碱激发锌渣胶凝材料设计制备与微观结构分析

doi:10.11896/cldb.21050274

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (7008KB)
Export: BibTeX | EndNote (RIS)

Abstract Taking zinc slag as raw material, this work prepared alkali-activated zinc slag cementitious material, based on the reuse of zinc slag solid waste. The orthogonal test was adopted to study the influence of ratio of liquid to solid, water glass modulus and cement content on the mechanical properties of alkali-activated zinc slag cementitious material system. And then, we analyzed the microstructure of alkali-activated zinc slag cementitious materials with different mixing ratios and explored the effects of temperature and specific surface area based on the optimal ratio by XRD and SEM. Finally, we tested the curing ability of alkali-activated zinc slag cementitious material to the zinc ion. The results show that the compressive strength of alkali-activated zinc slag cementitious material system is most affected by cement content, followed by ratio of liquid to solid and water glass modulus. In this study, under the condition of the cement content 10%, the ratio of liquid to solid 0.2, and the water glass modulus 0.8, the optimum mixing ratio is obtained, and the 28 d compressive strength can reach 56.5 MPa. In addition, the physical methods of steam curing and increasing the specific surface area of zinc slag powder can improve the early strength. The hydrated product of alkali-activated zinc slag cementitious materials is an amorphous gel phase mainly composed of C-(A)-S-H gel, which belongs to α-C-S-H gel. Its dense three-dimensional structure not only provides a positive effect for strength, but also has a good ability to solidify Zn²⁺, which provides a new way for the second utilization of zinc slag.

Key words： zinc slag orthogonal test compressive strength alkali excitation material microstructure solidified ion

Published: 25 November 2022 Online: 2022-11-25

CLC number:

TU528

Fund:Innovation Foundation of Changjiang Institute of Survey, Planning, Design and Research (CX2020K05) and the National Natural Science Foundation of China (51579195).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	XU Xian
	KANG Jing
	CAI Xinhua
	WANG Weikang

Cite this article:

XU Xian,KANG Jing,CAI Xinhua, et al. Design and Microstructure Analysis of Alkali-activated Zinc Slag Cementitious Materials[J]. Materials Reports, 2022, 36(22): 21050274-7.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.21050274 OR http://www.mater-rep.com/EN/Y2022/V36/I22/21050274

