INORGANIC MATERIALS AND CERAMIC MATRIX COMPOSITES |
|
|
|
|
|
Pozzolanic Reactivity and Hydration Properties Assessment of Tuff Powder in Composite Cementitious Materials |
WANG Xuhao1,*, HOU Xin1, GAN Long1,2, WANG Yuan1, BIAN Qinghua3, ZHANG Jiupeng1
|
1 School of Highway, Chang'an University, Xi'an 710064, China 2 PowderChina Chengdu Engineering Corporation Limited, Chengdu 610072, China 3 Gansu Road and Bridge Third Highway Engineering Corporation Limited, Lanzhou 730050, China |
|
|
Abstract To respond to the “carbon peak, carbon neutral” strategy and realize the green and sustainable development of the cement industry, it is proposed to study the mechanism of the hydration effect on cement-based materials when tuff powder is used as supplementary cementitious material to replace part of cement. Through the research, we hope to promote the application of tuff powder in a practical project. In this work,a comparative study was carried out using granite powder, fly ash and tuff powder. The pozzolanic reactivity was evaluated by the pozzolanic reactivity index method, and then the strength and hydration development of cement-powder and cement-fly ash composite system were studied by compressive strength test and microscopic analysis means such as X-ray diffraction (XRD), thermogravimetry-differential thermal analysis (TG-DTA) and scanning electron microscope (SEM). Finally, greenhouse gas emissions were assessed. The results showed that tuff powder had a weak pozzolanic reactivity. Specifically, its pozzolanic reactivity index was 52.5%, which was less than 65%. In general, it cannot be directly used as natural volcanic ash material for cement mortar and concrete. Tuff powder in cementitious materials will play the role of crystal nucleation, which can promote the early hydration of cement. The strength of nucleation effect was related to the fineness of the powder, and the smaller tuff powder had a stronger role in promoting hydration than the granite powder with a larger fineness. From the results of chemically bound water analysis, it was concluded that the hydration degree of tuff powder-cement composite system and fly ash-cement composite system was the same when the addition amount of mineral admixture was 20%, influenced by the nucleation effect and pozzolanic reactivity of tuff powder.
|
Published: 25 August 2022
Online: 2022-08-29
|
|
Fund:National Key R & D Program of China (2021YFB2601000), the National Natural Science Foundation of China (52178185) and the Fellowship of China Postdoctoral Science Foundation (2021MD703885). |
|
|
1 Stafford F N, Raupp-Pereira F, Labrincha J A, et al. Journal of Cleaner Production, 2016, 137, 1293. 2 Rajamma R, Senff L, Ribeiro M J, et al. Composites Part B: Enginee-ring, 2015, 77, 1. 3 Wan X M, Zhang Y, Zhao T J, et al. Materials Reports B: Research Papers, 2018, 32(6), 2091(in Chinese). 万小梅, 张宇, 赵铁军,等. 材料导报:研究篇, 2018, 32(6), 2091. 4 Liu S H, Fang P P, Wang H L, et al. Powder Technology,2021,380,59. 5 Shi Y, Li X, Li Y, et al. Frontiers in Materials, 2020, 7, 595997. 6 Letelier G V, Ortega J M, Tremiño R M, et al. Applied Sciences, 2020, 10(4), 1460. 7 Labbaci Y, Abdelaziz Y, Mekkaoui A, et al. Construction and Building Materials, 2017, 133, 468. 8 Zhang Y S, Bu C X, Xu W T, et al. Water Power, 1992(10), 30(in Chinese). 张玉生, 卜崇先, 许文涛, 等. 水力发电, 1992(10), 30. 9 Hu Y R, Hu X L. Yunnan Water Power,2000,16(2),53(in Chinese). 胡以仁, 胡晓林. 云南水力发电, 2000, 16(2), 53. 10 Soroka I, Setter N.Cement and Concrete Research, 1977, 7(4), 449. 11 Péra J, Husson S, Guilhot B.Cement and Concrete Composites, 1999, 21(2), 99. 12 Bentz D P.Cement and Concrete Composites, 2006, 28(2), 124. 13 Bentz D P, Ardani A, Barrett T, et al. Construction and Building Mate-rials, 2015, 75, 1. 14 Sato T, Diallo F.Transportation Research Record, 2010, 2141(1), 61. 15 Zajac M, Rossberg A, Saout G L, et al. Cement and Concrete Compo-sites, 2014, 46, 99. 16 Weerdt K D, Haha M B, Saout G L, et al. Cement and Concrete Research, 2011, 41(3), 279. 17 Matschei T, Lothenbach B, Glasser F P.Cement and Concrete Research, 2007, 37(4), 551. 18 Thongsanitgarn P, Wongkeo W, Chaipanich A, et al. Construction and Building Materials, 2014, 66(36), 410. 19 Wang J L. Research of effects and mechanism of manufactured sand chara-cteristics on Portland cement concrete. Ph.D. Thesis, Wuhan University of Technology, China, 2008(in Chinese). 王稷良. 机制砂特性对混凝土性能的影响及机理研究. 博士学位论文, 武汉理工大学, 2008. 20 Shen W G, Liu Y, Wang Z W, et al. Construction and Building Mate-rials, 2018, 172,574. 21 Shi C J, Wang D H, Jia H F. Journal of the Chinese Ceramic Society, 2017, 45(11), 1582(in Chinese). 史才军, 王德辉, 贾煌飞, 等. 硅酸盐学报, 2017, 45(11), 1582. 22 Letelier V, Ortega J M, Tremiño R M, et al. Applied Sciences, 2020, 10(4), 1460. 23 Hammond G P, Jones C I.Proceedings of the Institution of Civil Engineers-Energy, 2008, 161(2), 87. 24 Letelier V, Ortega J M, Tarela E, et al. Sustainability, 2018, 10(9), 3036. 25 Elza Bontempi.Journal of Cleaner Production, 2017, 162, 162. 26 Li X, Shi Y, Li J Z, et al. Journal of Building Materials, 2017, 20(3), 435(in Chinese). 李响, 石妍, 李家正, 等. 建筑材料学报, 2017, 20(3), 435. 27 Li X, Li Z P, Hu X, et al. Journal of Yangtze River Scientific Research Institute, 2018, 35(5), 115(in Chinese). 李响, 李正平, 胡贤, 等. 长江科学院院报, 2018, 35(5), 115. |
|
|
|