三乙醇胺对液体无碱速凝剂“促-抑”水泥早期水化的调控机理研究

doi:10.11896/cldb.21100165

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (3167KB)
Export: BibTeX | EndNote (RIS)

Abstract Triethanolamine (TEA), as a commonused component in cement concrete for early strength, which can significantly promote the development of early strength. In recent years, with the rapid development of shotcrete and liquid alkali-free accelerator, triethanolamine has been widely used due to its excellent early-strength characteristics. However, the performance of accelerator prepared from triethanolamine under different conditions are not the same or even the opposite. Its influence law and action mechanism on early hydration of cement need to be clarified. In this study, liquid alkali-free accelerator with different proportions of TEA was prepared. The influence of TEA in the alkali-free accelerator on the early hydration of cement was investigated in detail from the aspects of setting time, early strength, hydration exothermic behavior, hydrate phase and thermal analysis. The results show that when TEA accounted for 0.25% of the mass of alkali-free accelerator, the setting time was the shortest, the initial setting was 109 s, the final setting was 324 s, and the strength was the highest at 1 d, reaching 12.32 MPa, which meets the national standard requirements of accelerator for shotcrete. TEA can accelerate the accelerating effect of alkali-free accelerator on early hydration of cement at low dosage, while it can significantly weaken and inhibit early hydration of cement at high dosage. In addition, the complexation mec-hanism between TEA and aluminum phase was studied by means of conductivity and nuclear magnetic hydrogen spectroscopy, and the regulation mechanism of TEA to liquid alkali-free accelerators on the ‘accelerating-inhibiting' early hydration of cement was revealed:(ⅰ) when the content of TEA is low, metaaluminate ions complex with TEA and participate in accelerating the early hydration of C₃A;(ⅱ) high TEA content will produce a large amount of ettringite and TEA-Ca complex, which will cover the surface of C₃A and inhibit hydration. This study systematically explores the influence and regulation mechanism of liquid alkali-free accelerator with different TEA contents on early hydration of cement, which provides an important research basis and scientific guidance for the development of high-performance liquid alkali-free accelerator.

Key words： accelerator triethanolamine setting time early strength hydration

Published: 10 May 2023 Online: 2023-05-04

CLC number:

TU528.53

Fund:Natural Science Foundation of Hebei Province (E2022210028) and National Natural Science Foundation of China (51578025).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	LIU Xiao
	XIE Hui
	LUO Qifeng
	WANG Ziming
	CUI Suping
	GUO Jinbo
	ZHANG Guanhua

Cite this article:

LIU Xiao,XIE Hui,LUO Qifeng, et al. Study on Regulation Mechanism of Triethanolamine to Liquid Alkali-free Accelerator on ‘Accelerating-Inhibiting' of Early Hydration of Cement[J]. Materials Reports, 2023, 37(9): 21100165-6.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.21100165 OR http://www.mater-rep.com/EN/Y2023/V37/I9/21100165

1 Peter H,Martin L. Le's chemistry of cement and concrete,Butter worth-Heinemann,London,2005,pp. 1053.
2 Kong X M,Lu Z B,Liu H,et al. Cement and Concrete Research,2013,65,1101.
3 Liu J Q. Research on the synergestic effect of polycarboxylate superplasticizer and hardening accelerants. Master's Thesis,Beijing University of Technology,China,2008(in Chinese).
刘进强.聚羧酸系减水剂与早强组分的复合性能研究. 硕士学位论文,北京工业大学,2008.
4 Ramachandran V S. Aool Chem Biotech,1972,22(11),1125.
5 Ramachandran V S. Cement and Concrete Research,1973,3(1),41.
6 Ramachandran V S. Cement and Concrete Research,1976,6(5),623.
7 Huang Moting. Research on preparation and propreties of a new alkali-free flash setting admixture. Master's Thesis,Harbin Institute of Technology,China,2020(in Chinese).
黄莫霆. 新型无碱速凝剂的制备与性能研究. 硕士学位论文,哈尔滨工业大学,2020.
8 Gan Jiezhong. Research on the composition,properties and mechanism of chloride-free and alkali-free liquid accelerator. Master's Thesis,China Building Materials Academy,China,2014(in Chinese).
甘杰忠. 无碱无氯液体速凝剂的组成、性能及机理研究. 硕士学位论文,中国建筑材料科学研究总院,2014.
9 Zhang Yanrong,Kong Xiangming,Lu Zichen,et al. Cement and Concrete Research,2016,87,64.
10 Yohannes L Y,Yu Z C,Raymond H W L,et al. Construction and Building Materials,2017,141,94.
11 Han Jianguo,Wang Kejin,Shi Jiyao,et al. Construction and Building Materials,2015,93,457.
12 Ding Xiangqun,Li Xin,Guo Yizhe,et al. Concrete,2021(5),56(in Chinese).
丁向群,李欣,郭一哲,等. 混凝土,2021(5),56.
13 Jiang Min. Study on the preparation and performance of new type alkali-free and chlorine-free liquid accelerator. Master's Thesis,Hunan Normal University,China,2016(in Chinese).
蒋敏. 新型无氯液体无碱速凝剂的制备及其性能研究. 硕士学位论文,湖南师范大学,2016.
14 Perez J P,Nonat A,Pourchet S,et al. In:Seventh CANMET/ACI International Conference on Superplasticizers and Other Chemical Admixtures in Concrete. American Concrete Institute,Farmington Hills,2003,pp. 583.
15 Hu Shijun,Hu Dashi,Xiao Lihua. Journal of Daqing Petroleum Institute,1992(2),28(in Chinese).
胡世军,胡大石,肖丽华. 大庆石油学院学报,1992(2),28.
16 Lu Zichen,Kong Xiangming,Jansen Daniel,et al. Cement and Concrete Research,2020,132,106041.
17 He Tingshu,Li Hongyan,He Rui,et al. Bulletin of the Chinese Ceramic Society,2019,9(9),2707(in Chinese).
何廷树,李红艳,何蕊,等. 硅酸盐通报,2019,9(9),2707.
18 Tian Junzhuang. Preparation and performance research of high strength liquid alkali-free flash setting admixture. Master's Thesis,Chang'an University,China,2017(in Chinese).
田俊壮. 增强型液体无碱速凝剂的制备及性能研究. 硕士学位论文,长安大学,2017.
19 Yaphary Y L,Yu Z C,Lam R H W,et al. Construction and Building Materials,2017,141,94.
20 Yang Fumin. Railway Engineering,2021,61(2),139 (in Chinese).
杨富民. 铁道建筑,2021,61(2),139.
21 Yang Jin,Yang Mingjian,He Xingyang,et al. Construction and Building Materials,2021,306,124840.
22 Niu D T,Jiang L,Fei Q N. Journal of Wuhan University of Technology-Materials Science Edition,2013,28(6),1172.
23 Wang Jiahe,Xie Yongjiang,Zhong Xinhua,et al. Cement and Concrete Composites,2020,112,103684.
24 Lin Zongshou,Zhao Xiujian,Ye Jing,et al. Inorganic non-metallic materials engineering,Wuhan University of Technology Press,China,2013,pp. 218 (in Chinese).
林宗寿,赵修建,叶菁,等. 无机非金属材料工学,武汉理工大学出版社,2013,pp. 218.
25 Li Guoxin,Zhang Jiangbo,Niu Mengdie,et al. Construction and Building Materials,2020,233,117296.