碱激发材料氯离子传输性能测试方法及影响因素研究进展<sup>*</sup>

doi:10.11896/j.issn.1005-023X.2017.015.014

Abstract
Figure/Table
References
Related Citation (14)

Download:

Full Text ( PDF ) (1456KB)
Export: BibTeX | EndNote (RIS)

Abstract The transportation of chloride ions within cement-based materials is a complicated process. In this paper, the mecha-nism for transportation of chloride ions and the testing methods for Portland cement system are introduced firstly. On that basis, the factors influencing the chloride transportation of alkali-activated materials and the testing methods for chloride transportation properties of alkali-activated materials are reviewed. The type of activators, slag content, alkali dosage and modulus of water-glass is closely related to the chloride penetration resistance of alkali-activated materials. The high alkalinity and complex chemical composition of pore solution of alkali-activated materials hinders the application of rapid chloride penetration test, whose measurements are affected by composition and concentration in pore solution of testing samples. The natural diffusion test is a time-consumption method, which is not commonly used in practical. Unsteady electromigration test is widely applied to rapid determination of the chloride penetration resistance of Portland cement system. However, due to the different alkalinity of materials, the chloride concentration at color change boundary of Portland cement system varies from that of alkali-activated materials. Therefore, the preparation of test samples and the chloride concentration at color change boundary with silver nitrate colorimetric method in alkali-activated materials still need further study.

Key words： alkali-activated material chloride ion transport property testing method influencing factor

Published: 04 May 2018

CLC number:

TQ172

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	SHI Caijun
	ZHANG Liuyang
	ZHANG Jian
	LI Ning
	OU Zhihua

Cite this article:

SHI Caijun,ZHANG Liuyang,ZHANG Jian, et al. Advances in Testing Methods and Influencing Factors of Chloride Ion Transport Properties of Alkali-activated Materials[J]. Materials Reports, 2017, 31(15): 95-100.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2017.015.014 OR http://www.mater-rep.com/EN/Y2017/V31/I15/95

