超高韧性氯氧镁水泥基复合材料的耐水性能

doi:10.11896/cldb.18070111

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (3081KB)
Export: BibTeX | EndNote (RIS)

Abstract To improve the inherent brittleness and poor water resistance of the magnesium oxychloride cement (MOC) based composites, ultra-high toughness MOC composites (MOC-UHTC) was developed with the help of specially treated polyethylene (PE) fibers under the guidance of micromechanical design principle. The tensile, compressive and single-fiber pullout tests of materials in the four replacement ratio of fly ash (20%, 30%, 40% and 60%) were conducted. The effect of the replacement ratio of fly ash on the mechanical properties, water resistance of the materials was analyzed. And the phase composition of hydration products and the microstructure of the composites in different replacement ratio of fly ash was analyzed by XRD and SEM, respectively. The results indicate that MOC-UHTC exhibits outstanding strain hardening behavior and multi-cracking response. The tensile strain capacity of MOC-UHTC ranged from 5% to 8% with the tensile strength from 4 MPa to 7 MPa. The tensile and compressive strength retention coefficient of the composites exceeded 0.7 and 0.8 respectively, indicating that the water resis-tance was improved due to the addition of fly ash and PE fibers. Moreover, the tensile strain capacity had a certain increase after the composites immersed in water.

Key words： magnesium oxychloride cement fly ash polyethylene fiber strain hardening water resistance

Published: 12 July 2019

CLC number:

TU528.58

Fund:This work was financially supported by the National Natural Science Foundation of China (51478362, 51778461).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	WANG Yichao
	YU Jiangtao
	WEI Linzhuo
	XU Shilang

Cite this article:

WANG Yichao,YU Jiangtao,WEI Linzhuo, et al. Water-resistance Property of Ultra-high Toughness Magnesium Oxychloride Cement-based Composites[J]. Materials Reports, 2019, 33(16): 2665-2670.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.18070111 OR http://www.mater-rep.com/EN/Y2019/V33/I16/2665

[1] Ruan S, Qiu J, Yang E H, et al. Cement and Concrete Composites, 2018, 89, 52.
[2] Deng D, Zhang C. Cement and Concrete Research, 1999, 29 (9), 1365.
[3] Demediuk T, Cole W F, Hueber H V. Australian Journal of Chemistry, 1955, 8(2), 215.
[4] Siddique R, Naik T R. Waste Management, 2004, 24(6), 563.
[5] Li Z, Chau C K. Cement and Concrete Research, 2007, 37(6), 866.
[6] Li C D, Yu H F. Journal of Wuhan University of Technology (Materials Science Edition), 2010, 25(4), 721.
[7] Li Y, Yu H, Zheng L, et al. Construction and Building Materials, 2013, 38, 1.
[8] Deng D. Cement and Concrete Research, 2003, 33(9), 1311.
[9] Tatarczak A. In: Proceedings of the International Conference on Civil, Structural and Transportation Engineering. Canada, 2015, pp. 318.
[10] Li V C, Leung C K Y. Journal of Engineering Mechanics, 1992, 118(11), 2246.
[11] Xu S L, Li H D. China Civil Engineering Journal, 2008, 41(6), 45 (in Chinese).
徐世烺, 李贺东. 土木工程学报, 2008, 41(6), 45.
[12] Yu K, Wang Y, Yu J, et al. Construction and Building Materials, 2017, 137, 410.
[13] Wang Y C, Hou M J, Yu J T. Materials Review B:Research Papers, 2018, 31(10),3535 (in Chinese).
王义超, 侯梦君, 余江滔. 材料导报:研究篇, 2018, 31(10), 3535.
[14] Yu K, Yu J, Dai J, et al. Construction and Building Materials, 2018, 158, 217.
[15] Yu K Q, Li L Z, Yu J T, et al. Engineering Structures, 2018, 170, 11.
[16] Wang Y C, Yu J T, Wang J P, et al. Journal of Wuhan University of Technology, 2017, 39(10), 26 (in Chinese).
王义超, 余江滔, 王建平, 等. 武汉理工大学学报, 2017, 39(10), 26.
[17] Wei L, Wang Y, Yu J, et al. Construction & Building Materials, 2018, 165, 750.
[18] Wang Y C, Wei L Z, Yu J T, et al. Cement and Concrete Composites, 2019, 97, 248.
[19] Xu Y N. Experimental study on tensile, compressive and bionic structural beams of UHDCC. Master’s Thesis, Tongji University, China, 2017 (in Chinese).
徐延宁. UHDCC抗拉、抗压及仿生结构梁试验研究. 硕士学位论文, 同济大学, 2017.
[20] Xu W L. The development of ultra high ductility cementitious composites and the establishment of an analytic model based on micro-mechanics. Master’s Thesis, Tongji University, China, 2016 (in Chinese).
许万里. 超高延性水泥基的制备及微观力学模型解析. 硕士学位论文, 同济大学, 2016.
[21] Ranade R, Li V C, Stults M D, et al. ACI Materials Journal, 2013, 110(4), 413.
[22] Wang S, Li V C. ACI Materials Journal, 2008, 104(3), 233.
[23] Zhang C M, Deng D H. Journal of the Chinese Ceramic Society, 1995(6), 673 (in Chinese).
张传镁, 邓德华. 硅酸盐学报, 1995(6), 673.
[24] Chau C K, Chan J, Li Z. Cement and Concrete Composites, 2009, 31(4), 250.
[25] Li V C, Wang S X. Probabilistic Engineering Mechanics, 2006, 21(3), 201.
[26] Wang S, Li V C. In: Proceedings of FRAMCOS-S, vail, Colorado, USA, 2004, PP. 1005.
[27] Dong Z Y, Li Q B. Advanced in Mechanics, 2001, 31(4), 555(in Chinese).
董振英, 李庆斌. 力学进展, 2001, 31(4), 555.