Abstract Magnesium and its alloys are the lightest structural metals, which meet requirements for weight loss, energy saving and emission reduction. Magnesium alloys exhibits advantages of high damping capacity, perfect castability and weldability, positive thermal and electrical conductivity, and recyclability. Compared with aluminum alloys widely used at present, the use of magnesium alloys can meet the requirements of mechanical properties at the same time achieves effect of weight reduction and is beneficial to environment.
Magnesium alloys have broad application prospects,however, the widespread usage of magnesium alloys is limited by the characteristics of high affinity with oxygen and prone to form porous oxide scales on surface. Thus, it is of great significance to research the high temperature oxidation resistance of magnesium alloys.
Nowadays, investigations on high temperature oxidation of magnesium alloys mainly concentrate in the following aspects: (1) research on the oxidation behaviors of magnesium alloys at different temperatures; (2) effect of alloy-elements on high temperature oxidation resistance of magnesium alloys; (3) oxidation behaviors of magnesium alloys at different states (liquid/solid). So, in order to broaden the application of magnesium alloys, it is necessary to show a comprehensive summary on oxidation resistance and mechanism of magnesium alloys.
The present paper aims to review the research of home and abroad on high temperature oxidation of magnesium alloys. The oxidation beha-viors, effect of alloy-elements on high temperature oxidation resistance, oxidation mechanism of magnesium alloys,and reasons for failure of protective oxide film are discussed.

Key words： magnesium alloy high temperature oxidation alloying oxide film oxidation mechanism

Published: 10 January 2023 Online: 2023-01-31

CLC number:

TG146.2

Fund:National Natural Science Foundation of China (52274377).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	LI Duojiao
	CHENG Chunlong
	LE Qichi
	CHEN Liang
	YAN Jiashi

Cite this article:

LI Duojiao,CHENG Chunlong,LE Qichi, et al. Research Progress on Oxidation Mechanism of Magnesium Alloys[J]. Materials Reports, 2023, 37(1): 20120108-9.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.20120108 OR http://www.mater-rep.com/EN/Y2023/V37/I1/20120108