1 Shi C, Roy D, Krivenko P. Alkali-activated cements and concretes[M]. CRC Press,2006.
2 Shi C, Jiménez A F, Palomo A. New cements for the 21st century: The pursuit of an alternative to Portland cement[J]. Cem Concr Res,2011,41(7):750.
3 Provis J L, Palomo A, Shi C. Advances in understanding alkali-activated materials[J]. Cem Concr Res,2015,78:110.
4 Fernández-Jiménez A, Palomo J G, Puertas F. Alkali-activated slag mortars: Mechanical strength behaviour[J]. Cem Concr Res,1999,29(8):1313.
5 Bernal S A, Gutiérrez R M D, Provis J L. Engineering and durability properties of concretes based on alkali-activated granulated blast furnace slag/metakaolinblends[J]. Constr Building Mater,2012,33(7):99.
6 Puertas F, MartíNez-RamíRez S, Alonso S, et al. Alkali-activated fly ash/slag cements: Strength behaviour and hydration products[J]. Cem Concr Res,2000,30(10):1625.
7 Bernal S A, Gutiérrez R M D, Pedraza A L, et al. Effect of binder content on the performance of alkali-activated slag concretes[J]. Cem Concr Res,2011,41(1):1.
8 Pacheco-Torgal F,et al. Durability of alkali-activated binders: A clear advantage over Portland cement or an unproven issue?[J]. Constr Building Mater,2012,30(5):400.
9 Guerrieri M, Sanjayan J, Collins F. Residual strength properties of sodium silicate alkali activated slag paste exposed to elevated tempe-ratures[J]. Mater Struct,2010,43(6):765.
10 Puertas F, Palacios M, Gil-Maroto A, et al. Alkali-aggregate behaviour of alkali-activated slag mortars: Effect of aggregate type[J]. Cem Concr Compos,2009,31(5):277.
11 Shi C J, Deng D H, et al. Pore structure and chloride ion transport mechanisms in concrete[J]. Key Eng Mater,2006,302-303(3):528.
12 Streicher P E, Alexander M G. A critical evaluation of chloride diffusion test methods for concrete[C] ∥Proceedings of the third CANMET/ACI international conference on concrete durability. Nice, France,1994.
13 Stanish K D, Hooton R D, Thomas M D A. Testing the chloride penetration resistance of concrete: A literature review[R]. FHWA contract DTFH61.Canada:University of Toronto,1997:19.
14 Shi Caijun, Yuan Qiang, Deng Dehua, et al. Test methods for the transport of chloride ion in concrete[J]. J Chinese Ceram Soc,2007,35(4):522(in Chinese).
史才军, 元强, 邓德华,等. 混凝土中氯离子迁移特征的表征[J]. 硅酸盐学报,2007,35(4):522.
15 ASTM C1202. Electrical indication of concrete′s ability to resist chloride ion penetration [S]. Washington D C, USA: American Society for Testing and Materials,2000.
16 NORDTEST NT BUILD 492. Chloride migration coefficient from non-steady-state migration experiments [S]. Finland: Nordtest,1999.
17 NORDTEST NT BUILD 443. Accelerated chloride penetration [S].Finland: Nordtest,1995.
18 Shi C. Effect of supplementary cementing materials on the specific conductivity of pore solution and its implications on the rapid chloride permeability test(AASHTO T277and ASTM C1202) results[J]. Aci Mater J,1998, 95(4):389.
19 Shi C. Effect of mixing proportions of concrete on its electrical conductivity and the rapid chloride permeability test (ASTM C1202 or ASSHTO T277) results[J]. Cem Concr Res,2004,34(3):537.
20 Shi C. Strength, pore structure and permeability of alkali-activated slag mortars[J]. Cem Concr Res,1996, 26(12):1789.
21 Lloyd R R, Provis J L, Deventer J S J V. Pore solution composition and alkali diffusion in inorganic polymer cement[J]. Cem Concr Res,2010,40(9):1386.
22 Liu Xiaojin, Shi Caijun, et al. Study of hydration and microstructure of alkali-activated slag cement and portland cement by impedance spectroscopy[J]. Mater Rev:Res,2015,29(10):130(in Chinese).
刘小金, 史才军, 等. 用交流阻抗研究碱激发矿渣水泥与硅酸盐水泥的水化和微观结构[J]. 材料导报:研究篇, 2015,29(10):130.
23 Tang L, Nilsson L O. Rapid determination of the chloride diffusivity in concrete by applying an electrical field[J]. Am J Geriatric Psychia-try,1992,10(1):24.
24 AEC LABORATORY. Concrete testing, hardened concrete. Chloride penetration, APM 302, 2nd ed [S]. Vedbek, Denmark: AEC Laboratory,1991.
25 Ravikumar D, Neithalath N. Electrically induced chloride ion transport in alkali activated slag concretes and the influence of microstructure[J]. Cem Concr Res,2013,47(5):31.
26 Ravikumar D, Neithalath N. An electrical impedance investigation into the chloride ion transport resistance of alkali silicate powder activated slag concretes[J]. Cem Concr Compos,2013,44(44):58.
27 Tang L. Chloride transport in concrete—Measurement and prediction: Thèse[M]. Epfl,1996.
28 Otsuki N, Nagataki S, Nakashita K. Evaluation of the AgNO₃, solution spray method for measurement of chloride penetration into hardened cementitious matrix materials[J]. Constr Building Mater,1992,7(4):195.
29 Yuan Q, Deng D, Shi C, et al. Application of silver nitrate colorimetric method to non-steady-state diffusion test[J]. J Central South University,2012,19(10):2983.
30 He F, Shi C, Yuan Q, et al. AgNO₃ -based colorimetric methods for measurement of chloride penetration in concrete[J]. Constr Building Mater,2012,26(1):1.
31 Ismail I, Bernal S A, Provis J L, et al. Influence of fly ash on the water and chloride permeability of alkali-activated slag mortars and concretes[J]. Constr Building Mater,2013,48(11):1187.
32 Douglas E, Bilodeau A, Malhotra V M. Properties and durability of alkali-activated slag concrete[J]. Aci Mater J,1992,89(5):509.
33 Chen Qiao. Research on chloride ion permeability and reinforcement corrosion of alkali activated slag concrete[D]. Chongqing: Chongqing University,2008(in Chinese).
陈乔. 碱矿渣混凝土氯离子渗透及钢筋锈蚀性能研究[D]. 重庆:重庆大学,2008.
34 Chen Qiao, Cong Gang, Yang Changhui. The influences of mineral admixtures on chloride ion permeability in alkali activated slag concrete[J]. China Concr Cem Products,2008(3):11(in Chinese) .
陈乔, 丛钢, 杨长辉. 矿物掺合料对碱矿渣混凝土氯离子渗透性的影响[J]. 混凝土与水泥制品,2008(3):11.
35 Park J W, et al. Resistance of alkali-activated slag concrete to chloride-induced corrosion[J]. Adv Mater Sci Eng,2015,2015:1.
36 Mejia R, Delvasto S, Gutierrez C, et al. Chloride diffusion measured by a modified permeability test in normal and blended cements[J]. Adv Cem Res,2003,15(3):113.
37 ASTM C1543. Standard test method for determining the penetration of chloride ion into concrete by ponding[S]. Washington D C, USA: American Society for Testing and Materials,2010.
38 He F, Shi C, Yuan Q, et al. Calculation of chloride concentration at color change boundary of AgNO₃, colorimetric measurement[J]. Cem Concr Res,2011,41(11):1095.
39 Ma Q, Nanukuttan S V, Basheer P A M, et al. Chloride transport and the resulting corrosion of steel bars in alkali activated slag concretes[J]. Mater Struct,2016,49(9):1.
40 Zhu H, Zhang Z, Zhu Y, et al. Durability of alkali-activated fly ash concrete: Chloride penetration in pastes and mortars[J]. Constr Building Mater,2014,65(13):51.
41 Parˇízek L, Bílek V, Brˇezina M. Chloride resistance of alkali activated slag pastes with fly ash replacement[J].Mater Sci Forum,2016,851:98.
42 Yang T, Yao X, Zhang Z. Quantification of chloride diffusion in fly ash-slag-based geopolymers by X-ray fluorescence (XRF)[J]. Constr Building Mater,2014,69(11):109.
43 Liu Xiaojin. The study of hydration and microstructure of alkali-activated slag cements by impedance spectroscopy[D]. Changsha: Hunan University,2015(in Chinese).
刘小金. 用交流阻抗方法研究碱激发矿渣水泥浆体水化和微观结构[D]. 长沙:湖南大学,2015.
44 Wang S D, Scrivener K L, Pratt P L. Factors affecting the strength of alkali-activated slag[J]. Cem Concr Res, 1994, 24(6):1033.
45 Kim J C, Kim J K. Studies on the hydration of alkali activated slag [C]// Beijing International Symposium on Cement and Concrete.Beijing,1993.
46 Krizan D, Zivanovic B. Effects of dosage and modulus of water glass on early hydration of alkali-slag cements[J]. Cem Concr Res,2002,32(8):1181.
47 Bernal S A, Provis J L, Rose V, et al. Evolution of binder structure in sodium silicate-activated slag-metakaolinblends[J]. Cem Concr Compos,2011,33(1):46.
48 Ravikumar D, et al. Effects of activator characteristics on the reaction product formation in slag binders activated using alkali silicate powder and NaOH[J]. Cem Concr Compos,2012,34(7):809.