝缘浸渍漆[J].绝缘材料,2003(3):46.
3 Zhang L L.The research and application about the weathering pol-yurea coatings [D]. Guangzhou: South China University of Techno-logy,2015(in Chinese).
张伶俐.耐候性聚脲涂料研发及应用[D].广州:华南理工大学,2015.
4 Toutanji H A, Choi H, Wong D, et al. Applying a polyurea coating to high performance organic cementitious materials [J]. Construction and Building Materials,2013,38:1170.
5 Huang W B, Lv P. Dependence of dynamic mechanical property and morphology of polyaspartic esters based polyurea on curing temperature [J]. Polymer Materials Science and Engineering,2010,26(3):72(in Chinese).
黄微波,吕平.聚天冬氮酸酯聚脲的动态力学性质及结构形态的温度依赖性[J].高分子材料科学与工程,2010,26(3):72.
6 Wu S. Polyurea composition suitable for a golf ball cover: US,5484870 [P].1996-01-16.
7 Wicks D A, Yeske P E. Polyurea coating co-mpositions having improved pot lives: US,5243012 [P].1993-09-07.
8 Xu F. Study on adhesion properties of polyurea coatings for metal protection [D]. Qingdao: Qingdao Technological University,2014(in Chinese).
徐菲.金属防护用聚脲涂层附着性能研究[D].青岛:青岛理工大学,2014.
9 Primeau D J. A study of polyurea spray elastomer system [J]. High Solid Coatings,1994,15:2.
10 Hai N, William J, Allen D, et al. Polyurea/polysiloxane ceramer coatings [J]. Progress in Organic Coatings,2000,38(2):97.
11 Xue L, Mock W, Belytschko T. Penetration of DH-36 steel plates with and without polyurea coating [J]. Mechanics of Materials,2010,42(11):981.
12 Zwiener C, Pedain J, Kahl L.Process for the production of polyurethane coatings: US,5126170 [P].1992-06-30.
13 Richard R R, Edward P S. Improved polyurea coating from dimethy-substituted polyaspartic estermixtures: US,6458293B1 [P].2002-10-01.
14 Shenoy M A, D’Melo D J. Effect of crosslinking density on coating properties of a polyurea coating system [J]. Surface Coatings International Part B: Coatings Transactions,2006,89(3):221.
15 Lv P, Cheng G H, Huang W B. Aliphatic polyurea coating based on novel polyaspartic ester [J]. Polymer Materials Science and Engineering,2007,23(3):55(in Chinese).
吕平,陈国华,黄微波.新型聚天门冬氨酸酯合成脂肪族聚脲涂层[J].高分子材料科学与工程,2007,23(3):55.
16 Yang J, Wang G Y, Hu C P. Morphology and mechanical properties of aliphatic polyurea with different hard segment contents [J]. Acta Polymer Sinica,2003(6):794(in Chinese).
杨娟,王贵友,胡春圃.不同硬段含量脂肪族聚脲的结构与性能研究[J].高分子学报,2003(6):794.
17 Priya R, Nirav J. Synthesis and characterization of polyurea resin for dielectric coating applications [J]. Polymer Plastics Technology and Engineering,2016,16:55.
18 Hu X. Research on properties of polyura and its matched coating applied on outdoor swimming pool [D]. Qingdao: Qingdao Technolo-gical University,2014(in Chinese).
胡晓.户外泳池防护用聚脲涂层及其面漆的性能研究[D].青岛: 青岛理工大学,2013.
19 Guo C. Polyurea anticorrosion coating in desalination project [D]. Beijing: Beijing University of Chemical Technology,2014(in Chinese).
郭辰.海水淡化工程用聚脲防腐涂层体系的研制[D].北京:北京化工大学,2014.
20 Liu P L, Liu G Y, Huang W B. Preparation and study of polyaspartic polyurea [J]. Polyurethane Industry,2005,20(4):16(in Chinese).
刘培礼,刘光晔,黄微波.聚天门冬氨酸酯聚脲的制备与研究[J].聚氨酯工业,2005,20(4):16.