Preparation and Property of Waterborne Polyurethane Obtained with Polycarbonate |
XUE Xiaowu1,2, WANG Xinwen1, LIU Hongbo2, QING Ning1
|
1 School of Biotechnology and Health Science, Wuyi University, Jiangmen 529020 2 School of Applied Chemistry and Biological Technology, Shenzhen Polytechnic, Shenzhen 518055 |
|
|
Abstract A waterborne polyurethane with great stability was prepared and characterized by FT-IR in this work. This study analyzed the impact of different isocyanate index (R=n(NCO)/n(OH)), dimethylolpropionic acid (DMPA) and trimethylolpropane (TMP) content on the physical properties of WPCU. The study contrasts the performance of the best synthetic WPCU and polyester polyurethanes. The research found that: When the isocyanate index is 7, the prepared polycarbonate polyurethane has good mechanical properties. The tensile strength is up to 12.46 MPa, and the water absorption rate is only 25.88%. Adding TMP can increase the degree of crosslinking of the polyurethane. When the amount of TMP is increased from 0.5% to 1.5%, the tensile strength increases from 4.33 MPa to 7.56 MPa, and the elongation at break decreases from 307.12% to 258.53%. In the case of the same molecular weight, the WPCU has higher mechanical properties, hardness of 2H, and tensile strength is 6 times higher compared with the polyester type waterborne polyurethane (PESTUR)
|
Published: 05 July 2019
|
|
About author:: Hongbo Liu, Ph.D., professor, has been engaged in the research and development of special performance resins, composite materials and related fine chemicals. Guangdong professional leading talents, Shenzhen high-level talents, executive director of Shenzhen Coating Technology Society. He has presided over more than 20 various topics, published more than 50 papers in domestic and foreign journals, and applied for 12 invention patents (8 have been authorized).Xiaowu Xue, male, born in April 1992, native of Hefei, Anhui, Han nationality, is a graduate student. His research direction is waterborne polyurethane. |
|
|
1 Scrinzi E, Rossi S, Deflorian F, et al. Progress in Organic Coatings,2011,72,81. 2 许戈文. 聚氨酯材料, 化学工业出版社,2006. 3 郝广杰, 张邦华, 宋谋道, 等. 高分子材料科学与工程,2000,16(2),148. 4 陈福建, 李晓, 张卫英, 等. 石油化工,2008,37(10),1049 5 冉岚, 刘少友, 唐文华. 中国胶黏剂,2013,22(12),6 6 高笑飞, 吴明华, 洪国沈, 等. 印染助剂,2013,30(7),19 7 卢秀萍, 王文杰. 聚氨酯工业,2006(4),18 8 杨清萍. 大豆油基水性聚氨酯SiO2纳米复合材料研究. 硕士学位论文,五邑大学,2016. |
|
|
|