新型汽车用高强度中锰钢研究现状及发展趋势

doi:10.11896/cldb.18030219

Abstract
Figure/Table
References
Related Citation (7)

Download:

Full Text ( PDF ) (8458KB)
Export: BibTeX | EndNote (RIS)

Abstract With the global energy crisis and increasingly serious environmental problems, the automotive industry has the trend towards lightweight design to meet thedemands of energy saving, consumption reduction, environmental protection and safety. The main approaches to implement automotive lightweighting are as follow. Ⅰ. Employ the advanced materials and processes, that is, adopt lightweight materials or forming technology to achieve the weight reduction goal. Ⅱ. Optimize the structural design, including thin wall, cavity, miniaturization, compounding and structural and technological improvement of body parts., The application of high strength steel as the main material of the automobile can not only contribute to reducing of the body thickness and weight, but also improve the safety performance.
At present, the development of high strength steel has experienced three stages.As regard to microstructure, the first generation advanced high strength steel consists of ferrite (BCC) as matrix, the second generation consists of austenite (FCC), and the third generation consists of ferrite and retained austenite. Although the strength of the first generation advanced high strength steel is relatively high, its plasticity is limited. For the sake of solving this problem, a large amount of alloying elements, such as Cr, Ni, mn, Si and Al, are added in the second generation advanced high strength steel. Nevertheless, this approach increases the production cost, and also causes some problems in the subsequent processing, which blocks its widespread application in large-scale production. Accordingly, the content of alloying elements has been reduced in the third ge-neration advanced high strength steel, and the main alloying elements are composed of C, mn, Al, and Si. In this case, high strength and high plasticity can be achieved at a lower cost, as well as an excellent combination of elongation and tensile strength.
As a representative of the third generation advanced high strength steel, medium manganese high strength steel can achieveimproved plasticity and strength through TRIP or TWIP effects of retained austenite during deformation. The medium manganese high strength steel consists of sub-micron austenite and ferrite which are formed by the austenite reverse transformation in the annealing process of hot or cold rolled sheets. In recent years, most researches have focused on how to obtain appropriate fraction of stable retained austenite by optimizing process parameters, such as heating rate, austenitizing temperature, annealing temperature, annealing time and cooling rate, and fruitful results have been achieved. However, the study on its mechanical properties is limited to tensile properties. There is a lack of research on subsequent forming properties and fracture mechanism of medium manganese steel.
In this article, the development history and recent research situation of medium manganese high strength steel for automotive application are summarized. The advantages of medium manganese steel in material cost and mechanical properties are emphasized. Firstly, chemical composition design of medium manganese steel is introduced, as well as the effects of alloy element on the structures and properties of medium manganese steel. Secondly, the effects of intercritical annealing process parameters, including austenitization temperature, annealing temperature, annealing time, heating rate and cooling rate, on adjusting retained austenite are analyzed. Finally, the enhanced strength and toughness of me-dium manganese steel are revealed due to the TRIP and TWIP effects of retained austenite during the deformation process. The nucleation and growth of microvoid and fracture mechanism are explained. The cause of the lüders deformation behavior during stretching is studied. The application of medium manganese steel in hot forming process is introduced. In addition, the future development trend of medium manganese steel is predicted. It is believed that the industrial production and practical application of medium manganese steel can be realized in near future.

Key words： medium manganese steel retained austenite TRIP effect strengthening-toughening mechanism representative volume element (RVE)

Published: 10 April 2019

CLC number:

TG142

Fund:This work was financially supported by Natural Science Foundation of Hebei Province (E2018209278), Self-financing Project of Tangshan Science and Technology Plan (17110211a)

About author:: Qian Liu received his B.E. degree from Hebei Polytechnic University in 2009 and received his Ph.D. degree in material Science and Engineering from University of Science and Technology Beijing, in 2016. He is currently a lecturer in North China University of Science and Technology. His research interests are the optimization of the relationship between microstructure and performance for advanced material, forming process of high performance steel material, metal forming simulation technology and process parameter optimization.

