316L不锈钢表面激光熔覆Stellite6合金组织及其耐液态铅铋腐蚀性能

doi:10.11896/cldb.20010039

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (8524KB)
Export: BibTeX | EndNote (RIS)

Abstract Stellite6 alloy coating was prepared on the surface of 316L stainless steel by laser cladding with coaxial feeding powder, which aims to improve the Pb-Bi erosion resistance property of the 316L stainless steel. The Stellite6 alloy coating was placed in liquid Pb-Bi at 400 ℃ high speed flow corrosion test for 500 h, The relative flow rate was set at 2.56 m/s. The coating microstructure, phase composition, element distribution, hardness distribution and the Pb-Bi erosion resistance property were studied, the results show that the microstructure of the coating is composed of equiaxed, dendritic, cellular and planar crystals, and the grains in the overlap zone grow in different directions. The coating mainly includes γ-Co, CoC_x, (Cr,Fe)₇C₃ and M₂₃C₆ phases, each component element distributed on the coating surface evenly, Co, Cr and Fe elements diffuse between the 316L substrate and the coating layer obviously. The average hardness of the Stellite6 coating is 2.3 times that of the 316L substrate, and the highest hardness is 556.8HV. After the high-speed liquid Pb-Bi corrosion, large and continuous oxides are generated on the surface of 316L stainless steel, and there is a large number of micro-corrosion pits. The surface of Stellite6 coating is well maintained with a small amount of oxides existed and no obvious corrosion pits founded. Stellite6 coating surface roughness is 1.0 μm,while 316L surface roughness is 2.4 μm. Stellite6 alloy coating can effectively improve the corrosion resistance of 316L stainless steel matrix in high temperature liquid Pb-Bi alloy.

Key words： laser cladding Stellite6 coating Pb-Bi corrosion resistance property

Published: 10 May 2021

CLC number:

TG146.1+6

Fund:National Natural Science Foundation Youth Found of China (51505197), Equipment Pre-research Field Fund Project (JZX7Y20190263074601).

About author:: Yanchao Zhang is a master degree candidate in Jiangsu University, his tutor is Qiang Zhu. He is engaged in researching on the laser cladding technology and corrosion of nucelear materials in lead-bismuth eutectic alloy.
Qiang Zhu is an associate professor in Jiangsu University, He is mainly engaged in the research and the development of welding technology, advanced connection technology. He has published more than 20 journal papers and authorized 3 national invention patents.

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	ZHANG Yanchao
	WEI Pengyu
	ZHU Qiang
	ZHAO Wentao
	LI Tianqing
	ZENG Qingbo

Cite this article:

ZHANG Yanchao,WEI Pengyu,ZHU Qiang, et al. Microstructure and Pb-Bi Erosion Resistance Property of Stellite6 Coating by Laser Cladding on 316L Stainless Steel Surface[J]. Materials Reports, 2021, 35(8): 8121-8126.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.20010039 OR http://www.mater-rep.com/EN/Y2021/V35/I8/8121

1 Chen X C, Li S, Ren X L, et al. Energy and Energy Conservation,2018,155(8),58(in Chinese).
陈小砖,李硕,任晓利,等.能源与节能,2018,155(8),58.
2 Rong L J, Zhang Y T, Lu S P. Handbook on lead-bismuth eutectic alloy and lead-properties, materials compatibility, thermal-hydraulics and technologies, Science Press, China,2014(in Chinese).
戎利建,张玉妥,陆善平.铅与铅铋共晶手册-性能,材料相容性,热工水力学和技术,科学出版社,2014.
3 Martinelli L, Dufrenoy T, Jaakou K, et al. Journal of Nuclear Materials,2008,376(3),282.
4 Wu Y C, Huang Q Y, Bai Y Q, et al. Nuclear Science and Engineering,2010,30(3),238(in Chinese).
吴宜灿,黄群英,柏云清,等.核科学与工程,2010,30(3),238.
5 Zhu Q, Zhao J, Lei Y C, et al. Surface Technology,2019,48(1),234(in Chinese).
朱强,赵军,雷玉成,等.表面技术,2019,48(1),234.
6 Park J J, Butt D P, Beard C A. Nuclear Engineering and Design,2000,196(3),315.
7 Fazio C, Benamati G, Martini C, et al. Journal of Nuclear Materials,2001,296(1),243.
8 Konys J, Muscher H, et al. Journal of Nuclear Materials,2001,296(1-3),289.
9 Xu Y L, Long B, Atomic Energy Science and Technology,2003,37(4),325(in Chinese).
许咏丽,龙斌.原子能科学技术,2003,37(4),325.
10 Shi J, Liu F, Wang W G, et al. Hot Working Technology,2016(20),93(in Chinese).
时健,刘峰,王望根,等.热加工工艺,2016 (20),93.
11 Muller G, Schumacher G, Zimmermann F. Journal of Nuclear Materials,2000,278(1),85.
12 Huang F, Lei Y C, Lu C, et al. Journal of Functional Materials,2017(1),1199(in Chinese).
黄飞,雷玉成,陆超,等.功能材料,2017(1),1199.
13 Zhang D Q, Niu X L, Li J H, et al. Machinery Design & Manufacture,2015,(6),105(in Chinese).
张德强,牛兴林,李金华,等.机械设计与制造,2015,(6),105.
14 Wang D S, Tian Z J, Shen L D, et al. Applied Laser,2012(6),85(in Chinese).
王东生,田宗军,沈理达,等.应用激光,2012(6),85.
15 Ren C, Li Z G, Shu D, et al. Chinese Journal of Lasers,2017,44(4),0402010(in Chinese).
任超,李铸国,疏达,等.中国激光,2017,44(4),0402010.
16 D′oliveiraa S C, Silva P S C, Vilarr M. Surface and Coatings Technology,2002,153(2),203.
17 Pant B K, Mann B S. Journal of Materials Engineering & Performance,2012,21(6),1051.
18 Tian S J, Zhang J W. Journal of University of Science and Technology of China,2015,(9),751(in Chinese)
田书建,张建武.中国科学技术大学学报,2015,(9),751.
19 Woodford D A. Metallurgical Transactions,1972,3(5),1137.