预分解磷石膏制备贝利特-硫铝酸盐水泥

doi:10.11896/j.issn.1005-023X.2017.024.001

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (2003KB)
Export: BibTeX | EndNote (RIS)

Abstract The decomposition characteristics of phosphogypsum (PG) in reductive atmosphere at low temperature and oxidizing atmosphere at high temperature were investigated. The decomposed phosphogypsum as a calcium source in place of limestone was used to prepare belite-calcium sulphoaluminate cement. The results showed that the decomposition rate of PG with the ratio of C/S=2 could reach 87.69% with the calcining process of CO₂-950 ℃-1 h/air-1 200 ℃-1 h. SO₂ could be controlled to concentratedly release in the temperature range of 900－1 200 ℃.The decomposed PG with the decomposition rate of 87.69% was used to prepare BCSA cement. C₂AS was detected in the cement clinker except for C₄A₃, C₂S and C₄AF. The compressive strength of cement paste at 3 d could reach 41.4 MPa. About 0.98 t phosphogypsum is consumed for 1 t BCSA cement clinker, reducing the amount of limestone nearly 50%.

Key words： decomposed phosphogypsum decomposition characteristics piecewise calcination belite-calcium sulphoaluminate cement

Published: 08 May 2018

CLC number:

TU52

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	LIANG Jiao
	CHU Wanyi
	HUANG Yongbo
	LI Fengling
	LIU Na
	QIAN Jueshi

Cite this article:

LIANG Jiao,CHU Wanyi,HUANG Yongbo, et al. Utilizing Decomposed Phosphogypsum for the Preparation of Belite-Calcium Sulphoaluminate Cement[J]. Materials Reports, 2017, 31(24): 1-5.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2017.024.001 OR http://www.mater-rep.com/EN/Y2017/V31/I24/1

1 Pérez-López R, Alvarez-Valero A M, Nieto J M. Changes in mobility of toxic elements during the production of phosphoric acid in the fertilizer industry of Huelva (SW Spain) and environmental impact of phosphogypsum wastes[J]. J Hazard Mater, 2007,148(3):745.
2 Yang X, Zhang Z, Wang X, et al. Thermodynamic study of phosphogypsum decomposition by sulfur[J]. J Chem Thermodyn, 2013,57(1):39.
3 State Development,Reform Commission. The national development and reform commission(2014)[J]. Recy Res Cir Eco, 2014,7(10):2(in Chinese).
国家发展和改革委员会. 中国资源综合利用年度报告(2014)[J]. 再生资源与循环经济, 2014,7(10):2.
4 Tayibi H, Choura M, López F A, et al. Environ mental impact and management of phosphogypsum[J]. J Environ Manage, 2009,90(8):2377.
5 Shen Y, Qian J, Chai J, et al. Calcium sulphoaluminate cements made with phosphogypsum: Production issues and material properties[J]. Cem Concr Compos, 2014,48(4):67.
6 Tomaszewska M. Concentration of the extraction fluid from sulfuric acid treatment of phosphogypsum by membrane distillation[J]. J Membr Sci, 1993,78(3):277.
7 Ma L, Ning P, Zheng S, et al. Reaction mechanism and kinetic analysis of the decomposition of phosphogypsum via a solid-state reaction[J]. Ind Eng Chem Res, 2010,49(8):3597.
8 Xiao H P, Zhou J H, Cao X Y, et al. Experiments and model of the decomposition of CaSO₄ under CO atmosphere[J]. J Fuel Chem Technol, 2005,33:151.
9 Li J X, Shu Y Z, Tang S L, et al. Feasibility analysis of cement production technique with the dry method in the new process for acid production from phosphogypsum[J]. Bull Chin Ceram Soc, 2009,28(3):563(in Chinese).
李建锡, 舒艺周, 唐霜露,等. 新型干法预分解磷石膏制硫酸联产水泥可行性分析[J]. 硅酸盐通报, 2009,28(3):563.
10Chai J Q, Zhang J, Shen Y, et al. Effect of phosphogypsum pyrolysis in sintering clinker on properties of sulphoaluminate cement[J]. Non Met Min, 2013,36(6):1(in Chinese).
柴俊青, 张健, 沈燕,等. 磷石膏高温分解对烧制硫铝酸盐水泥性能的影响[J]. 非金属矿, 2013,36(6):1.
11Li J X, Yu S, Ma L P, et al. Thermal analysis of phosphogypsum decomposition[J]. J Environ Eng, 2009, 3(10):1861(in Chinese).
李建锡, 余苏, 马丽萍,等. 磷石膏预分解的热分析研究[J]. 环境工程学报, 2009, 3(10):1861.
12Zheng S C, Ma L P, Ning P, et al. Thermal decomposition kinetics of phosphogypsum reduced with high sulfur coal[J]. J Wuhan Univ Technol, 2010,32(5):109(in Chinese).
郑绍聪, 马丽萍, 宁平,等. 高硫煤还原磷石膏的热分解动力学[J]. 武汉理工大学学报, 2010,32(5):109.
13Jagtap S B, Wheelock T D. Regeneration of sulfided calcium-based sorbents by a cyclic process[J]. Energy Fuels, 1996,10(3):821.
14Yan X, Ma L, Zhu B, et al. Reaction mechanism process analysis with phosphogypsum decomposition in multiatmosphere control[J]. Ind Eng Chem Res, 2014,53(50):19453.
15Zhu K, Xie G L, Chen Z R, et al. Reaction characteristics of phosphogypsum under carbon monoxide atmosphere[J]. J Chin Ceram Soc, 2013,41(11):1540(in Chinese).
朱凯, 解桂林, 陈昭睿,等. 磷石膏在一氧化碳气氛下的还原反应特性[J]. 硅酸盐学报, 2013,41(11):1540.
16Ezzedine K, Malvy D, Mauger E, et al. Hydration behavior of C₂S and C₂AS nanomaterials, synthetized by sol-gel method[J]. J Therm Anal Calorim, 2006,86(3):595.
17Benarchid M Y, Rogez J. The effect of Cr₂O₃ and P₂O₅ additions on the phase transformations during the formation of calciumsulfoaluminate C₄A₃[J]. Cem Concr Res, 2005,35(11):2074.
18Huang Y, Qian J, Liang J, et al. Characterization and calorimetric study of early-age hydration behaviors of synthetic ye’elimite doped with the impurities in phosphogypsum[J]. J Therm Anal Calorim, 2015,123(2):1.
19Chae W H, Yum G C, Oh H K, et al. The effects of additives on formation of C₂S, C₄A₃S and C₄AF[C]∥Proceedings of the 10th ICCC. Gothenburg, Sweden, 1997.