增材制造316L不锈钢组织结构特征与硬化机理

doi:10.11896/cldb.22060103

Abstract
Figure/Table
References
Related Citation (7)

Download:

Full Text ( PDF ) (17346KB)
Export: BibTeX | EndNote (RIS)

Abstract 316L stainless steels with dendritic/cellular structure in various sizes were prepared by different additive manufacturing technologies, that is, wire and arc additive manufacturing (WAAM), directed energy deposition (DED), and laser selective melting (SLM). The formation mec-hanism of dendritic/cellular structure and its influence on the mechanical properties were studied. The results show that the cell/dendrite size progressively decreases in WAAM, DED, and SLM, due to the increase in cooling rates. Meanwhile, bone-like δ ferrites and pronounced enrichment of Cr and Mo are observed in the intercellular/interdendritic regions of the WAAM and DED samples, whereas such phenomena are absent in the SLM sample, because the high cooling rate during SLM significantly suppressed the formation of δ ferrites and element segregation. The microhardness of WAAM, DED, and SLM samples increased progressively, and the hardening mechanism is highly related to the solidification cellular/dendrite size as well as the high density of dislocations induced by the thermal stresses during the additive manufacturing process.

Key words： metal additive manufacturing cellular structure hardening mechanism

Published: 10 February 2024 Online: 2024-02-19

CLC number:

TG142.71

Fund:Key Research and Development Program of Shaanxi Province (2022GY-383),the Fundamental Research Funds for the Central Universities of Chang'an University (300102313205),Fund of the State Key Laboratory of Solidification Processing in NWPU (SKLSP202110).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	LIU Yuan
	KOU Haonan
	HE Yiqing
	YOU Ruichang
	ZHANG Xin
	TENG Juheng
	LI Yao
	ZHANG Fengying

Cite this article:

LIU Yuan,KOU Haonan,HE Yiqing, et al. Microstructural Characteristics and Hardening Mechanism of Additively Manufactured 316L Stainless Steels[J]. Materials Reports, 2024, 38(3): 22060103-6.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.22060103 OR http://www.mater-rep.com/EN/Y2024/V38/I3/22060103

1 Kalinin G, Barabash V, Cardella A, et al. Journal of Nuclear Materials, 2000, 283, 10
2 Guo S, Han E H, Wang H T, et al. Acta Metallurgica Sinica, 2017, 53(4), 455 (in Chinese).
郭舒, 韩恩厚, 王海涛, 等. 金属学报, 2017, 53(4), 10.
3 Wang Z N, Liang T, Zhang L, et al. Rare Metal Materials and Enginee-ring, 2018, 47 (11), 8 (in Chinese).
王志楠, 梁田, 张龙, 等. 稀有金属材料与工程, 2018, 47 (11), 8.
4 Zhong Y, Ránnar Lars-Erik, Liu L F, et al. Journal of Nuclear Mate-rials, 2017, 486 (12), 234.
5 Huang W D. The Journal of New Industrialization, 2016, 6 (3), 53 (in Chinese).
黄卫东. 新型工业化, 2016, 6(3), 53.
6 Huang S H, Peng L, Mokas Da R A, et al. The International Journal of Advanced Manufacturing Technology, 2013, 67(5), 1191.
7 Herzog D, Seyda V, Wycisk E, et al. Acta Materialia, 2017, 117, 371.
8 Lewandowski J J, Seifi M. Annual Review of Materials Research, 2016, 46, 151.
9 Wang Z, Palmer T A, Beese A M. Acta Materialia, 2016, 110, 226.
10 Zhong J, Sun Z, Xi P, et al. NPG Asia Materials, 2018, 10(4), 127.
11 Wang Y M, Voisin T, Mckeown J T, et al. Nature Materials, 2018, 17(1), 63.
12 Ramakrishnan P. Indian Welding Journal, 1972, 4(3), 89.
13 Xiao H. Microstructure control and its mechanisms during laser additive manufacturing of Inconel 718. Ph. D. Thesis, Hunan University, China, 2017 (in Chinese).
肖辉. 激光增材制造Inconel 718合金凝固组织调控及机理研究. 博士学位论文, 湖南大学, 2017
14 Zhong Y, Liu L, Wikman S, et al. Journal of Nuclear Materials, 2016, 470, 170.
15 Ding Q, Fu X, Chen D, et al. Materials Today, 2019, 25, 21.
16 Shamsujjoha M, Agnew S R, Fitz-Gerald J M, et al. Metallurgical and Materials Transactions A, 2018, 49(7), 3011.
17 Li Z, He B, Guo Q. Scripta Materialia, 2020, 177, 17.
18 Chen X, Li J, Cheng X, et al. Materials Science and Engineering A, 2017, 703, 567.
19 Ma M, Wang Z, Zeng X. Materials Science and Engineering A, 2017, 685, 265.
20 Frazier W E. Journal of Materials Engineering and Performance, 2014, 23 (6), 1917.
21 Thijs L, Sistiaga M M, Wauthle R, et al. Acta Materialia, 2013, 61 (12), 4657.
22 Wan H Y, Zhou Z J, Li C P, et al. Journal of Materials Science and Technology, 2018, 34 (10), 1799.
23 Pham M S, Dovgyy B, Hooper P A, et al. Nature Communications, 2020, 11, 749.
24 Debroy T, Wei H L, Zuback J, et al. Progress in Materials Science, 2018, 92, 112.
25 Fu J W, Yang Y S, Guo J J, et al. Metal Science Journal, 2008, 24 (8), 941.
26 Wang X G, Liu F C, Fang P, et al. Transactions of the China Welding Institution, 2019, 40(5), 9 (in Chinese).
王晓光, 刘奋成, 方平, 等. 焊接学报, 2019, 40(5), 9.
27 Krauss, G. Metallurgical and Materials Transactions B, 2003, 34(6), 781.
28 Antonsson T, Fredriksson H. Metallurgical and Materials Transactions B, 2005, 36, 85.
29 Saeidi K, Gao X, Zhong Y, et al. Materials Science and Engineering A, 2015, 625, 221.
30 David S A, Vitek J M, Reed R W, et al. Welding Research Supplement, DOI:10. 2172/5957599.
31 Umeda T, Okane T. Science & Technology of Advanced Materials, 2001, 2 (1), 231.
32 Osada T, Gu Y, Nagashima N, et al. Acta Materialia, 2013, 61 (5), 1820.
33 Chen X H, Lu J, Lu L, et al. Scripta Materialia, 2005, 52(10), 1039.