超声冲击对高速列车转向架焊接十字接头超高周疲劳性能的影响<sup>*</sup>

doi:10.11896/j.issn.1005-023X.2017.020.017

Abstract
Figure/Table
References
Related Citation (2)

Download:

Full Text ( PDF ) (1875KB)
Export: BibTeX | EndNote (RIS)

Abstract To address the fatigue problem occurring to the bogie of high-speed train in the practical application, the weld toes were treated by HJ-Ⅲ type ultrasonic impact treatment device at room temperature, in order to investigate the effect of ultrasonic impact treatment (UIT) on very high cycle fatigue (VHCF) behavior of welded SAM490BW cross joint of high-speed train bogie. The results indicated that the S-N curves of as-welded and UIT specimens exhibit a plateau beyond 10⁷cycles. Compared with the as-welded joints, the degree of improvement of VHCF performance of SAM490BW steel cross welded joint treated was up to 25%. There were several crack initiation locations on the fracture surface for as-welded samples, whereas, there was only one crack source for UIT specimens. The concentration coefficient of the welded joints toes decreased by 32.4% after UIT, the crack initiation probability was reduced. Residual tensile stress could be significantly reduced by UIT and residual compressive stress was induced on surface of welded joints toe, up to -255.5 MPa. A surface layer of nanocrystalline microstructure could be produced, the average grain size was less than 100 nm. Crack propagation path, in plastic deformation region, could get longer by implementing the UIT.

Key words： bogie weld joint ultrasonic impact treatment very high cycle fatigue performance high-speed train

Published: 05 May 2018

CLC number:	U270.331
	U270.41
	TG457.11

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	LU Zongmin
	HE Bolin
	YU Yingxia

Cite this article:

LU Zongmin,HE Bolin,YU Yingxia. Influence of Ultrasonic Impact on the Very High Cycle Fatigue Properties of Welded Cross Joint for High-speed Train Bogie[J]. Materials Reports, 2017, 31(20): 77-81.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2017.020.017 OR http://www.mater-rep.com/EN/Y2017/V31/I20/77

1 Qin Guodong, Liu Zhiming, Cui Erguang, et al. Practical analysis method for fatigue life of welded frame of speed-up bogie[J]. China Railway Sci, 2004,25(1):46(in Chinese).
秦国栋, 刘志明, 崔二光, 等. 提速转向架焊接构架疲劳寿命的实用分析方法[J]. 中国铁道科学, 2004,25(1):46.
2 Malaki M, Ding H T. A review of ultrasonic peening treatment[J]. Mater Des, 2015,87:1072.
3 Ye Xionglin, Zhu Youli, Ma Lili, et al. Fatigue performance improvement of 22SiMn2TiB steel welded joint by ultrasonic impact treatment[J]. J Mech Eng, 2009,45(8):283(in Chinese).
叶雄林, 朱有利, 马丽丽, 等. 超声冲击处理改善22SiMn2TiB钢焊接接头的疲劳性能[J]. 机械工程学报, 2009,45(8):283.
4 Mori T, Shimanuki H, Tanaka M. Effect of UIT on fatigue strength of web-gusset welded joints considering service condition of steel structures[J]. Welding World, 2012,56:141.
5 Zhu Youli, Li Zhanming, He Jiawu, et al. Microstructure changes of 2A12 aluminum alloy weld bead surface layer by ultrasonic impact treatment[J]. J Mater Eng, 2009,35(7):79(in Chinese).
朱有利, 李占明, 何嘉武, 等. 超声冲击处理2A12 铝合金焊缝表层微观组织结构变化[J]. 材料工程, 2009,35(7):79.
6 Deng Caiyan, Liu Xi, Wang Dongpo. Fatigue performance of Q345 steel welded joints by high temperature ultrasonic peening[J]. Trans China Welding Institution, 2014,35(11):47.
7 邓彩艳, 刘夕, 王东坡. 高温超声冲击处理Q345钢焊接接头的疲劳性能[J]. 焊接学报, 2014,35(11):47.
8 He Bolin, Yu Yingxia, Shi Jianping, et al. The effect of ultrasonic impact on the fatigue properties of 16MnR steel welded joints for bogie[J]. China Railway Sci, 2011,32(5):96(in Chinese).
何柏林, 于影霞, 史建平, 等. 超声冲击对转向架用16MnR钢焊接接头疲劳性能的影响[J]. 中国铁道科学, 2011,32(5):96.
9 Wang Dongpo, Zhou Da. Mechanism analysis of fatigue strength improvement of welded joints by ultrasonic peening method[J]. J Tianjin University, 2007,40(5):623(in Chinese).
王东坡, 周达. 超声冲击法提高焊接接头疲劳强度的机理分析[J]. 天津大学学报, 2007,40(5):623.
10He Bolin, Yu Yingxia, Yu Huanghuang, et al. Effect of ultrasonic impact on the surface microstructure and fatigue properties of welded cross joint for train bogie[J]. Trans China Welding Institution, 2013,34(8):51(in Chinese).
何柏林, 于影霞, 余皇皇, 等. 超声冲击对转向架焊接十字接头表层组织及疲劳性能的影响[J]. 焊接学报, 2013,34(8):51.
11Radaj D, Sonsino C M, Fricke W. Fatigue assessment of welded joints by local approaches[M]. 2th ed. Cambridge: Woodhead Publishing, 2006.
12Neuber H. Theory of notch stresses[M]. 2th ed. Berlin: Springer-Verlag, 1958.
13Moore H F. A study of size effect and notch-sensitivity in fatigue tests of steel[C]∥ Proceedings of American Society for Testing Materials, 1945: 507.
14Pilkey W D, Pilkey D F. Peterson′s stress concentration factors [M]. 3th ed. New York: John Wiley & Sons, 2008: 35.
15Gao Wenbin, Wang Dongpo, Cheng Fangjie, et al. Enhancement of the fatigue strength of underwater wet welds by grinding and ultrasonic impact treatment[J]. J Mater Process Technol, 2015,223: 305.
16Li Huimin, Li Miaoquan, Liu Yingang, et al. Research progress in nanocrystalline microstructure, mechanical properties and nanocrystallization mechanism of titanium alloys via surface mechanical treatment[J]. Chin J Nonferrous Metals, 2015,25(3):641(in Chinese).
李慧敏, 李淼泉, 刘印刚, 等. 钛合金表层机械处理的纳米化组织、力学性能与机理研究进展[J]. 中国有色金属学报, 2015,25(3):641.