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	LIU Qian
	ZHENG Xiaoping
	ZHANG Ronghua
	TIAN Yaqiang
	CHEN Liansheng

Cite this article:

LIU Qian,ZHENG Xiaoping,ZHANG Ronghua, et al. medium manganese High Strength Steel for Automotive Application: Status Quo and Prospects[J]. Materials Reports, 2019, 33(7): 1215-1220.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.18030219 OR http://www.mater-rep.com/EN/Y2019/V33/I7/1215

1 Grange R A, Hribal C R.Low-carbon 6% manganese martensitic steels.USS: Bain Laboratory for Fundamental Research Report, 1968.
2 miller R L.metallurgical Transactions, 1972, 3(4), 905.
3 Furukawa T, Huang H, matsumura O.materials Science and Technology, 1994, 10(11), 964.
4 merwin m J, Zahumensky P.Iron & Steel Technology, 2007, 4(10), 68.
5 Dong H, Wang m Q, Weng Y Q.Iron and Steel, 2010, 45(7), 1 (in Chinese).
董瀚,王毛球,翁宇庆.钢铁,2010,45(7),1.
6 Latypov m I, Shin S, De Cooman B C, et al.Acta materialia, 2016, 108, 219.
7 Aydin H, Essadiqi E, Jung I, et al.materials Science and Engineering: A, 2013, 564, 501.
8 Park S J, Hwang B, Lee K H, et al.Scripta materialia, 2013, 68(6), 365.
9 Lee D, Kim J, Lee S, et al.materials Science and Engineering: A, 2017, 706, 1.
10 Liu S, Xiong Z, Guo H, et al.Acta materialia, 2017, 124, 159.
11 Shi J, Sun X, Wang m, et al.Scripta materialia, 2010, 63(8), 815.
12 Xu Y B, Zou Y, Hu Z P, et al.materials Science and Engineering: A, 2017, 698, 126.
13 Zou Y, Xu Y B, Hu Z P, et al.materials Science and Engineering: A, 2016, 675, 153.
14 Lee S, Estrin Y, De Cooman B C.metallurgical and materials Transactions A, 2013, 44(7), 3136.
15 Yang F, Luo H, Hu C, et al.materials Science and Engineering: A, 2017, 685, 115.
16 Hu B, Luo H. metals, 2017, 7(12), 464.
17 Wang Y, Zang S, Sun L, et al.materials & Design, 2017, 129, 34.
18 He B B, Hu B, Yen H W, et al.Science, 2017, 357(6355), 1029.
19 Zhang m, Li L, Ding J, et al.Acta materialia, 2017, 141, 294.
20 Cai Z H, Ding H, Xue X, et al.materials Science and Engineering: A, 2013, 560, 388.
21 Zhang X Y, Tan J, Ren W, et al. materials Review A:Review Papers, 2015, 29(7), 106 (in Chinese).
张啸宇,谭俊,任伟,等.材料导报:综述篇,2015,29(7),106.
22 Han J, Lee S, Jung J, et al.Acta materialia, 2014, 78, 369.
23 Jang J m, Kim S J, Kang N H, et al.metals and materials International, 2009, 15(6), 909.
24 Han J, Lee Y.Acta materialia, 2014, 67, 354.
25 Cai Z H, Ding H, Kamoutsi H, et al.materials Science and Engineering: A, 2016, 654, 359.
26 Seo E J, Cho L, De Cooman B C.Acta materialia, 2016, 107, 354.
27 Zhao Z Z, Liang J H, Zhao A m, et al.Journal of Alloys and Compounds, 2017, 691, 51.
28 Cao J L, Zhao A m, Li Z, et al.Journal of University of Science and Technology Beijing, 2013, 11(35), 1465 (in Chinese).
曹佳丽,赵爱民,李振,等.北京科技大学学报,2013,11(35),1465.
29 Huang m X, He B B.Journal of materials Science & Technology, 2018, 34(3), 417.
30 De moor E, matlock D K, Speer J G, et al.Scripta materialia, 2011, 64(2), 185.
31 Hossain R, Pahlevani F, Quadir m Z, et al.Scientific Reports, 2016, 6, 34958.
32 Zhu J, Ding R, He J, et al.Scripta materialia, 2017, 136, 6.
33 He B B, Luo H W, Huang m X.International Journal of Plasticity, 2016, 78, 173.
34 Lee S, Estrin Y, De Cooman B C.metallurgical and materials Transactions A, 2014, 45(2), 717.
35 Choi H, Lee S, Lee J, et al.materials Science and Engineering: A, 2017, 687, 200.
36 Li X, Song R, Zhou N, et al.materials Science and Engineering: A, 2018, 709, 97.
37 Furukawa T.materials Science and Technology, 1989, 5(5), 465.
38 Karbasian H, Tekkaya A E.Journal of materials Processing Technology, 2010, 210(15), 2103.
39 Chang Y, Wang C Y, Zhao K m, et al.materials & Design, 2016, 94, 424.
40 Li X, Chang Y, Wang C, et al.materials Science and Engineering: A, 2017, 679, 240.