| Surface Corrosion Behavior of Ni60A/WC Laser Cladding Coating |
| XIAO Qi, SUN Wenlei, LIU Jinduo, HUANG Haibo
|
| School of Mechanical Engineering, Xinjiang University, Urumqi 830047, China |
|
|
|
|
Abstract Roller bit is an important part of drilling equipment which is vulnerable to wear and corrosion. In order to extend the service life of the roller bit, the strengthen layer can be fabricated by laser cladding. In this paper, Ni60A coating and 5wt%,15wt%,25wt% WC reinforced Ni based coatings were prepared on 15CrNiMo steel by YLS-2000 laser instrument. Furthermore, the microstructure and element distribution of the coatings were analyzed by means of SEM and EDS. And the phase composition of each coating was investigated by XRD. Meanwhile, the electrochemical corrosion test was performed on a CHI660E type electrochemical workstation. The effect of WC content on the microstructure and corrosion resis-tance of Ni60A/WC cladding layer was studied, and the corrosion behavior of Ni60A/WC cladding layer and substrate in different pH corrosion solution was discussed. The results show that with the increase of WC content, micro area directional solidification appears in the coatings. In addition, the γ(Fe, Ni) and intermetallic compound of M23C6, M6C, et al are observed in Ni60A/WC layers. What's more, compared with the substrate, the corrosion current density of Ni60A/WC coating in different pH value corrosion solution is reduced by 1—2 orders of magnitude which perform good corrosion resistance, but its corrosion resistance is negatively related to the addition of WC. Besides, enrichment of H+ and OH- surroundings make the passivation film change from low valent oxide to superoxide.
|
|
Published: 10 May 2021
|
|
|
| Fund:Xinjiang Karamay Major Special Project (2018ZD002B). |
About author:: Qi Xiao is a graduate student of 2018 from Xinjiang University. He specializes in laser cladding remanufacturing and surface modification of materials.
Wenlei Sun is a doctor and professor who is mainly engaged in digital design and manufacturing,additive remanufacturing technology research and other aspects of research. |
|
|
1 Wang D, Wang Y M, Yang Y Q, et al. Journal of Materials Processing Technology,2019,273,116277.
2 Long Y T, Nie P L, Li Z G, et al. Transactions of Nonferrous Metals Society of China,2016,26(2),431.
3 Zhang X Y, Pfeiffer S, Rutkowski P, et al. Applied Surface Science,2020,520,146340.
4 Fan P F, Zhang G. International Journal of Refractory Metals and Hard Materials,2020,87,105133.
5 Zhou Y K, Liu X B, Kang J J, et al. Engineering Failure Analysis,2020,109,10438.
6 Zhou J L, Kong D J, Journal of Alloys and Compounds,2019,795,416.
7 Bartkowski D, Ynarczak A, Piasecki A, et al. Optics & Laser Technology,2015,68,191.
8 Liu J, Liu H, Tian X, et al. Journal of Alloys and Compounds,2020,822,153708.
9 Wang X, Zhou S F, Dai X, et al. International Journal of Refractory Metals and Hard Materials,2017,64,234.
10 Chaidemenopoulos N G, Psyllaki P P, Pavlidou E, et al. Surface and Coatings Technology,2019,357,651.
11 Liu X M. Applied Laser,2006(5),299(in Chinese).
刘喜明.应用激光,2006(5),299.
12 Zhou S F, Dai X Q, Zhen H Z, et al. Journal of Mechanical Enginee-ring,2012,48(7),113(in Chinese).
周圣丰,戴晓琴,郑海忠,等.机械工程学报,2012,48(7),113.
13 Wang Y, Li K Y, Scenini F, et al. Surface and Coatings Technology,2016,302,27.
14 Zhao M Q, Lei A L. Corrosion and protection of metal, National Defense Industry Press, China,2008(in Chinese).
赵麦群,雷阿丽.金属的腐蚀与防护,国防工业出版社,2008.
15 Seo D, Lee J B, Corrosion Science,2020,173,108789. |
|
|
|
渝公网安备50019002502923号 © Editorial Office of Materials Reports.
2021, Vol. 35 