聚四氟乙烯/聚醚醚酮(PTFE/PEEK)复合材料的制备及摩擦学性能研究

doi:10.11896/cldb.24120093

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (51135KB)
Export: BibTeX | EndNote (RIS)

Abstract The composite material with PTFE micro-powder as additive phase and PEEK as matrix was prepared by hot pressing sintering method. The effects of PTFE content, load and velocity on the properties of PEEK and its composites were studied systematically. The results showed that PTFE/PEEK composites were successfully prepared by hot pressing sintering method. The addition of PTFE don’t change the crystal structure and chemical structure of the composites, but it can effectively improve the tribological properties of PEEK composites. The friction coefficient and wear rate of PTFE/PEEK-based composites decreases first and then increases with the increase of PTFE content. When the mass fraction of PTFE is 10%, the tribological properties of PTFE/PEEK composites are the best. Compared with pure PEEK (62.83 mm/s, 25 N), the friction coefficient and wear rate of 10% PTFE/PEEK composite are reduced by 66.7% and 76.0%, respectively. The friction coefficient of pure PEEK and 10% PTFE/PEEK composites increases first and then decreases with the increase of load, and increases with the increase of linear velocity. The wear rate of pure PEEK and 10% PTFE/PEEK composite gradually increases with the increase of load. The wear rate of pure PEEK gradually increases with the increase of line speed, and the wear rate of 10% PTFE/PEEK composite first decreases and then increases with the increase of line speed. The wear mechanism of pure PEEK under different loads or different speeds is mainly fatigue wear and adhesive wear. The wear mechanism of 10% PTFE/PEEK composite at low load (25, 50 N) is mainly slight adhesive wear and fatigue wear, accompanied by small abrasive wear. When the load is 75 N, the wear mechanism is mainly severe adhesive wear.

Key words： polyether-ether-ketone (PEEK) polytetrafluoroethylene (PTFE) composite friction and wear

Published: 10 December 2025 Online: 2025-12-03

CLC number:

TB332

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	WANG Yixuan
	TANG Mingjin
	YANG Xiaoxuan
	WANG Lulu
	XUE Jianxin
	WANG Shuai
	SONG Chenfei
	LU Huanhuan
	LI Jie
	PANG Xianjuan

Cite this article:

WANG Yixuan,TANG Mingjin,YANG Xiaoxuan, et al. Preparation and Tribological Properties of Polytetrafluoroethylene/Polyether Ether Ketone (PTFE/PEEK) Composite Materials[J]. Materials Reports, 2025, 39(23): 24120093-10.

URL:

https://www.mater-rep.com/EN/10.11896/cldb.24120093 OR https://www.mater-rep.com/EN/Y2025/V39/I23/24120093

