METALS AND METAL MATRIX COMPOSITES |
|
|
|
|
|
Constitutive Equation and Thermal Processing Map of Spray Formed AlSi25Cu4Mg Wear Resistant Alloy |
HU Yusheng1,2, FENG Di3, ZHOU Jiandang4, ZHU Tian3, ZHANG Hao4, ZHANG Jie4, FAN Xi4, SONG Feidao4
|
1 State Key Laboratory of Air-conditioning Equipment and System Energy Conservation, Zhuhai 519070, China 2 Gree Electric Appliances,Inc.of Zhuhai, Zhuhai 519000, China 3 School of Materials Science and Engineering, Jiangsu University of Science and Technology, Zhenjiang 212003, China 4 Jiangsu Haoran Spray Forming Alloy Co, Zhenjiang 212003, China |
|
|
Abstract The hot deformation behavior of a spray formed AlSi25Cu4Mg wear resistant alloy were investigated using Gleeble-3500 test machine at 623—723 K with strain rates from 0.001 s-1 to 5 s-1, and the constitutive equation including Zener-Hollomon parameter (Z parameter) and processing map were established. Results revealed that the activation energy of the spray formed high Si content aluminum alloy was 194.8 kJ/mol, the flow stress rises with the decreasing of deformation temperature and the increase of strain rate. Processing map exhibited a high power dissipation degree of 31%, which indicates a high dynamic soften degree when the alloy deformed with low Z parameter values. The spray formed AlSi25Cu4Mg alloy showed an excellent deformation ability during hot extrution with the temperature range of 713—723 K and the strain rate below 1 s-1. After aging, the tensile strength along extrusion direction of thealloy was 487 MPa. The hardness has reached to 187HV, which satisfies the property requirement.
|
Published: 26 April 2020
|
|
Fund:This work was financially supported by the State Key Laboratory of Air-conditioning Equipment and System Energy Conservation (ACSKL2018KT15), the National Natural Science Foundation Youth Fund of China (51801082), the Provincial Natural Science Foundation of Jiangsu (BK20160560). |
Corresponding Authors:
Di Fengreceived his Ph.D. degree in materials from Central South University in December 2014. He is currently an associate professor in Jiangsu University of Science and Technology. His research interests are the theoretical and applied research of high performance aluminum alloy.
|
About author:: Yusheng Hu, male, professor of engineering, focusing on the research of compressor,motor and equipment technology. |
|
|
1 Gan W P, Liu H, Yang F L.Materials Review, 2006, 20(3), 126(in Chinese). 甘卫平, 刘泓, 杨伏良. 材料导报, 2006, 20(3), 126. 2 Choi S W, Cho H S, Kumai S.Journal of Alloys and Compounds, 2016, 655, 6. 3 Lin G Y, Lei Y X, Guo D Q, et al.The Chinese Journal of Nonferrous Metals, 2014,24(3), 584(in Chinese). 林高用, 雷玉霞, 郭道强, 等. 中国有色金属学报, 2014, 24(3), 584. 4 Li P W, Li H Z, Liang X P, et al. Materials Science & Engineering A, 2018,732, 341. 5 Yu H, Cheng R F, Hang X M, et al.Transactions of Materials and Heat Treatment, 2012, 33(12), 58(in Chinese). 于浩, 程如法, 黄笑梅,等. 材料热处理学报, 2012, 33(12),58(in Chinese). 6 Li Y Z, Du X F, Sun J. Materials Science and Engineering of Powder Metallurgy, 2015, 20(3), 331(in Chinese). 李永志, 都学飞, 孙静. 粉末冶金材料科学与工程, 2015, 20(3),331. 7 Su J H. Study on microstructure and properties of high performance hype-reutectic Al-Si-Cu-Mg alloy. Master's Thesis, Shenyang University of Technology, China, 2017(in Chinese). 孙继鸿. 高性能过共晶Al-Si-Cu-Mg合金组织与性能的研究. 硕士学位论文, 沈阳工业大学, 2017. 8 Pan Y P. The study of high strength and toughness Al-Si-Cu-Mg cast alloys on microstructures and mechanical properties. Master's Thesis, Ge-neral Research Institute for Nonferrous Metals, China, 2015(in Chinese). 潘彦鹏. 高强韧铸造Al-Si-Cu-Mg合金组织性能研究. 硕士学位论文, 北京有色金属研究总院, 2015. 9 Zhu Q. Heat treatment process and strengthening mechanism of semi-solid cast Al-Si-Cu-Mg aluminum alloys. Master's Thesis, General Research Institute for Nonferrous Metals, China, 2017(in Chinese). 朱强. 半固态铸造Al-Si-Cu-Mg合金热处理工艺及强化机理研究. 硕士学位论文, 北京有色金属研究总院, 2017. 10 Shi Y J. Study on heat treatment process of semi-solid forming hypereutectic Al-Si-Cu-Mg Alloy. Master's Thesis, Shenyang University of Techno-logy, China, 2018(in Chinese). 史原脊. 半固态成形过共晶Al-Si-Cu-Mg合金热处理工艺研究. 硕士学位论文, 沈阳工业大学, 2018. 11 Yan S F. Study on semi-solid deforming characteristic and forming process of Al-Si-Cu-Mg Alloy. Master's Thesis, Inner Mongolia University of Technology, China, 2005(in Chinese). 闫淑芳. Al-Si-Cu-Mg合金半固态变形特征及成形模拟的研究. 硕士学位论文, 内蒙古工业大学, 2005. 12 Zhen Z S, Zhao A M, Mao W M, et al. The Chinese Journal of Nonferrous Metals, 2000, 10(6), 815(in Chinese). 甄子胜, 赵爱民, 毛卫民, 等. 中国有色金属学报, 2000, 10(6), 815. 13 Zhu Q L. Microstructure evolvement and mechanics behavior of high silicon aluminum alloys prepared by spray deposition. Master's Thesis, Harbin Institute of Technology, China, 2006(in Chinese). 朱奇林. 喷射成形高硅铝合金的组织演变和力学行为. 硕士学位论文, 哈尔滨工业大学, 2006. 14 Fu D F. The process and mechanical properties of high silicon-content aluminum alloy by multi-layer spray deposition technology. Master's Thesis, Central South University, China, 2001(in Chinese). 傅定发.多层喷射沉积高硅铝合金工艺及性能研究. 硕士学位论文, 中南大学, 2001. 15 Sun X B. Study on microstructure and mechanical properties of spray deposited high silicon aluminum alloy. Master's Thesis, Harbin Institute of Technology, China, 2011(in Chinese). 孙晓兵. 喷射成形高硅铝合金组织及性能研究. 硕士学位论文, 哈尔滨工业大学, 2011. 16 Feng D, Zhang X M, Liu S D. Rare Metal Materials and Engineering, 2016, 45(8), 2104(in Chinese). 冯迪, 张新明, 刘胜胆, 等. 稀有金属材料与工程, 2016, 45(8), 2104. 17 Feng D, Wang G Y, Chen H M, et al.Metal and Materials International, 2018, 24(1), 195. 18 Shaha S K, Czerwinski F, Kasprzak W, et al.Materials Science & Engineering A, 2016, 657, 441. |
|
|
|