材料在铝液中熔蚀-磨损行为的研究进展

doi:10.11896/cldb.17120109

Abstract
Figure/Table
References
Related Citation (2)

Download:

Full Text ( PDF ) (3025KB)
Export: BibTeX | EndNote (RIS)

Abstract In the field of metallurgical, chemical, aerospace and automotive, corrosion-wear damage to the key components used in high temperature corrosive environment under dynamic loading often results in tremendous economic losses. Many researches have focused on the accelerated degradation of materials in corrosive gas, solution or particle erosion conditions. However, the corrosion-wear behavior of materials in high temperature metal melt has been rarely reported, and the synergy mechanism between corrosion and wear is still inexplicit. Aluminum and its alloys are widely used in buildings, transportation, energy, aerospace, electronics and other areas. However, aluminum melt is one of the most corrosive metallic fluids. Some key parts in the production process of aluminum industry, such as metallurgy, forming and hot dip, are often damaged by corrosion and wear. At present, a large number of wear-resisting materials of high alloy, such as die steel, are still used, but they are costly and have a short service life. Production can only be maintained by frequent replacement of parts. Therefore, it is urgent to develop new liquid-aluminum-resistant corrosion and wear materials to meet the needs of aluminum industrial production and application.
However, due to the particularity of high temperature metal melt as a corrosive medium, few studies have been reported on the corrosion behavior of high temperature metal melt. On the one hand, due to the lack of special equipment to test and characterize the corrosion and wear behaviors of materials. On the other hand, due to the complex metallurgical physical and chemical reactions at the corrosion interface, the interaction mechanism between corrosion and wear behaviors is still unclear. At present, for the studies of the material corrosion behavior and mechanism in the liquid aluminum are more, while that of the material corrosion and wear behavior in the liquid aluminum are few. Some researches focused on the erosion and wear behavior in aluminum alloy molten shaping process and material substitution. The study of material corrosion-wear mechanism in liquid aluminum is still in the blank.
In the past two years, on the basis of developing a new corrosion and wear of high-temperature metal melt test system, the corrosion and wear behavior of materials in high-temperature aluminum liquid has been studied, and a large number of materials have been screened. It is found that the corrosion and wear resistance of the commonly used metal materials is depend on the formation rate and characterization of intermetallic compound layer, as well as the combination between the substrate and intermetallic zone. The amount of material erosion-wear loss is much larger than the sum of pure corrosion and pure wear material loss indicates that the corrosion-wear failure of material in aluminum liquid is not a simple superposition of corrosion and wear behavior, and the main failure mechanism lies in the synergy mechanism between corrosion and wear. For the commonly used H13 steel materials, the ratio of corrosion-wear interaction under typical working conditions is more than 90%. In the aspect of material development, data collecting is relied on single corrosion test or high temperature friction and wear test. The development of materials with excellent corrosion-wear resistance in molten aluminum mainly focus on three aspects: microstructure regulation of ferrous alloy, application of refractory metals and surface treatment technology. Intermetallic matrix composites developed in recent years have also opened up new ideas for the development of new materials with excellent corrosion-wear resistance in molten aluminum.
This paper briefly introduces the corrosion and wear failure behavior of materials in aluminum liquid, and points out that the interaction between corrosion and wear is the key reason for the failure of materials or parts. On this basis, the performance requirements of materials with excellent corrosion-wear resistance in molten aluminum are put forward. Based on the review of the research progress, the paper puts forward the future development direction and research focus of these new materials.

Key words： corrosion-wear molten aluminum synergy mechanism intermetallics

Published: 10 April 2020

CLC number:

TB37

Fund:This work was financially supported by the National Natural Science Foundation of China (51605106), the Joint Funds of the Science and Technology Foundation of Guizhou Province, China (20167437), the Opening Project of Guangdong Key Laboratory for Advanced Metallic Materials Processing, South China University of Technology (GJ201608).