1 Qiu X T, Fu C L, Gu A Q, et al. High Performance Polymers, 2019, 326, 645.
2 Chen C Y, Zhang C, Zhao Z Q, et al. International Journal of Mechanical Sciences, 2019, 155, 170.
3 Zhu S, Qian Y, Elwathig A M, et al. Composites Communications, 2020, 18, 43.
4 Yi M, Duan H T, Chen S, et al. Engineering Plastics Application, 2018, 46(6), 105 (in Chinese).
易蒙, 段海涛, 陈松, 等. 工程塑料应用, 2018, 46(6), 105.
5 Li N, Chen D Q, Gao X Y, et al. Reviews on Advanced Materials Science, 2020, 59, 399.
6 Dang Z, Gao D Q, Yang J, et al. Engineering Plastics Application, 2020, 48(9), 166 (in Chinese).
党哲, 高东强, 杨杰, 等. 工程塑料应用, 2020, 48(9), 166.
7 Sabbir A, Shantanu. Journal of Polymer Engineering Bhowmik, 2018, 39(1), 1.
8 Guo L H, Zhang G, Wang D A, et al. Composites Part A:Applied Science and Manufacturing, 2017, 102, 400.
9 Pang X J, Yue S W, Huang S L, et al. Frontiers in Materials, 2023, 10, 1197604.
10 Awaja F, Guarino R, Tripathi M, et al. Tribology International, 2022, 176, 107915.
11 Henriques B, Fabris D, Joana M G, et al. Journal of the Mechanical Behavior of Biomedical Materials, 2018, 84, 225.
12 Cheng B X, Duan H T, Chen Q, et al. Applied Surface Science, 2021, 566, 150668.
13 Yue S W, Pang X J, Niu Y X, et al. Materials Reports, 2022, 36(16), 255 (in Chinese).
岳世伟, 逄显娟, 牛一旭, 等. 材料导报, 2022, 36(16), 255.
14 Huang S L, Pang X J, Yue S W, et al. Tribology, 2023, 43(6), 616 (in Chinese).
黄素玲, 逄显娟, 岳世伟, 等. 摩擦学学报, 2023, 43(6), 616.
15 Hou X, Bai P P, Li J Y, et al. Friction, 2023, 11, 1660.
16 Feng C N, Guo Y, Yu Z Y, et al. Tribology International, 2023, 181, 108315.
17 Ángel A A, Lu C, Verónica S M, et al. Polymers, 2020, 12(12), 2765.
18 Wang Q F, Wang Y X, Wang H L, et al. Polymers for Advanced Techno-logies, 2017, 29(2), 896.
19 Cai Z J, Wang J Q. Materials for Mechanical Engineering, 2018, 42(5), 69 (in Chinese).
蔡振杰, 王佳祺. 机械工程材料, 2018, 42(5), 69.
20 Ma Z L, Zhang G C, Yang Q, et al. The Journal of Supercritical Fluids, 2018, 140, 116.
21 Huang L. Polymer materials, Chemical Industry Press, China, 2005, pp. 136 (in Chinese).
黄丽. 高分子材料, 化学工业出版社, 2005, pp. 136.
22 Dhanumalayan E, Girish M J. Advanced Composites and Hybrid Materials, 2018, 1, 247.
23 Wang R L, Xu G B, He Y C. E-Polymers, 2017, 17(3), 215.
24 Ye J, Khare H S, Wear, 2013, 297(1-2), 1095.
25 Zang H, Wu Y, Liang M, et al. Journal of Thermoplastic Composite Materials, 2020, 35(9), 1319.
26 Onodera T, Nunoshige J, Kawasaki K, et al. The Journal of Physical Chemistry C, 2017, 121(27), 14589.
27 Gu D P, Zhang L X, Chen S W, et al. Polymers, 2018, 10(9), 966.
28 Zheng Q, Zhang Y F. Applied Physics A, 2020, 126, 104.
29 Su Y L, Chen X M, Yu Z D, et al. Journal of Materials Science, 2017, 52, 2934.
30 Venkata K E, Rajesh G, Anbuchezhiyan G, et al. Materials Today:Proceedings, 2023, 5, 630.
31 Cheng H, Xie Y C, Tang Q H, et al. Transactions of Nonferrous Metals Society of China, 2018, 28(7), 1360.
32 Zhang L, Fang W L, Tian W B, et al. Coatings, 2024, 14(1), 16.
33 Pang X J, Yue S W, Huang S L, et al. China Mechanical Engineering, 2023, 34(3), 277 (in Chinese).
逄显娟, 岳世伟, 黄素玲, 等. 中国机械工程, 2023, 34(3), 277.
34 Xie J M, Pang X J, Zhao R F, et al. Materials Reports, 2024, 38(16), 273 (in Chinese).
谢金梦, 逄显娟, 赵若凡, 等. 材料导报, 2024, 38(16), 273.
35 Huang S L. Preparation and properties of PEEK-based wear-resistant and antistatic composites. Master’s Thesis, Henan University of Science and Technology, China, 2023 (in Chinese).
黄素玲. PEEK基耐磨抗静电复合材料的制备及性能研究. 硕士学位论文, 河南科技大学, 2023.
36 Yang K, Niu Y P, Li Y, et al. Tribology International, 2023, 186, 108597.
37 Zhang Z W, He Y, He Y, et al. Materials, 2022, 15(19), 6524.
38 Georgescu G, Deleanu L, Titire L C, et al. Materials, 2021, 14(4), 997.