矿物掺合料对聚羧酸减水剂与水泥相容性的影响<sup>*</sup>

doi:10.11896/j.issn.1005-023X.2017.012.024

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (1481KB)
Export: BibTeX | EndNote (RIS)

Abstract Quick loss of fluidity and slump is commonly happened in concrete due to poor compatibility between superplasticizer and cement, which can be affected by the use of mineral admixtures. The effects of fly ash, slag and silica fume on fluidity of cement pastes, mortars and concretes were studied, and their effects on the content of polycarboxylate superplasticizer adsorbed on cement were tested by TOC method. Then, the compatibility between polycarboxylate superplasticizer and cement affected by fly ash, slag and silica fume was analysed. The results show that the beneficial impact of fly ash combined with slag on the fluidity of cement paste could be regarded as a superposition effect and quantified by the weighted average of the water-reducing rate. Silica fume has an adverse effect which is greater than the additional water-reducing effect of fly ash and slag on the fluidity of cement paste, which is unfavourable to the compatibility between polycarboxylate superplasticizer and cement. Fly ash and slag increase the effective adsorption content, resulting in good dispersion or high water reducing by polycarboxylate superplasticizer. There exists additional water-reducing effect induced by fly ash and slag in concrete but not obviously.

Key words： admixture polycarboxylate superplasticizer superimposed effect fluidity compatibility effective absorption content

Published: 08 May 2018

CLC number:

TU528.04

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	LI Zhikun
	PENG Jiahui
	YANG Zaifu

Cite this article:

LI Zhikun,PENG Jiahui,YANG Zaifu. Effect of Mineral Admixtures on the Compatibility of Polycarboxylate Superplasticizer and Cement[J]. Materials Reports, 2017, 31(12): 115-120.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2017.012.024 OR http://www.mater-rep.com/EN/Y2017/V31/I12/115

1 Ma B, Ma M, Shen X, et al. Compatibility between a polycarboxylate superplasticizer and the belite-rich sulfoaluminate cement: Setting time and the hydration properties [J]. Construct Build Mater,2014,51:47.
2 Bahurudeen A, Marckson A V, Kishore A, et al. Development of sugarcane bagasse ash based Portland pozzolana cement and evaluation of compatibility with superplasticizers[J]. Construct Build Mater,2014,68:465.
3 Nagrockiene D, Pundienè I, Kicaite A. The effect of cement type and plasticizer addition on concrete properties[J]. Construct Build Mater,2013,45:324.
4 Mardani-Aghabaglou A, Boyacc1 O C, Hosseinnezhad H, et al. Effe-ct of gypsum type on properties of cementitious materials containing high range water reducing admixture[J]. Cem Concr Compos,2016,68:15.
5 Mardani-Aghabaglou A, Tuyan M, Yc1lmaz G, et al. Effect of di-fferent types of superplasticizer on fresh, rheological and strength properties of self-consolidating concrete[J]. Construct Build Mater,2013,47:1020.
6 Alonso M M, Palacios M, Puertas F. Compatibility between polycarboxylate-based admixtures and blended-cement pastes[J]. Cem Concr Compos,2013,35(1):151.
7 Sun Yuan, Sun Zhenping. Study on the effect of admixtures on the compatibility between cement and water reducer[J]. Cement,2003(6):7(in Chinese).
孙媛, 孙振平. 混合材对水泥与减水剂适应性的影响研究[J]. 水泥,2003(6):7.
8 Burgos-Montes O, Alonso M M, Puertas F. Viscosity and water demand of limestone-and fly ash-blended cement pastes in the presence of superplasticisers[J]. Construct Build Mater,2013,48:417.
9 Wan Huiwen, Tang Chungang, Zhang Yu. Effects of mineral admixtures and superplasticizer on rhelogical performance of cement paste[J]. J Wuhan University of Technology,2007,29(12):11(in Chinese).
万惠文, 唐春刚, 张瑜. 矿物掺合料与高效减水剂对浆体流变性的影响[J]. 武汉理工大学学报,2007,29(12):11.
10 Schröfl C, Gruber M, Plank J. Preferential adsorption of polycarboxylate superplasticizers on cement and silica fume in ultra-high performance concrete (UHPC)[J]. Cem Concr Res,2012,42(11):1401.
11 Tkaczewska E. Effect of the superplasticizer type on the properties of the fly ash blended cement[J]. Construct Build Mater,2014,70:388.
12 Toledano-Prados M, Lorenzo-Pesqueira M, González-Fonteboa B, et al. Effect of polycarboxylate superplasticizers on large amounts of fly ash cements[J]. Construct Build Mater,2013,48:628.
13 Huang Haibin, Ma Changquan, Wang Zhengshan. Study of suita-bility of naphthalene efficient superplasticizer with cement and fly ash mixture[J]. Coal Ash,2008,20(2):38(in Chinese).
黄海滨, 马长全, 王振山. 萘系高效减水剂与水泥、粉煤灰等掺合料适应性的试验研究[J]. 粉煤灰,2008,20(2):38.
14 Wang Shichao, Yu Liming, Hu Xiaowei. Analysis of factors of affecting suitability of concrete additives and cement admixture[J]. Coal Ash,2007,19(4):47(in Chinese).
王士超, 俞黎明, 虎孝伟. 混凝土外加剂与水泥、掺合料适应性的影响因素分析[J]. 粉煤灰,2007,19(4):47.
15 Burgos-Montes O, Palacios M, Rivilla P, et al. Compatibility between superplasticizer admixtures and cements with mineral additions[J]. Construct Build Mater,2012,31:300.
16 Hallal A, Kadri E H, Ezziane K, et al. Combined effect of mineral admixtures with superplasticizers on the fluidity of the blended cement paste[J]. Construct Build Mater,2010,24(8):1418.
17 Ezziane K, Ngo T T, Kaci A. Evaluation of rheological parameters of mortar containing various amounts of mineral addition with polycarboxylate superplasticizer[J]. Construct Build Mater,2014,70:549.
18 Jalal M, Pouladkhan A, Harandi O F, et al. Comparative study on effects of class F fly ash, nano silica and silica fume on properties of high performance self compacting concrete[J]. Construct Build Mater,2015,94:90.