About author:: Huaqiang Xiaoreceived his B.E. degree in materials science from Taiyuan University of Technology in 2006 and received his Ph.D. degree in materials forming engineering from the National Engineering Research Center of Near-Net-Shape Forming for Metallic Materials, South China University of Technology, in 2013. His research has focused on metal matrix composites.

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	XIAO Huaqiang
	CHEN Yujia
	CHEN Weiping
	HE Jiarong
	ZHAO Sihao

Cite this article:

XIAO Huaqiang,CHEN Yujia,CHEN Weiping, et al. Research Progress on Corrosion-Wear Behavior of Materials in Molten Aluminum[J]. Materials Reports, 2020, 34(7): 7123-7129.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.17120109 OR http://www.mater-rep.com/EN/Y2020/V34/I7/7123

1 Liu Y, Mol J M C, Janssen G C A M. Scripta Materialia, 2015, 107, 92.
2 Guzmán A M, Martínez D I, González R. Engineering Failure Analysis, 2014, 46(46),188.
3 Dearnley P A, Mallia B. Wear, 2013, 306(1-2),263.
4 Zhang X M, Chen W P. Transactions of Nonferrous Metals Society of China, 2015, 25(6),1715.
5 Kim H J, Yoon B H, Lee C H. Wear, 2003, 254(5-6),408.
6 Chen W P, Wu J, Luo H F. Special Casting & Nonferrous Alloys, 2012, 32(10),883(in Chinese).
陈维平, 吴晶, 罗洪峰. 特种铸造及有色合金, 2012, 32(10), 883.
7 Zhang X, Chen W, Luo H, et al. Corrosion Science, 2017, 125(8),20.
8 Xiao H Q,Chen W P.Transactions of Nonferrous Metals Society of China, 2017, 27(1),89(in Chinese).
肖华强,陈维平. 中国有色金属学报, 2017, 27(1), 89.
9 Chen W P, Fang S C, Zeng Y, et al. Transactions of Nonferrous Metals Society of China, 2013, 23(11), 3127(in Chinese).
陈维平, 方思聪, 曾勇,等. 中国有色金属学报, 2013, 23(11), 3127.
10 Zhu Y, Schwam D, Wallace J F, et al. Materials Science and Enginee-ring: A, 2004, 379 (1), 420.
11 Wu J. The screening experiments of corrosion-wear resistant metal mate-rials in molten aluminum and device development. Master’s Thesis, South China University of Technology, China, 2012(in Chinese).
吴晶. 耐铝液腐蚀-磨损金属材料的筛选及其试验设备的研制.硕士学位论文,华南理工大学,2012.
12 Xiao H, Chen W, Liu Z. Transactions of Nonferrous Metals Society of China, 2012, 22 (9),2320.
13 Balloy D, Tissier J C, Giorgi M L, et al.Metallurgical & Materials Tran-sactions A, 2010, 41(9), 2366.
14 Gao Z Y, Zhang J L, Wu W X, et al. Foundry, 2009, 58(9),937(in Chinese).
高占勇,张金龙,武文霞,等.铸造,2009, 58(9),937.
15 Chen W P, Zhu S L, Gong J L, et al. Journal of Hunan University, 1991, 18 (4), 71(in Chinese).
陈维平, 朱士鎏, 龚建森,等. 湖南大学学报, 1991, 18 (4), 71.
16 Yu Y, Xie H D. Corrosion & Protection, 2012, 33(3), 216(in Chinese).
余岩, 谢海东. 腐蚀与防护, 2012, 33(3), 216.
17 Zhang X, Li X, Chen W. Surface and Interface Analysis, 2015, 47 (6), 648.
18 Ling Z, Chen W, Lu T, et al. Wear, 2019, 430-431, 81.
19 Castro M N I, Robles J M A, Hernandez D A C, et al. Ceramics International, 2010, 36(4),1205.
