输氢管道非金属密封材料氢适应性研究

doi:10.11896/cldb.25030182

Abstract
Figure/Table
References
Related Citation (1)

Download:

Full Text ( PDF ) (78790KB)
Export: BibTeX | EndNote (RIS)

Abstract In the process of hydrogen transportation through pipelines, hydrogen permeation into non-metallic sealing materials induces material degradation, elevating operationalsafety risks. This study investigates three representative non-metallic sealing materials—nitrile rubber (NBR), fluororubber (FKM), and polytetrafluoroethylene (PTFE) — through aging and rapid gas decompression (RGD) tests under hydrogen exposure at 6.3 MPa and 60 ℃, employing specialized non-metallic penetration test equipment and high-temperature/high-pressure aging apparatus. Post-RGD evaluation revealed cross-section assessment grades of 0 for both NBR and PTFE and 1 for FKM, all significantly below the critical threshold of 3 specified in GB/T 34903-2017, confirming compliance with acceptance criteria. Compared to ambient air conditions at room temperature, aging experiments demonstrated distinct tensile property variations under hydrogen exposure at 6.3 MPa and 60 ℃: NBR exhibited a 27.24% increase in tensile strength and a 22.21% decrease in elongation at break; FKM showed a 21.44% increase in tensile strength accompanied by a 17.16% reduction in elongation at break; PTFE displayed a 16.29% decrease in tensile strength and a 30.65% drop in elongation at break. Crucially, all tensile property fluctuations remained within the 50% tolerance limit mandated by GB/T 34903-2017. This systematic investigation elucidates degradation mechanisms of mechanical and sealing properties in hydrogen environments, establishes material suitability criteria for hydrogen service conditions, and develops a robust evaluation methodology for seal performance under hydrogen exposure. The findings provide critical insights for material selection and performance assessment of non-metallic seals in hydrogen pipeline systems, offering practical guidelines for engineering applications.

Key words： hydrogen transmission pipelines non-metallic sealing materials nitrile rubber (NBR) fluoroelastomer (FKM) polytetrafluoroethylene (PTFE) hydrogen compatibility

Published: 25 March 2026 Online: 2026-04-03

CLC number:

TE83

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	XU Meng
	QU Shimin
	SUN Chen
	LYU Liangliang
	LI Xin
	NASHENG Batu
	LU Yanghui

Cite this article:

XU Meng,QU Shimin,SUN Chen, et al. Study on Hydrogen Compatibility of Non-metallic Sealing Materials for Hydrogen Transmission Pipelines[J]. Materials Reports, 2026, 40(6): 25030182-9.

URL:

https://www.mater-rep.com/EN/10.11896/cldb.25030182 OR https://www.mater-rep.com/EN/Y2026/V40/I6/25030182

1 Zhang C, Shao Y, Shen W, et al. ACS Omega, 2023, 8(22), 19212.
2 Yu Q, Hao Y, Ali K, et al. Energy Conversion and Management, 2024, 301, 118025.
3 Huang S, Yang Z L, Li Z Y. Chemical Industry and Engineering Progress, 2024, 43(2), 882(in Chinese).
黄晟, 杨振丽, 李振宇. 化工进展, 2024, 43(2), 882.
4 Liu Z T, Wu Y F, Li Y G, et al. Materials Reports, DOI: 10. 11896/cldb. 24040041 (in Chinese).
刘志坦, 吴溢凡, 李玉刚, 等. 材料导报, DOI: 10. 11896/cldb. 24040041.
5 Zhao Q, Xing Y Y, Wang X Y, et al. Materials Reports , 2024, 38(12), 132(in Chinese).
赵茜, 邢云颖, 王修云, 等. 材料导报, 2024, 38(12), 132.
6 Xu M, Wang T J, Chang X L, et al. Mechanics in Engineering, 2025, 47(1), 131(in Chinese).
徐猛, 王铁军, 常雪伦, 等. 力学与实践, 2025, 47(1), 131.
7 Shang J, Lu Y H, Zheng J Y, et al. Chemical Industry and Engineering Progress, 2021, 40(10), 5499(in Chinese).
尚娟, 鲁仰辉, 郑津洋, 等. 化工进展, 2021, 40(10), 5499.
8 Field R A, Derwent R G. International Journal of Hydrogen Energy, 2021, 58, 46.
9 Melaina M W, Antonia O, Penev M. National Renewable Energy Laboratory, DOI:10. 2172/1219920.
10 Guy P, Laszlo T, Julien C. Processes, 2021, 9 (7), 1219.
11 Birkitt K, Loo-Morrey M, Sanchez C, et al. International Journal of Hydrogen Energy, 2021, 46(23), 12290.
12 Liu C W, Zhang R, Tian L, et al. Natural Gas Industry, 2022, 42(9), 145(in Chinese).
刘翠伟, 张睿, 田磊, 等. 天然气工业, 2022, 42(9), 145.
13 Zhao Y Z, Zhang X, Zheng J Y, et al. Chemical Engineering & Machinery, 2016(1), 1 (in Chinese).
赵永志, 张鑫, 郑津洋, 等. 化工机械, 2016(1), 1.
14 Liang X B, Fie F, Ma W F, et al. Processes, 2024, 12(11), 2353.
15 Morgan G . JEC Composites Magazine, 2021, 143, 26.
16 Yu Z L, Zhang L Y, Ning C, et al. Mechanics in Engineering, 2022, 44(3), 491(in Chinese).
于子龙, 张立业, 宁晨, 等. 力学与实践, 2022, 44(3), 491.
17 Barth R R, Simmons K L, San Marchi C W. Sandia National Laboratories, DOI:10. 2172/1104755.
18 Flory P J . Principles of polymer chemistry, Cornell University Press, America, 1953, pp. 687.
19 Wu X, Zhang H, Yang M, et al. International Journal of Hydrogen Energy, 2022, 47(12), 8071.
20 Kulkarni S S, Shin Y, Choi K S, et al. Polymer: the International Journal for the Science and Technology of Polymers, 2023, 282, 13.
21 Yamabe J, Koga A, Nishimura S. Nippon Gomu Kyokaishi, 2010, 83(6), 159.
22 Wilson M A, Frischknecht A L. International Journal of Hydrogen Energy, 2022, 47(33), 15094.
23 Bouledroua O, Hafsi Z, Djukic M B, et al. International Journal of Hydrogen Energy, 2020, 45( 35), 18010.
24 Liu X B, Zhang D, Wu X J, et al. Mechanics in Engineering, 2023, 45(2), 245(in Chinese).
刘啸奔, 张东, 武学健, 等. 力学与实践, 2023, 45(2), 245.
25 Zhu J L, Zhang J, Li Y X, et al. Oil & Gas Storage and Transportation, 2024, 43(7), 730(in Chinese).
朱建鲁, 张捷, 李玉星, 等. 油气储运, 2024, 43(7), 730.
26 Zhou C L, Liu X H, Zheng Y R, et al. Composites Part B: Engineering, 2024, 275(15), 111342. 1.
27 Flaconneche B, Martin J, Klopffer M H. Oil & Gas Science and Technology, 2001, 56(3), 261.
28 Menon C, Kruizenga A M, Alvine J, et al. ASME 2016 Pressure Vessels and Piping Conference, Vancouver: ASME, 2016, pp. V06BT06A037.
29 Guo Y, Yang J T, Zhuang J Y, et al. Applied Catalysis A, General, 2019, 589, 117312.