| POLYMERS AND POLYMER MATRIX COMPOSITES |
|
|
|
|
|
| Effect of Lanthanum Cerium 2-Aminonicotinate Acid on Thermal Stability of PVC |
| YANG Yuxuan1,2,3, DU Guifang1,2,3, LIU Zhaogang1,2,3,*, ZHAO Jingang1,2,3, CHEN Mingguang1,4, HU Yanhong1,2,3, WU Jinxiu1,2,3, FENG Fushan1,2,3
|
1 School of Materials and Metallurgy, Inner Mongolia University of Science and Technology, Baotou 014010, Inner Mongolia, China
2 Key Laboratory of Rare Earth Hydrometallurgy and Light Rare Earth Application of Inner Mongolia Autonomous Region, Baotou 014010, Inner Mongolia, China
3 Key Laboratory of green extraction and efficient utilization of LREE resources, Ministry of education, Baotou 014010, Inner Mongolia, China
4 Baotou Research Institute of Rare Earth, Baotou 014030, Inner Mongolia, China |
|
|
|
|
Abstract Lanthanum cerium 2-aminonicotinate acid was synthesized from 2-aminonicotinic acid(2-ANA), Ce(NO3)3, La(NO3)3 and NaOH. The effects of 2-LCANA and its compound stabilizer on the thermal stability, rheological and mechanical properties of polyvinyl chloride (PVC) were studied. The results showed that 2-LCANA and its compound stabilizer improved the thermal stability of PVC. When m(2-LCANA)∶m(ZnSt2)∶m(PE)=2∶1∶2, the thermal stability time was 38 min, which could reduce the loss in the processing process and enhance the mechanical properties of PVC. However, with the increase of temperature, 2-LCANA was more effective than m(2-LCANA)∶m(ZnSt2)∶m(PE)=2∶1∶2 in inhibiting the degradation of PVC. 2-LCANA can absorb HCl gas released from PVC degradation, generate LaCl3 and CeCl3, wea-ken the catalytic effect of HCl on PVC degradation, effectively prevent the breakage of C-Cl and C-H connected with chlorine on PVC chain, reduce the generation of conjugated double bonds, slow down PVC discoloration, and delay the thermal degradation of PVC.
|
|
Published: 10 April 2024
Online: 2024-04-11
|
|
|
| Fund:National Natural Science Foundation of China (51634005) and the Natural Science Foundation of Inner Mongolia Autonomous Region, China (2022LSM05022). |
|
|
1 Mohame N A. Polymer Degradation and Stability, 2017, 146, 42.
2 Stranes W H. Progress in Polymer Science, 2002, 27(10), 2133.
3 Stranes W H. Journal of Polymer Science Part A: Polymer Chemistry, 2005, 43(12), 2451.
4 Tawfik S Y, Asaad J N, Sabaa M W. Polymer Degradation & Stability, 2006, 91(2), 385.
5 Fisch M H, Bacalouglu R. Plastics, Rubber and Composites, 1999, 28(3), 119.
6 Newman E J, Stark T D. Geosynthetics International, 2009, 16(2), 97.
7 Grivel J C, Zhao Y, Guevara MJ S, et al. Thermochimica Acta, 2015, 612, 1.
8 Ye F, Ye Q, Guo X, et al. Journal of Vinyl and Additive Technology, 2019, 25(4), 347.
9 Li M, Liang Y D, Wu Y X, et al. Polymer Degradation & Stability, 2017, 140, 176.
10 Atakul S, Balköse D, Ülkü S. Journal of Vinyl and Additive Technology, 2005, 11(2), 47.
11 Zhang M Q, Han W Y, Hu X M, et al. Polymer Degradation and Stability, 2020, 181, 109340.
12 Li D, Xie L, Ming F, et al. Polymer Degradation and Stability, 2015, 114, 52.
13 Hao L, Li D, Li R. Engineering Plastics Application, 2016, 44(12), 131 (in Chinese).
刘浩, 李德刚, 李瑞姣. 工程塑料应用, 2016, 44(12), 131.
14 Liu F, Li J, Shi K. Polyvinyl Chloride, 2011, 39(8), 19 (in Chinese).
刘芳, 李杰, 时凯. 聚氯乙烯, 2011, 39(8), 19.
15 An L M, Song X X, Cao X. Plastics Additives, 2013(3), 30(in Chinese).
安立梅, 宋小弦, 曹雄. 塑料助剂, 2013(3), 30.
16 Ding H. Study on the synthesis and application of rare-earth as new thermal stabilizer for PVC. Master’s Thesis, Xi’an University of Science and Technology, China, 2008 (in Chinese).
丁贺. PVC新型稀土热稳定剂的合成与应用研究. 硕士学位论文, 西安科技大学, 2008.
17 Zhang N, Zhang Q, Zhang H X, et al. Plastics, 2017, 46(1), 63 (in Chinese).
张宁, 张青, 张红霞, 等. 塑料, 2017, 46(1), 63.
18 Wang S S. Study on blended modification of PVC composite material. Master’s Thesis, South China University of Technology, China, 2014 (in Chinese).
王莎莎. PVC复合材料共混改性研究. 硕士学位论文, 华南理工大学, 2014.
19 Hao L, Li D, Li R, et al. Journal of Vinyl and Additive Technology, 2018, 24(4), 314.
20 Abbas K B, Sorvik E M. Journal of Vinyl Technology, 1980, 2(2), 87.
21 Mackenzie M W, Willis H A, Owen R C, et al. European Polymer Journal, 1983, 19(6), 511.
22 Vrandecic N S, Klaric I, Roje U. Polymer Degradation & Stability, 2001, 74(2), 203.
23 Xu X P. Design, preparation, application and stabilizing mechanism of urea derivatives as novel thermal stabilizers for poly(vinyl chloride). Ph. D. Thesis, College of Materials Science and Engineering Zhejiang University of Technology, China, 2015 (in Chinese).
徐晓鹏. 新型多功能脲衍生物类PVC热稳定剂的设计、制备、应用及稳定机理研究. 博士学位论文, 浙江工业大学, 2015. |
|
|
|
渝公网安备50019002502923号 © Editorial Office of Materials Reports.
2024, Vol. 38 