部分浸泡再生混凝土复合盐侵蚀微观特征与损伤演化

doi:10.11896/cldb.22070227

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (37868KB)
Export: BibTeX | EndNote (RIS)

Abstract Aim to investigate the microstructure characteristics and damage evolution of recycled aggregate concrete (RAC) construction members which were partially buried in soil and partially exposed air, the partial immersion experiment was developed as the compound salt solution of 7.5%MgSO₄, 7.5%Na₂SO₄, and 5%NaCl (mass ratio), to simulate the service environment of the soil and underground water in Northwest China. The durability degradation law of partial immersion RAC was studied by testing the visual appearance, mass, and relative dynamic elastic modulus (RDEM). After that, the microstructure characteristics of RAC exposed to the compound salt solution were analyzed based on the mineral composition and its relative weight using XRD, FTIR, and TG methods. Moreover, SEM and EDS revealed the damaged mechanism for observation of the microstructure and the element compositions of the interesting zone. Results showed that the RDEM changed along the RAC specimen’s height. The varying of the RDEM of the testing area range of 3—6 was relatively stable. Afterward, the values decreased to the lowest at the testing area range of 7—8 and then rose to 100% rapidly at the testing area range of 11—12. The four exposure regions, namely, capillary saturation zone, liquid-gas two-phase interface zone, moisture transport zone, and dry zone, were distributed from bottom to up for the partial-immersion RAC. With an increase in the immersion day, the corrosion mechanism of the capillary saturation zone changed from chemical attack to chemical attack with physical damage. The damage faction of liquid-gas two-phase interface zone became from chemical attack-physical damage to chemical attack with physical damage. The moisture transport zone’s damage mode was specially transited from non-damaged to chemical attack-physical damage.

Key words： recycled aggregate concrete compound sale attack partial immersion microstructure characteristics damage evolution

Published: 25 August 2024 Online: 2024-09-10

CLC number:

TU528

Fund:National Natural Science Foundation of China (51908440), the Natural Science Foundation of Shaanxi Province (2024JC-YBMC-268) and the Opening Fund of State Key Laboratory of Green Building in Western China (LSKF202216).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	WANG Jiabin
	CHE Zhihao
	HOU Zeyu
	FAN Yijie
	NIU Ditao

Cite this article:

WANG Jiabin,CHE Zhihao,HOU Zeyu, et al. The Damage Evolution and Microstructure Characteristics of Partial Immersion Recycled Aggregate Concrete Subjected to Compound Salt[J]. Materials Reports, 2024, 38(16): 22070227-12.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.22070227 OR http://www.mater-rep.com/EN/Y2024/V38/I16/22070227