1 Mehra D, Mahapatra M M, Harsha S P. Journal of Magnesium and Alloys, 2018, 6(1), 100.
2 Ali Y, Qiu D, Jiang B, et al. Journal of Alloys and Compounds, 2015, 619, 639.
3 Luo K, Effect of Y and Gd content on the microstructure and mechanical properties of Mg-Y-RE alloys. Master’s Thesis, Shanghai Jiao Tong University, China, 2019(in Chinese).
骆康. Y与Gd含量对Mg-Y-RE铸造镁合金微观组织与力学性能的影响. 硕士学位论文. 上海交通大学, 2019.
4 Yeganeh M, Mohammadi N. Journal of Magnesium and Alloys, 2018, 6(1), 59.
5 Ji H, Liu W C, Wu G H,, et al. Materials Science & Engineering A, 2018, 739, 395.
6 Lyu J B, Kim J, Liao H X, et al. Materials Science & Engineering A, 2020, 773, 138735.
7 Du J Q, Lan Z Q, Zhang H, et al. Journal of Alloys and Compounds, 2019, 802, 667.
8 Ning H, Zhou X Y, Zhang Z Y, et al. Applied Surface Science, 2019, 464, 644.
9 Homma T, Kunito N, Kamado S. Scripta Materialia, 2009, 61(6), 647.
10 Itoi T, Takahashi K, Moriyama H, et al. Scripta Materialia, 2008, 59(10), 1155.
11 Wang J F, Song P F, Huang S, et al. Materials Letters, 2013, 93, 415.
12 Pan H, Pan F, Xiao W, et al. International Journal of Thermophysics, 2013, 34(7), 1336.
13 Pan H, Pan F, Wang X. Materials Science and Technology: MST: A Publication of the Institute of Metals, 2014, 918, 165614.
14 Lentz M, Coelho R S, Camin B, et al. Materials Science and Engineering A, 2014, 610(29), 54.
15 Li J, Yang Y, Deng H, et al. Journal of Alloys and Compounds, 2020, 823, 153839.
16 Czerwinski F. Corrosion Science, 2014, 86, 1.
17 Mordike B L, Ebert T. Materials Science and Engineering A, 2001, 302, 37.
18 Ren P L. Advanced Materials Industry, 2014(4), 45(in Chinese).
任朋立. 新材料产业, 2014(4), 45.
19 Yu X, Jiang B, Yang H, et al. Applied Surface Science, 2015, 353, 1013.
20 Kondori B, Mahmudi R. Metallurgical & Materials Transactions A, 2009, 40(8), 2007.
21 Luo A A. Metallurgical Reviews, 2014, 49(1), 13.
22 Pan N, Wei Y H, Hou L F, et al. Transactions of Materials and Heat Treatment, 2013(3), 67(in Chinese).
潘娜, 卫英慧, 侯利锋, 等. 材料热处理学报, 2013(3), 67
23 Czerwinski F. Acta Materialia, 2002, 50(10), 2639.
24 Medved J, Mrvar P, Vonina M. Oxidation of Metals, 2009, 71(5-6), 257.
25 Zhou L H. Transactions of Nonferrous Metals Society of China, 2009, 19(2), 299.
26 Fan J F, Cheng S L, Xie H, et al. Metallurgical & Materials Transactions A, 2005, 36(1), 235.
27 Wang X M, Zeng X Q, Wu G S, et al. Applied Surface Science, 2007, 253(22), 9017.
28 Zou Y L. Research of an ignition-proof magnesium alloy with rare earth addition. Master’s Thesis, Chongqing University, China, 2003(in Chinese).
邹永良. 稀土阻燃镁合金的研究. 硕士学位论文, 重庆大学, 2003.
29 Czerwinski F. International Materials Reviews, 2015, 60(5), 264.
30 Lee D B. Corrosion Science, 2013, 70, 243.
31 Li Q, Wang Q, Wang Y, et al. Journal of Alloys & Compounds, 2007, 427(1-2), 115.
32 Xing Q Y, Meng L G, Yang S J, et al. Foundry, 2018, 67(4), 317(in Chinese).
邢清源, 孟令刚, 杨守杰, 等. 铸造, 2018, 67(4), 317.
33 Wu L Y. The research on microstructure, properties at high temperature for Mg-Gd-Y-Zn alloy. Ph. D. Thesis, Hunan University, China, 2012(in Chinese).
吴落义. Mg-Gd-Y-Zn系合金的微观组织与高温性能研究. 博士学位论文, 湖南大学, 2012.
34 Tan Q, Atrens A, Mo N, et al. Corrosion Science the Journal on Environmental Degradation of Materials & Its Control, 2016, 112, 734.
35 Tan Q Y. Surface Innovations, 2019, 7(2), 71.
36 Fournier V, Marcus P, Olefjord I. Surface and Interface Analysis, 2002, 34(1), 494.
37 Czerwinski F. JOM, 2012, 64(12), 1477.
38 Gulbransen E A. Transaction of the Electrochemical Society, 2015, 87(1), 589.
