基于C(t)积分及参数Ac的P92钢高温蠕变裂纹扩展研究*

doi:10.11896/j.issn.1005-023X.2017.018.028

Abstract
Figure/Table
References
Related Citation (1)

Download:

Full Text ( PDF ) (1528KB)
Export: BibTeX | EndNote (RIS)

Abstract Creep crack growth is a major failure mechanism of components working under high temperature, and the constraint effect at the crack tip has significant influence on the creep crack growth rate. The C(t) integral, which represents the stress and strain rate field at the crack tip, was investigated by simulations. The influence of the constraint effect of P92 steel on the creep crack growth was studied based on the parameter A_c using finite element analysis, and the result of which was compared with experimental data. Firstly, the results showed that the value of the C(t) integral decreased sharply as the crack propagated and the C(t) integral was affected by the distance from the crack tip strongly and was affected by the constraint effect to some extent. Secondly, the study indicated that the constraint effect had an influence on the creep crack growth rate and a higher constraint resulted in a faster creep crack growth rate. Finally, it was testified that the parameter A_c was effective in evaluating the constraint level at the crack tip. The utilization of parameter A_c in predicting the service life needed further exploration, which had a great significance in evaluating the lifetime of the defected components working under high temperature.

Key words： creep crack growth constraint effect A_c C(t) integral P92 steel

Published: 08 May 2018

CLC number:

TG142.73

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	TIAN Lanlan
	LIU Jun
	HE Bin
	CHEN Jianen
	WANG Xiaofeng
	GE Weimin

Cite this article:

TIAN Lanlan,LIU Jun,HE Bin, et al. Investigation of Creep Crack Growth of the P92 Steel Under High Temperature Based on the C(t) Integral and Parameter A_c[J]. Materials Reports, 2017, 31(18): 141-145.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2017.018.028 OR http://www.mater-rep.com/EN/Y2017/V31/I18/141

1 Zhao L, Jing H Y, Xiu J J, et al. Experimental investigation of specimen size effect on creep crack growth behavior in P92 steel welded joint[J]. Mater Des, 2014,57:736.
2 Zhao L, Jing H Y, Xu L Y, et al. Analysis of creep crack growth behavior of P92 steel welded joint by experiment and numerical si-mulation [J]. Mater Sci Eng A, 2012,558:119.
3 Shlyannikov V N, Boychenko N V, Tartygasheva A M. In-plane and out-of-plane crack-tip constraint effects under biaxial nonlinear deformation [J]. Eng Fracture Mech, 2011,78(8SI):1771.
4 Ma H S, Wang G Z, Liu S, et al. In-plane and out-of-plane unified constraint-dependent creep crack growth rate of 316H steel[J]. Eng Fracture Mech, 2016,155:88.
5 O′Dowd N P, Shih C F. Family of crack-tip fields characterized by a triaxiality parameter. Ⅰ. Structure of fields[J]. J Mech Phys So-lids, 1991,39(8):989.
6 Budden P J, Ainsworth R A. The effect of constraint on creep fracture assessments [J]. Int J Fracture, 1999,97(1-4):237.
7 Zhao L, Jing H Y, Xu L Y, et al. Evaluation of constraint effects on creep crack growth by experimental investigation and numerical si-mulation [J]. Eng Fracture Mech, 2012,96:251.
8 Wang G Z, Liu X L, Xuan F Z,et al. Effect of constraint induced by crack depth on creep crack-tip stress field in CT specimens[J]. Int J Solids Structures, 2010,47(1):51.
9 Yang S, Chao Y J, Sutton M A. Higher-order asymptotic crack-tip fields in a power-law creeping material[J]. Int J Solids Structures, 2001,38(21):3853.
10Xiang M J, Yu Z B, Guo W L. Characterization of three-dimensional crack border fields in creeping solids [J]. Int J Solids Structures, 2011,48(19):2695.
11Zhao L, Xu L Y, Han Y D, et al. Quantifying the constraint effect induced by specimen geometry on creep crack growth behavior in P92 steel[J]. Int J Mech Sci,2015,94-95: 63.
12Oh C S, Kim N H, Kim Y J, et al. Creep failure simulations of 316H at 550 ℃: Part Ⅰ Method and validation[J]. Eng J Fracture Mech, 2013,105:169.
13Yatomi M, Davies C M, Nikbin K M. Creep crack growth simulations in 316H stainless steel[J]. Eng Fracture Mech, 2008,75(18):5140.
14Oh C S, Kim Y J, Yoon K B, et al. The relationship between C_t and contour integrals under small-scale transient creep [J]. Eng Fracture Mech, 2010,77(3):565.
15ASTME1457-13.Standard test method for measurement of creep crack growth times and rates in metals[S]. United States: West Conshohocken: ASTM International, 2014.
16He Bin, Liu Jun, Chen Jianen, et al. Finite element simulation of high temperature creep crack growth rate of P92 steel with different constraints [J]. Mater Rev:Res, 2016,30(8):145(in Chinese)
何滨,刘军,陈建恩,等. 不同拘束条件下P92钢高温蠕变裂纹扩展速率的有限元模拟[J]. 材料导报:研究篇,2016,30(8):145.
17Song T K, Kim Y J, Nikbin K, et al. Estimation of the transient creep parameter C(t) under combined mechanical and thermal stresses[J]. Eng Fracture Mech, 2010,77(4):685.
18Wen Jianfeng.Strain-based damage mechanics model and its application to numerical simulations of creep crack growth[D].Shanghai: East China University of Science and Technology, 2014(in Chinese).
温建锋. 基于应变的损伤力学模型及其在蠕变裂纹扩展数值模拟中的应用[D]. 上海:华东理工大学,2014.
19Zhao Lei. Research on life assessment method considering constraint effect for P92 pipe with defects at elevated temperature[D].Tianjin: Tianjin University,2012(in Chinese).
赵雷.考虑拘束效应的高温下含缺陷P92管道寿命评估方法研究[D].天津:天津大学, 2012.