1 Wang C, Xiao J, Zhang C, et al. Engineering Structure, 2020, 205, 110102
2 Xu J, Chen Z, Xue J, et al. Procedia Engineering, 2017, 210, 109.
3 Tang Y, Xiao J, Zhang H, et al. Construction and Building Materials, 2022, 323, 126546.
4 Ma K, Xie Y, Liu Y, et al. Corrosion & Protection, 2008, 29(9), 530(in Chinese).
马昆林, 谢友均, 刘运华, 等. 腐蚀与防护, 2008, 29(9), 530.
5 Sakr M R, Bassuoni M T. Cement and Concrete Research, 2021, 141, 106324.
6 ZhangY, Hua Y, Zhu X. Journal of Cleaner Production, 2022, 331, 130022.
7 Wang, J, Niu D. Materials Reports, 2019, 33(10), 3426(in Chinese).
王家滨, 牛荻涛. 材料导报, 2019, 33(10), 3426.
8 Zhutovsky S, Hooton R D. Construction and Building Materials, 2017, 145, 98.
9 Liu Z, Pei M, Zhang F, et al. Journal of Building Materials, 2020, 23(3), 485(in Chinese).
刘赞群, 裴敏, 张丰燕, 等. 建筑材料学报, 2020, 23(3), 485.
10 Liu Z, Pei M, Liu H, et al. Journal of Building Materials, 2020, 23(4), 787(in Chinese).
刘赞群, 裴敏, 刘厚, 等. 建筑材料学报, 2020, 23(4), 787.
11 Xie F, Li J, Zhao G, et al. Construction and Building Materials, 2020, 253, 119144.
12 Mohammed H. A, Raid S. A, Hossein M, et al. Construction and Building Materials, 2019, 229, 116920.
13 Jiang X, Mu S, Yang Z, at al. Construction and Building Materials, 2021, 266, 120936.
14 Ma K, Xie Y, Long G, et al. Journal of Central South University (Science and Technology), 2010, 40(1), 303(in Chinese).
马昆林, 谢友均, 龙广成, 等. 中南大学学报(自然科学版), 2010, 41(1), 303.
15 Zhang Z, Zhou J, Yang J, et al. Construction and Building Materials, 2020, 260, 119932.
16 Zhang Z, Zhou J, Yang J, et al. Materials and Structures, 2020, 53, 104.
17 Liu Z, Hu W, Pei M, et al. Construction and Building Materials, 2018, 192, 167.
18 Du J, Tang Z, Li G, et al. Construction and Building Materials, 2019, 225, 611.
19 Wang J, Hou Z, Zhang K, et al. Materials Reports, 2022, 36(23), 21080171 (in Chinese).
王家滨, 侯泽宇, 张凯峰, 等. 材料导报, 2022, 36(23), 21080171.
20 Wang J, Hou Z, Zhang K, et al. Materials Reports, 2022, 36(12), 21060067 (in Chinese).
王家滨, 侯泽宇, 张凯峰, 等. 材料导报, 2022, 36(12), 21060067.
21 Luo Q, Bungey J H. Hydro-Science and Engineering, 1996(3), 264(in Chinese).
罗骐先, Bungey J H. 水利水运科学研究, 1996(3), 264.
22 Chen X, Lyu S, Zhang L, et al. Journal of Inorganic Materials, 2010, 25(2), 129(in Chinese).
陈雪刚, 吕双双, 张路, 等. 无机材料学报, 2010, 25(2), 129.
23 Song Q, Nie J, Wu D, at al. Construction and Building Materials, 2021, 285, 122955.
24 Xie N, Dang T, Shi X. Cement and Concrete Research, 2019, 120, 244.
25 Yang S. Science Technology and Engineering, 2018, 18(4), 143(in Chinese).
杨淑雁. 科学技术与工程, 2018, 18(4), 143.
26 Zhang S, Zuo X, Tang Y, et al. Journal of the Chinese Ceramic Society, 2019, 47(2), 184(in Chinese).
张林松, 左晓宝, 汤玉娟, 等. 硅酸盐学报, 2019, 47(2), 184.
27 Weerdt K D, Justnes H. Cement and Concrete Composites, 2015, 55, 215.
28 Xie F, Li J, Zhao G, et al. Construction and Building Materials, 2021, 297, 123771.
29 Ellina B, Barbara L, Christophe C, et al. Cement and Concrete Research, 2019, 116, 309.
30 Dominik N, Kasper E, Emilie L, et al. Cement and Concrete Research, 2016, 79, 323.
31 Yang N, Yue W. The handbook of inorganic metalloid materials atlas, Wuhan University of Technology Press, China, 2000 (in Chinese).
杨南如, 岳文海. 无机非金属材料图谱手册, 武汉工业大学出版社, 2000.
32 Gou S, Nai X, Xiao J, et al. Journal of Inorganic Materials, 2019, 34(7), 781(in Chinese).
苟生莲, 乃学瑛, 肖剑飞, 等. 无机材料学报, 2019, 34(7), 781.
33 Du J, Liu Z, Sun J, et al. Construction and Building Materials, 2022, 322, 126370.
34 Brown P W, Badger S. Cement and Concrete Research, 2000, 30, 1535.
35 Groege W. Cement and Concrete Research, 2004, 34, 1613.
36 Gao S, Guo J, Gong Y. Case Studies in Construction Materials, 2022, 16, e01034.
37 Niels T, Sadananda S. Materials Characterization, 2004, 53, 123.
38 Zhu J, Gao J, Chen F, et al. Journal of Southeast University (Natural Science Edition), 2019, 49(5), 964(in Chinese).
朱健健, 高建明, 陈菲, 等. 东南大学学报(自然科学版), 2019, 49(5), 964.