Metals and Metal Matrix Composites |
|
|
|
|
|
Research Status in Light-weight High-entropy Alloys |
LI Meng1, YANG Chengbo1, ZHANG Jing1,*, ZHENG Kaihong2
|
1 College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China 2 Guangdong Institute of Materials and Processing, Guangzhou 510651, China |
|
|
Abstract As a brand-new type of multi-principal component solid solution alloy, high-entropy alloys (HEAs) have drawn widely attention of researchers due to their unique alloy design concept and amazing performances, which has become a hot spot in current material research. Among them, light-weight high-entropy alloys (LWHEAs) are thought to be a novel kind of light-weight alloy materials developed based on the light-weight design of HEAs. They feature high specific strength and excellent specific hardness in general, which is superior to most traditional lightweight alloys, implicating great application potential in the fields of aerospace, energy transportation and electronic communication. However, the current research of LWHEAs is still at an exploratory stage, and two stern challenges encountered in developing LWHEAs: (ⅰ)in terms of the alloy design, most LWHEAs are developed by a trial-and-error method based on the empirical criteria of traditional HEAs consist of transition metal elements, and reliable methods for guiding the design of LWHEAs are not available; (ⅱ) in terms of the preparation technology, it is difficult to produce bulk LWHEA materials with simple microstructures and exceptional properties by using the current preparation methods. Hitherto, almost 100 kinds of LWHEAs have been explored experimentally by researchers. And they have been striving to search for suitable empirical criteria for predicting the phase structure of LWHEAs, which involving many thermos-physical parameters such as the mixing entropy (ΔSmix), the mixing enthalpy(ΔHmix), the atom radius difference(δ), and the valence electron concentration(VEC).More recently, the use of computer simulation methods to assist LWHEA design begins to develop gradually and shows apparent advantages, for instance, utilizing phase diagram calculation (CALPHAD) and first-principles calculation (DFT) to predict the phase formation and phase transition of LWHEAs. Although the vacuum casting provides a simple route to obtain bulk LWHEAs, many LWHEAs prepared from which display a multi-phased microstructure. Works in the past years have established a new avenue to overcome the complex microstructures, by introducing mechanical alloying process, which have successfully achieved the reduced tendency of alloys to form complex phases such as intermetallic compounds (IM), and produced LWHEAs with simpler phase constitutions. Besides, although most as-cast LWHEAs generally manifest complex multi-phased microstructure with poor plasticity, the Al-rich (or Mg-rich) LWHEAs,according to the existing data, form simple microstructures very often with a dominated solid solution (SS) phase and traces of IM phase, and in consequence show the potential for a good combination of strength and ductility. In this review, according to the current research status in LWHEAs, the light elements selection rule is first summarized. Also, the recent deve-lopment of LWHEAs including alloy design methods, preparation processes, microstructures and properties are summed up. In addition, the empirical phase formation rules about LWHEAs design also are analyzed in details, especially, the phase formation rules suitable to Ⅰ-type and Ⅱ-type LWHEAs respectively are proposed, which is supposed to guide future LWHEAs design. Finally, the main problems of LWHEAs are discussed and future research directions in LWHEAs are suggested.
|
Published: 17 November 2020
|
|
Fund:This work was financially supported by the Fundamental Research Funds for the Central Universities (2018CDPTCG0001/42). |
About author:: Meng Li received her B.E. degree in metal material engineering from Xi'an Technological University in 2017. She is currently pursuing her M.S. at the College of Materials Science and Engineering, Chongqing University under the supervision of Prof. Jing Zhang. Her research has focused on light-weighthigh-entropy alloys. Jing Zhang received her Ph.D. degree in materials science from Chongqing University in 1999. During 2000 to 2001 she worked at the National High Resolution Electron Microscopy Center in Delft University of Technology of the Netherlandas a postdoctoral research fellow. She also has two-year collaborative research experience in University of London, UK.Since 2007 she has been a full professor in Chongqing University, and currently she is the vice director of the National Engineering Research Center for Magnesium Alloys. Her research interests include magnesium alloys, aluminum alloys and light-weight high-entropy alloys. |
|
|
[1] |
Zhu L, Li N, Childs P R N.Propulsion and Power Research, 2018, 7(2), 103.
