Stellite12钴基合金热循环冲击前后拉伸断裂机理研究

doi:10.11896/j.issn.1005-023X.2017.024.031

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (750KB)
Export: BibTeX | EndNote (RIS)

Abstract By means of in-situ tensile tests of Stellite12 cobalt-based alloy (after the thermal cycling shock at 700 ℃ / 20 ℃ for different times and unshocked) with different notch size, in combination with the analysis of experiment data and SEM observation of fracture, the tensile fracture process and fracture mechanism were investigated before and after thermal cycling shock of Stellite12 cobalt-based alloy. The result of in-situ tensile experiment reveals that after the thermal cycling, the fracture process of specimen with different size notch has a little difference. There were micro surface cracks on the root of small circular notch specimen and many oxydic micropores on the specimen edge and side of the cracks after thermal cycling. When the sample experienced in-situ tensile test, cracks extended in the direction of the thickness of the specimen firstly on the process of thermal shock, to be connected in thickness direction, and then the substrate phase of the crack tip deformation occurred, black phase (white phase) transgranular cracking, oxydic micropores expanding, specimen instantaneously fracturing in the end. But the great circle specimen after thermal cycling shock generated no obvious crack on the surface. During in-situ tensile test, the substrate phase of the crack tip deformation occurred, with black phase (white phase) transgranular cracking, oxydic micropores expanding, specimen instantaneously fracturing. While, the original unshocked specimen experienced deformation, transgranular cracking and fracture when energy accumulating. Three kinds of original specimens are similar to the process of fracture because the stress concentration of the small arc radius specimen is bigger, so as to make its fracture stress lower than the tablet and the great circle sample.

Key words： cobalt-based alloy in-situ tensile thermal cycling shock fracture

Published: 08 May 2018

CLC number:

TG146.1

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	ZHANG Haiyan
	CAO Rui
	CHE Hongyan
	LIU Guohui
	CHEN Jianhong

Cite this article:

ZHANG Haiyan,CAO Rui,CHE Hongyan, et al. Investigation of Fracture Mechanism Before and After Thermal Cycling Stellite12 Cobalt-based Alloy with Tensile Tests[J]. Materials Reports, 2017, 31(24): 156-160.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2017.024.031 OR http://www.mater-rep.com/EN/Y2017/V31/I24/156

1 Zhang Zhongjian, Zhao Shengzhi, Peng Wen, et al. Behavior of fatigue crack initiation and propagation of cemented carbides[J]. Chin J Nonferrous Metals,2014,24(12):3031(in Chinese).
张忠健,赵声志,彭文,等. 硬质合金疲劳裂纹的萌生与扩展行为[J]. 中国有色金属学报,2014,24(12):3031.
2 Baik S I, Choi E G, Jun J H, et al. Defect structure induced by iron injection in WC-Co[J]. Scr Mater, 2008,58:614.
3 Abdel-Aal H A, Nouari M, Mansori M E. The effect of thermal property degradation on wear of WC-Co inserts in dry cutting[J]. Wear, 2008,265:1670.
4 Yilbas B S, Arif A F M, Karatas C, et al. Cemented carbide cutting tool: Laster processing and thermal stress analysis[J]. Appl Surf Sci, 2007,253:5544.
5 Jiang W H, Guan H R, Hu Z Q. Development of a heat treatment for a directionally solidified cobalt-base superalloy[J]. Metall Mater Trans A,1999,30:2251.
6 Xu Shengqian, Chen Zhenhua, Zhang Zhongjian, et al. Study on thermo-mechanical-corrosion fatigue behaviour of cemented carbides[J]. Cenmented Carbide, 2013,30(3):161(in Chinese).
徐盛乾,陈振华,张忠健,等. WC-热机械腐蚀疲劳性能的研究[J]. 硬质合金,2013,30(3):161.
7 Zhang Xi, Gao Wei. Research on structure and wear resistance of cobalt-based alloy plasma surfacing welding layer[J]. Hot Working Technol, 2014,43(23):21(in Chinese).
张希,高伟. 钴基合金等离子堆焊层组织及耐磨性研究[J].热加工工艺,2014,43(23):21.
8 Schleinkofer U, Soekel H G. Fatigue of hard metals and cermets[J]. Mater Sci Eng A,1996,209:313.
9 Torres T, Anglada M. Fatigue mechanics of WC-Co cemented carbides[J].Int J Refractory Metals Hard Mater, 2001,19:341.
10Chen Zhenhua, Jang Yong, Chen Ding, et al. Fatigue and fracture of cemented carbides[J]. Chin J Nonferrous Metals,2011,21(10):2394(in Chinese).
陈振华,姜勇,陈鼎,等. 硬质合金的疲劳与断裂[J].中国有色金属学报,2011,21(10):2394.
11Guo Shengda, Zhang Zhengfu. Study on fatigue property of WC-Co cemented carbide[J]. Mater Rev: Rev, 2009,23(6):69(in Chinese).
郭圣达,张正富. WC-Co类硬质合金疲劳特性研究现状[J].材料导报:综述篇,2009,23(6):69.
12Ding Y, Wang C Q, Tian Y, et al. Influence of aging treatment on deformation behavior of 96.5Sn3.5Ag lead-free solder alloy during in situ tensile tests[J]. J Alloys Compd, 2007,428:274.
13Oh S H, Legros M, Kiener D, et al. In situ observation of dislocation nucleation and escape in a submicrometre aluminium single crystal[J]. Nat Mater, 2006,8(2):95.
14Cao Rui, Lin Youzhi, Chen Jianhong, et al. Fracture process and fracture mechanism in fully lamellar TiAl alloys with tensile tests[J]. Chin J Mech Eng, 2008,44(1):40(in Chinese).
曹睿,林有智,陈剑虹,等. 全层状TiAl基合金拉伸试验断裂过程及机理[J]. 机械工程学报,2008,44(1):40.
15Huang Daoyuan. Microstructures, properties, and mechanisms of Co-based cemented carbides under external heat/load conditions[D]. Changsha: Central South University,2010(in Chinese).
黄道远. 热/力作用下钴基硬质合金组织性能变化及相关机理的研究[D].长沙:中南大学,2010.
16Cao Rui, Chen Jianhong, Zhang Ji,et al. Fracture mechanisms of intermetallic TiAl alloys[J]. Chin J Rare Metals, 2004(5):894(in Chinese).
曹睿,陈剑虹,张继,等. 金属间化合物TiAl合金的缺口断裂机制研究[J]. 稀有金属,2004(5):894.
17Jiang Yong. Understanding the fatigue behavior of WC-Co based cemented carbide and stress analysis method[D]. Changsha: Hunan University,2011:17(in Chinese).
姜勇. WC-Co类硬质合金的疲劳性能及应力分析方法的研究[D].长沙: 湖南大学,2011.