聚氨酯软质泡沫制品阻燃性能检测分析

doi:10.11896/cldb.22060066

Abstract
Figure/Table
References
Related Citation (1)

Download:

Full Text ( PDF ) (6649KB)
Export: BibTeX | EndNote (RIS)

Abstract The combustion characteristics, cell structure of flexible polyurethane (PU) foam were tested by limit oxygen index tester, vertical burning tester and SEM, and fire grade classified by 7.1.4 and 8.1.4 of GB 50826 Technical code for construction of electromagnetic wave anechoic enclosure. The relationship between different combustion characteristics of PU was studied. The applicability of the burning test method was discussed. The results show that the lower limit oxygen index(LOI), the more difficult the PU foam is to extinguish after being ignited in the air, and the less mass remains. The PU foam with high density and high LOI was tested by vertical burning, the specimen was extinguished after the bur-ner was removed. There is no significant correlation between oxygen index and vertical combustion height (flame height). The judgement results of flexible PU foam according to requirement in absorbing material show that unqualified flame height of vertical combustion is the main reason for the unqualified flame retardant performance. Due to the open-cell structure of flexible PU foam and the characteristics of vertical burning test method, the evaluation method of vertical burning performance of flexible PU foam using GB/T 8333-2012 is debatable.

Key words： flexible PU foam combustion grade limit oxygen index vertical burning test

Published: 10 February 2024 Online: 2024-02-19

CLC number:

TQ328

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	LIU Yina
	YANG Rongjie
	FENG Wenjing
	WANG Kun
	OU Liang
	CHEN Zhaoheng
	CHEN Yulong

Cite this article:

LIU Yina,YANG Rongjie,FENG Wenjing, et al. Experimental Study on Flame Retardancy of Flexible Polyurethane Foam Products[J]. Materials Reports, 2024, 38(3): 22060066-4.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.22060066 OR http://www.mater-rep.com/EN/Y2024/V38/I3/22060066

1 Feng W J, Li S P, Chen Y J, et al. China Plastics, 2020, 34(3), 93(in Chinese).
冯文静, 李守平, 陈雅君, 等. 中国塑料, 2020, 34(3), 93.
2 Mathivanan S, Mohan R, Das B N , et al. Journal of Polymer Enginee-ring, 2016, 36(3), 253.
3 Gong N. Flexible polyurethane foam combustion performance and fire hazard analysis. Master's Thesis, Southwest Jiaotong University, China, 2011(in Chinese).
龚娜. 软质聚氨酯泡沫塑料燃烧性能及火灾危险性分析. 硕士学位论文, 西南交通大学, 2011.
4 Liu G S, Feng J, Hao J W, et al. China Plastics, 2011, 25(11), 5(in Chinese).
刘国胜, 冯捷, 郝建薇, 等. 中国塑料, 2011, 25(11), 5.
5 Migda W, Szczepanski M, Jankowski R, et al. Periodica Polytechnica-civil Engineering, 2019, 63(2), 480.
6 GB 50826-2012 Technical code for constructuin of electromagnetic wave anechoic enclosure, China Standards Press, China, 2012(in Chinese).
GB 50826-2012电磁波暗室工程技术规范, 中国标准出版社, 2012.
7 GB 8624-2012 Classification for burning behavior of building materials and products, China Standards Press, China, 2012(in Chinese).
GB 8624-2012建筑材料及制品燃烧性能分级, 中国标准出版社, 2012.
8 TB/T 3237-2010 Flame retardant technical specification of decorating materials for multiple unit train, China Rails Press, China, 2010(in Chinese).
TB/T 3237-2010动车组用内装材料阻燃技术条件, 中国铁道出版社, 2010.
9 TB/T 3138-2018 Techinical Specification of flame retardant materials for railway locomotive and vehicle, China Rails Press, China, 2018(in Chinese).
TB/T 3138-2018机车车辆用材料阻燃技术要求, 中国铁道出版社, 2018.
10 GB/T 8333-2008 Test method for flammability of rigid cellular plastic-Virtical burning method, China standards Press, China, 2008(in Chinese).
GB/T 8333-2008硬质泡沫塑料燃烧性能试验方法垂直燃烧法, 中国标准出版社, 2008.
11 GB/T 2406. 2-2009 Plastics-Determination of burning behaviour by oxygen index-Part 2:Ambient-temperature test, China standards Press, China, 2009(in Chinese).
GB/T 2406. 2-2009塑料用氧指数法测定燃烧行为:第2部分室温试验, 中国标准出版社, 2009.
12 ASTM D 3014-2011 Standard test method for flame height, time of bur-ning, and loss of mass of rigid thermoset cellular plastics in a vertical position, American Society of Testing Materials, 2011.