20 Castro M N I, Robles J M A, Hernandez D A C, et al. Ceramic International, 2016, 42(2), 3491.
21 Castro M N I, Robles J M A, Hernandez D A C, et al. Journal of the European Ceramic Society, 2015, 35(15), 4287.
22 Adabifiroozjaei E, Koshy P, Sorrell C C. Journal of the European Cera-mic Society, 2012, 32(8),1463.
23 AdabiFiroozjaei E, Koshy P, Sorrell C C. Journal of the European Ceramic Society, 2013, 33(6), 1067.
24 Wang W J, Lin J P, Wang Y L, et al. Rare Metal Materials and Engineering, 2007, 36 (6), 994(in Chinese).
王文俊, 林均品, 王艳丽, 等. 稀有金属材料与工程, 2007, 36 (6), 994.
25 Wang W J, Lin Y L, Wang J P, et al. Journal of Iron and Steel Research, 2007, 19 (3), 1(in Chinese).
王文俊, 王艳丽, 林均品, 等.钢铁研究学报, 2007, 19 (3), 1.
26 Geng G Q, Guan L, Li N, et al. Hot Working Technology, 2006, 35 (6), 14(in Chinese).
耿刚强, 官磊, 李宁, 等. 热加工工艺, 2006, 35 (6), 14.
27 Karger-Kocsis J, Felhös D, Xu D, et al. Wear, 2008, 265(3-4),292.
28 Zhang X M. Research on the corrosion-wear resistance of the novel Fe-Cr-B cast steel and their three-dimensional interconnected ZrO₂ reinforced metal matrix composites in molten aluminum. Ph.D. Thesis, South China University of Technology, China, 2015(in Chinese).
张先满. 新型Fe-Cr-B铸钢及其三维网络结构ZrO₂增强复合材料的铝液腐蚀-磨损研究.博士学位论文,华南理工大学, 2015.
29 Rio E D, Nash J M, Williams J C, et al. Materials Science & Engineering A, 2007, 463(1-2),115.
30 James G, William L, Peters K M. International Journal of Applied Ceramic Technology, 2008, 5(3),265.
31 Chen W, Xiao H, Fu Z, et al. Materials and Design, 2013, 49,929.
32 Zeng Y. The preparation of Ti₃AlC₂/TiAl₃ Composites and their corrosion-wear performance to liquid aluminum. Master’s Thesis, South China University of Technology, China, 2015(in Chinese).
曾勇. Ti₃AlC₂/TiAl₃制备及其耐铝液熔蚀-磨损性能. 硕士学位论文,华南理工大学, 2015.
33 Wang R, Min Y A,Wu X C. Heat Treatment of Metals, 2003,28 (12),5(in Chinese).
王荣, 闵永安, 吴晓春. 金属热处理, 2003,28 (12),5.
34 Vourlias G, Pistofidis N, Psyllaki P, et al. Journal of Alloys and Compounds, 2009,483,382.
35 Joshi V, Kulkarni K, Shivpuri R, et al. Surface and Coatings Technology, 2001, 146-147,338.
36 Wang Y. Surface and Coatings Technology,1997,94,60.
37 Liu H B, Zhang M Q, Yang L H, et al. Chinese Journal of Vacuum Science and Technology, 2015, 35(3),290(in Chinese).
刘海彬, 张民权, 杨灵华,等. 真空科学与技术学报, 2015, 35(3),290.
38 Tanaka S, Takagi M, Mano T. Journal of Physics: Conference Series, DOI: 10.1088/1742-6596/417/1/012032.
39 Luo Z M, Ni D H, Yi Y Y, et al. Corrosion & Protection, 2016, 37(5),388(in Chinese).
罗哲民, 倪东惠, 易耀勇, 等. 腐蚀与防护, 2016, 37(5),388.
40 Ramos-Masana A, Colominas C. Surface & Coating Technology, 2019, 375,171.
41 Zhu Z. Low temperature plasma nitriding (LTPN) technology and its effect on the properties of duplex treatment of H13 die steel. Master’s Thesis, South China University of Technology, China, 2016(in Chinese).
朱振中.低温离子氮化及其对双重处理H13模具钢性能的影响.硕士学位论文,华南理工大学, 2016.