|
[2] |
Hirsch J, Al-Samman T. Acta Materialia, 2013, 61(3), 818.
|
[3] |
Cantor B, Chang I T H, Knight P, et al. Materials Science and Enginee-ring A, 2004, 375, 213.
|
[4] |
Yeh J W, Chen S K, Lin S J, et al. Advanced Engineering Materials, 2004, 6(5), 299.
|
[5] |
Tsai M H,Yeh J W. Materials Research Letters, 2014, 2(3), 107.
|
[6] |
Zhang Y, et al. Progress in Materials Science, 2014, 61, 1.
|
[7] |
Senkov O N,Miller J D,Miracle D B, et al. Nature Communications, 2015, 6, 6529.
|
[8] |
Fu X, Schuh C A, Olivetti E A. Scripta Materialia, 2017, 138, 45.
|
[9] |
Youssef K M, et al. Materials Research Letters, 2015, 3(2), 95.
|
[10] |
Zhang Y, Zhou Y J, Lin J P, et al. Advanced Engineering Materials, 2008, 10(6), 534.
|
[11] |
Guo S, Hu Q, Ng C, et al. Intermetallics, 2013, 41, 96.
|
[12] |
Yang X, Zhang Y. Materials Chemistry and Physics, 2012, 132, 233.
|
[13] |
Zhang Y, Yang X, Liaw P K. JOM, 2012, 64(7), 830.
|
[14] |
Ye Y F,Wang Q,Lu J, et al. Scripta Materialia, 2015, 104, 53.
|
[15] |
Singh A K, Kumar N, Akanksha D, et al. Intermetallics, 2014, 53, 112.
|
[16] |
King D J M, et al. Acta Materialia, 2016, 104, 172.
|
[17] |
Senkov O N, Miracle D B. Journal of Alloys and Compounds, 2016, 658, 603.
|
[18] |
Takeuchi A, Inoue A.Materials Transactions, 2005, 46(12), 2817.
|
[19] |
Guo S.Materials Science and Technology, 2015, 31(10), 1223.
|
[20] |
Yang X, Chen S Y, Cotton J D, et al. JOM, 2014, 66(10), 2009.
|
[21] |
Miracle D B, Senkov O N. Acta Materialia, 2017, 122, 448.
|
[22] |
Huang X J, Miao J S, Luo A A. Journal of Materials Science, 2019, 54(3), 2271.
|
[23] |
Feng R, Gao M C, Lee C, et al. Entropy, 2016, 18(9), 333.
|
[24] |
Stepanov N D, Yurchenko N Y, Shaysutanov D G, et al. Materials Science and Technology, 2015, 31(10), 1184.
|
[25] |
Stepanov N D, Yurchenko N Y, Skibin D V, et al. Journal of Alloys and Compounds, 2015, 652, 266.
|
[26] |
Stepanov N D, et al. Materials Letters, 2015, 142,153.
|
[27] |
Jayaraj J, Thirathipviwat P, Han J, et al. Intermetallics, 2018, 100, 9.
|
[28] |
Chen W,Tang Q H,Wang H, et al. Materials Science and Technology, 2018, 34(11), 1309.
|
[29] |
Qiu Y, Hu Y J, Taylor A, et al. Acta Materialia, 2017, 123, 115.
|
[30] |
Kang M J, Lim K R, Won J W, et al. Entropy, 2018, 20(5), 355.
|
[31] |
Bolbut V, Wessel E, Kruger M. Scripta Materialia, 2018, 150, 54.