39 Czerwinski F. JOM, 2004, 56(5), 29.
40 Wang X F, Xiong S M. Transactions of Nonferrous Metals Society of China, 2011, 21(4), 807.
41 Jeurgens L P H, Vinodh M S, Mittemeijer E J. Acta Materialia, 2008, 56(17), 4621.
42 Rao J S. Study on oxidation behavior of ignition-proof magnesium alloy added with RE. Ph. D. Thesis, Chongqing University, China, 2010(in Chinese).
饶劲松. 混合稀土阻燃镁合金氧化行为的研究. 博士学位论文. 重庆大学, 2010.
43 Zeng R C. Material corrosion and protection, Chemical Industry Press, China, 2006(in Chinese).
曾荣昌. 材料的腐蚀与防护, 化学工业出版社, 2006.
44 Breiter A L, Mal'Tsev V M, Popov E I. Combustion, Explosion and Shock Waves, 1977, 13(4), 475.
45 Cheng C, Lan Q, Liao Q, et al. Corrosion Science, 2019, 160, 108176.
46 Czerwinski F, Szpunar J A. Acta Materialia, 1998, 46(4), 1403.
47 Lee D B. Oxidation of Metals, 2016, 8(1-2), 65.
48 Jang D I, Kim S K. Essential readings in magnesium technology, Springer International Publishing, Germany, 2016, pp. 145.
49 Inoue S I, Yamasaki M, Kawamura Y. Corrosion Science, 2017, 122, 118.
50 Tan Q, Mo N, Jiang B, et al. Corrosion Science, 2017, 122, 1.
51 Han D, Zhang J, Huang J F, et al. Journal of Magnesium and Alloys, 2020, 8(2), 329.
52 Inoue S, Yamasaki M, Kawamura Y. Corrosion Science, 2017, 112, 118.
53 Cheng C, Li X, Le Q, et al. Journal of Magnesium and Alloys, 2020, 8(4), 1281.
54 Dai J H. Investigation on diffusion behaviors of alloy elements in magne-sium. Ph. D. Thesis, Chongqing University, China, 2016(in Chinese).
戴甲洪. 合金元素在镁合金中扩散行为的研究. 博士学位论文, 重庆大学, 2016.
55 Fan C. The study on the oxidation kinetics of the rare-earth magnesium alloy. Master’s Thesis, Chongqing University, China, 2006(in Chinese).
范超. 混合稀土阻燃镁合金氧化动力学的研究. 硕士学位论文, 重庆大学, 2006.
56 Hao X B. The study on ignition-proof behavior and strengthening mechanism of magnesium alloy. Master’s Thesis, Hebei University of Technology, China, 2008(in Chinese).
郝孝博. 镁合金阻燃行为及其强化机理的研究. 硕士学位论文, 河北工业大学, 2008.
57 He Y D, Qi H B. Introduction to material corrosion and protection, Machinery Industry Press, China, 2005(in Chinese).
何业东, 齐慧滨. 材料腐蚀与防护概论, 机械工业出版社, 2005.
58 Inoue S I, Yamasaki M, Kawamura Y. Corrosion Science, 2019, 149, 133.
59 Isshiki M, Irifune T, Kei H, et al. Nature: International Weekly Journal of Science, 2004, 427(6969), 60.
60 Czerwinski F. Corrosion Science, 2004, 46(2), 377.
61 Huang H, Yuan G, Chu Z, et al. Materials Science and Engineering A: Structural Materials: Properties, Microstructure and Processing, 2013, 560, 241.
62 Pan F S, Han E H. High-performance wrought magnesium alloy and processing technology, Science Press, China, 2007(in Chinese).
潘复生, 韩恩厚. 高性能变形镁合金及加工技术, 科学出版社, 2007.
63 Kim Y M, Yim C D, Kim H S, et al. Scripta Materialia, 2011, 65(11), 958.
64 Han D, Zhang J, Huang J, et al. Journal of Magnesium and Alloys, 2020, 8(2), 329.
65 Inoue S I, Yamasaki M, Kawamura Y. Corrosion Science, 2020, 174, 108858.
66 Czerwinski F. Journal of the Electrochemical Society, 1993, 140(9), 2606.
67 Fan J F, Yang G C, Zhou R H, et al. The Chinese Journal of Nonferrous Metals, 2006, 16(10), 1716(in Chinese).
樊建锋, 杨根仓, 周尧和, 等. 中国有色金属学报, 2006, 16(10), 1716.
68 Kiejna A, Wojciechowski K F. Journal of Physics C Solid State Physics, 1983, 16(35), 6883.
69 Aydin D S, Bayindir Z, Pekguleryuz M O. Journal of Materials Science, 2013, 48(23), 8117.
70 Yamauchi H. Physical Review B-Condens Matter, 1985, 31(12), 7688.
71 Ren F, Cao K, Ren J, et al. Journal of Computational and Theoretical Nanoscience, 2014, 11(2), 344.