1 Zhang Y H, Tang Y H, Chen J H, et al. Nonferrous Metals Engineering, 2021,11(2), 120(in Chinese).
章艳红,唐玉红,陈俊华, 等.有色金属工程, 2021,11(2), 120.
2 Deng Q F. Research on the comprehensive utilization of indigenous zinc smelting slag. Master's Thesis, Central South University, China, 2013(in Chinese).
邓秋凤. 土法炼锌废渣资源化利用的研究. 硕士学位论文, 中南大学, 2013.
3 Lei H Z, Yang G C, Li Y G, et al. Yunnan Metallurgy, 2018,47(4), 63(in Chinese).
雷华志,杨光灿,李雨耕, 等.云南冶金,2018,47(4), 63.
4 Omran M, Fabritius T, Yu Y W, et al.Journal of Sustainable Metallurgy, 2021, 7, 15.
5 Xie K, Wang H B, Liu S P, et al. Nonferrous Metals(Extractive Metallurgy), 2019(7), 30(in Chinese).
谢铿,王海北,刘三平, 等.有色金属(冶炼部分),2019(7), 30.
6 He Z X, Xiao Q C, Zhou X Y, et al. Journal of Central South University(Science and Technology), 2015, 46(10), 3961(in Chinese).
何哲祥,肖祈春,周喜艳, 等.中南大学学报(自然科学版),2015,46(10), 3961.
7 Wang Y J, Pan M Y, Zhang Z R, et al. Guangzhou Chemical Industry, 2019,47(16), 71(in Chinese).
王艳君,潘梦雅,张择瑞, 等.广州化工, 2019,47(16), 71.
8 Zhang S Z, Gong K C. Journal of Materials Science and Engineering, 2003,21(3),430(in Chinese).
张书政, 龚克成. 材料科学与工程学报, 2003,21(3),430.
9 Gomes K C, Carvalho M, Diniz D D P, et al. Revista Matéria, 2019, 24, 4.
10 Çelikten S, Sarıdemir M, Özgür Deneme I·. Construction and Building Materials, 2019, 217, 50.
11 Shaikh F U A. International Journal of Sustainable Built Environment, 2016, 5(2), 277.
12 You N Q, Li B L, Cao R L, et al. Construction and Building Materials, 2019, 227,116614
13 Xie F Z, Liu Z, Zhang D W, et al.Construction and Building Materials,2020, 252,119132.
14 Jiang G Z, Wu A X, Wang Y M, Chinese Journal of Engineering, 2020,42(8), 963(in Chinese)
姜关照,吴爱祥,王贻明. 工程科学学报,2020,42(8), 963.
15 Wang A G, Zheng Y, Zhang Z H, et al. Engineering,2020,6(6),695.
16 De Pereira D S T, Da Silva F J, Porto A B R, et al. Journal of Materials Research and Technology, 2018, 7(4), 606.
17 Nath S K. Journal of Hazardous Materials, 2020, 387,121673.
18 Chen W, Peng R, Straub C, et al. Construction and Building Materials, 2020, 236,117745.
19 Zhang P P, Muhammada F, Yu L, et al. Construction and Building Materials, 2020,249,118759.
20 Yu L, Fang L, Zhang P, et al.International Journal of Environmental Research and Public Health, 2021,18,9960.
21 Jiang Y F, Wu L, Liu Y, New Building Materials, 2019, 46(9), 57(in Chinese).
姜玉凤,吴璐,刘宇.新型建筑材料,2019,46(9), 57.
22 Zheng W Z, Zou M N, Wang Y. Journal of Building Structures, 2019, 40(1),28(in Chinese).
郑文忠, 邹梦娜, 王英.建筑结构学报, 2019,40(1),28.
23 Lei Y S. Study on microstructure on hydrated calcium silicate and inf-luence for the performance of fly ash baking-free bricks. Master's Thesis, North University of China, China, 2014(in Chinese).
雷永胜.水化硅酸钙微结构及其对粉煤灰免烧砖性能影响的研究. 硕士学位论文, 中北大学,2014.
24 Zhao J, Zhang Y X, Zhang Y W.Journal of Wuhan University of Techno-logy(Materials Science), 2017, 32(6), 1388.
25 Shrivas R, Paramkusam B R, Dwivedi S B. KSCE Journal of Civil Engineering, 2021, 25(5), 1600.
26 Hou Y F. Cementitious materials, China Electric Power Press, China, 2012, pp.126(in Chinese).
侯云芬.胶凝材料,中国电力出版社,2012, pp. 126.
27 Yi J S. Study on physical and mechanical properties of water glass superfine slag powder cement grouting material. Master's Thesis, Anhui University of Science and Technology, China, 2020(in Chinese).
易健胜. 水玻璃-超细矿渣粉-水泥注浆材料物理力学性能研究. 硕士学位论文. 安徽理工大学, 2020.
28 Jiang G Z, Wu A X, Wang Y M, et al. Chinese Journal of Engineering, 2017,39(9),1305(in Chinese).
姜关照, 吴爱祥, 王贻明, 等.工程科学学报, 2017,39(9),1305.
29 Garcia-Lodeiro I, Palomo A, Fernández-Jiménez A, et al.Cement and Concrete Research, 2011, 41(9), 923.
30 Yang D, Lu M Y, Song D, et al. Materials Reports, 2021,35(Z1),644(in Chinese).
杨达, 卢明阳, 宋迪, 等.材料导报, 2021,35(Z1),644.
31 Peng H, Chen Z K, Cui C, et al. Journal of Building Materials, 2017,20(3),379(in Chinese).
彭晖, 陈治坤, 崔潮, 等.建筑材料学报, 2017,20(3),379.