|
[32] |
Menou E,Tancret F, et al. Scripta Materialia, 2018, 156, 120.
|
[33] |
Tseng K K, Yang Y C, Juan C C, et al. Science China Technological Sciences, 2018, 61(2), 184.
|
[34] |
Li R, Gao J C, Fan K.Materials Science Forum, 2010, 650, 265.
|
[35] |
Du X H, et al. Key Engineering Materials, 2017, 727, 132.
|
[36] |
Jia Y F,Jia Y D, Wu S W, et al. Materials, 2019, 12(7), 1136.
|
[37] |
Li R X, Wang Z, et al. Science China Materials, 2019, 62, 736.
|
[38] |
Shao L, Zhang T, Li L, et al. Journal of Materials Engineering and Performance, 2018,27(12), 6648.
|
[39] |
Jon M S, Iban V, Joseba A, et al. Metals, 2018, 8(3), 167.
|
[40] |
Gao X Q, Zhao K, Ke H B, et al. Journal of Non-Crystalline Solids, 2011, 357(21), 3557.
|
[41] |
Chen Y L, Tsai C W, Juan C C, et al. Journal of Alloys and Compounds, 2010, 506(1), 210.
|
[42] |
Hammond V H, Atwater M A, Darling K A. et al. JOM, 2014, 66, 2021.
|
[43] |
Maulik O, Kumar V. Materials Characterization, 2015, 110, 116.
|
[44] |
Maulik O, Kumar D, Kumar S, et al. Intermetallics, 2016, 77, 46.
|
[45] |
Tan X R, Zhang G P, et al. Materials and Design, 2016, 109, 27.
|
[46] |
Ge W J, et al. Journal of Iron and Steel Research, 2017, 24(4), 448.
|
[47] |
Zepon G, Leiva D R, Strozi R B, et al. International Journal of Hydrogen Energy, 2018, 43(3), 1702.
|
[48] |
Wang W, Li B Y, Zhai S C, et al. Metals and Materials International, 2018, 24(5), 1112.
|
[49] |
Liang S M, Rainer S F. Journal of Phase Equilibria and Diffusion, 2017, 38(4), 369.
|
[50] |
Tan Y M, et al. Journal of Alloys and Compouds, 2018, 742, 430.
|
[51] |
Guo S, Ng C, Lu J, et al. Journal of Applied Physics, 2011, 109(10), 103505.
|
[52] |
Takeuchi A, Amiya K, Wada T, et al. JOM, 2014, 66(10), 1984.
|
[53] |
Kube S A, Sohn S, Uhl D, et al. Acta Materialia, 2019, 166, 677.
|
[54] |
Zhao Y J, Qiao J W, Ma S G, et al. Materials & Design, 2016, 96, 10.
|
[55] |
Zhang F, Zhang C, Chen S L, et al. CALPHAD: Computer Coupling of Phase Diagrams and Thermochemistry, 2014, 45, 1.
|
[56] |
Sun W H, Huang X J, Luo A A. CALPHAD: Computer Coupling of Phase Diagrams and Thermochemistry, 2017, 56, 19.
|
[57] |
Rui F, Gao M C, Chuan Z, et al. Acta Materialia, 2018, 146, 28.
|
[58] |
Rui F, et al. NPJ Computational Materials, 2017, 3, UNSP 50.
|
[59] |
Tian F Y, Delczeg L, et al. Physical Review, 2013, 88, 085128.
|
[60] |
Yadav S, Sarkar S, Aggarwal A, et al. Wear, 2018, 410, 93.
|
[61] |
Suryanarayana C. Progress in Materials Science, 2001, 46(1-2), 1.
|
[62] |
Varalakshmi S, Kamaraj M, Murty B S. Journal of Alloys and Compouds, 2008, 460(1-2), 253.
|
[63] |
Tan X R, Zhao R F, Ren B, et al. Materials Science and Technology, 2016, 32(15), 1582.
|
|
|
|