利用聚丙烯酸正丁酯@聚甲基丙烯酸甲酯核/壳结构聚合物增韧氰酸酯树脂

doi:10.11896/cldb.201904027

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (2976KB)

Suppl. Info.
Export: BibTeX | EndNote (RIS)

Abstract Aseries of core-shell structured poly(n-butyl acrylate)@poly(methyl methacrylate) (named PBMMA) impact modifiers differing in core/shell weight ratio (60/40,65/35,75/25,70/30, to 80/20) with an average particle size of 346 nm were prepared by seed emulsion polymerization. The toughening effects of the core-shell structured particles with various compositions and under different adding amounts toward cyanate ester (CE) resin were investigated. It was found that the polymerization had a very high instantaneous conversion (90wt%) and overall conversion (95wt%). The PBMMA latexes had an obvious core-shell structure confirmed by transmission electron microscope, and the weight ratio of core/shell had inconspicuous influence on the seed-emulsion polymerization process. The mechanical properties of the PBMMA/CE blends were evaluated, and scanning electron microscope (SEM) was used to observe the fractured surface morphology. We also conducted the dynamic mechanical analysis by which the molecular movement of the CE/PBMMA blends could be revealed. The results showed that PBMMA can be dispersed well in the matrix, and the brittle-ductile transition point emerges under an appropriate value of the core-shell weight ratio (60/40) and the adding amount of the core-shell structured particles (5wt%). As a result, the PBMMA/CE blend was determined to have a high impact strength which is 3.78 times of pure CE resin. The mechanical properties agreed well with the SEM observation.

Key words： cyanate ester resin acrylate ester core-shell structure seed emulsion polymerization toughening

Published: 11 March 2019

CLC number:

TQ 323.9

Fund:This research was financially supported by the Natural Science Foundation of Hebei Province (E2016202036), the Program of Science and Technology Plan of Tianjin (17YFCZZC00280).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	ZHAI Le
	JI Haifeng
	YAO Yanmei
	QU Xiongwei

Cite this article:

ZHAI Le,JI Haifeng,YAO Yanmei, et al. Toughening Cyanate Ester Resin by Using Poly(n-butyl acrylate)@Polymethyl Methacrylate Core-Shell Structured Polymer Particles[J]. Materials Reports, 2019, 33(4): 705-708.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.201904027 OR http://www.mater-rep.com/EN/Y2019/V33/I4/705

Laskoski M, Dominguez D D, Keller T M. Journal of Polymer Science: Part A: Polymer Chemistry,2006,44(15),4559.2 Zhang B F, Wang Z G, Zhang X. Polymer,2009,50(3),817.3 Rau A V, Srinivasan S A, MeGrath J E, et al. Polymer Composites,1998,19(2),166.4 Karad S K, Attwood D, Jones F R. Composite: Part A,2002,33(12),1665.5 Nair C P R, Mathew D, Ninan K N. Advances in Polymer Science, 2001,155(1),1.6 Fang H Q, Liang G Z, Wang J L, et al. Material Review,2004,18(9),47(in Chinese).房红强,梁国正,王结良,等.材料导报,2004,18(9),47.7 Gong D J, Wei B R, Liu C H. Journal of Insulating Materials,2009,42(5),52(in Chinese).宫大军,魏伯荣,柳丛辉.绝缘材料,2009,42(5),52.8 Zhang X Y, Gu A J, Liang G Z, et al. Journal of Polymer Research,2011,18(6),1441.9 Liu J F, Zhang D W, Yang H L, et al. Thermosetting Resin,2008,23(2),11(in Chinese).刘敬峰,张德文,杨慧丽,等.热固性树脂,2008,23(2),11.10 Iijima T, Kaise T, Tomoi M. Journal of Applied Polymer Science,2003,88(1),1.11 Zhong X Y, Bao J W, Chen X B, et al. Jouranl of Materials Enginee-ring,2006(1),38(in Chinese).钟翔屿,包建文,陈祥宝,等.材料工程,2006(1),38.12 Huang F P, Li C L, Zhu B L, et al. Fiber Reinforced Plastics/Compo-sites,2015(5),27(in Chinese).黄凤萍,李春雷,祝宝林,等.玻璃钢/复合材料,2015(5),27.13 Yang P C, Pickelman D M, Woo E P. In: 35th International SAMPE Symposium. Anaheim, California,1990,pp.1131.14 Yang J Y, Liang G Z, Tang Y S, et al. Chinese Journal of Materials Research,2005,19(6),625(in Chinese).杨洁颖,梁国正,唐玉生,等.材料研究学报,2005,19(6),625.15 Fang Z P, Wang J G, Gu A J. Polymer Engineering & Science,2006,46(5),670.16 Lyu S H, Lv Q Q, Yang Q R. China Plastics,2005,19(3),28(in Chinese).吕生华,吕庆强,杨权荣.中国塑料,2005,19(3),28.17 Fu N, Li G H, Zhang Q X, et al. RSC Advances,2014,4(3),1067.18 Dong Q, Alojz I. Polymer,2015,66(1),16.19 Fan H, Wang J L. Polymer Materials Science and Engineering,2001,17(1),121(in Chinese).范宏,王建黎.高分子材料科学与工程,2001,17(1),121.20 Wang Q J, Huang Y, Xiong J, et al. Fiber Reinforced Plastics/Composites 2003(4),50(in Chinese).王琦洁,黄英,熊佳,等.玻璃钢/复合材料,2003(4),50.