混杂纤维高强高延性水泥基复合材料弯曲性能及预测模型

doi:10.11896/cldb.24120022

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (39803KB)
Export: BibTeX | EndNote (RIS)

Abstract High-strength engineered cementitious composite (HS-ECC) holds promising application prospects in civil engineering, and a thorough understanding of their flexural properties is essential for practical engineering applications. Currently, there is a relative lack of research on the hybrid reinforcement mechanism of polyethylene fibers (PEF) and steel fibers (SF) in HS-ECC, and effective predictive models for flexural properties are also lacking. To address this, the influence of hybrid PEF-SF fiber content and hyrbid ratio on the workability, compressive strength, and flexural properties of HS-ECC were investigated through slump tests, compressive strength tests, and four-point bending tests. Furthermore, a predictive model for flexural properties was established. The results indicate that both PEF and SF degrade the cementitous composite’s workability, with PEF having a more significant negative impact. SF exhibits a more pronounced enhancement effect on flexural strength and compressive strength, but the fiber reinforcement efficiency decreases with the increasing of fiber content. Both PEF and SF contribute to increasing peak deflection, with higher PEF content being beneficial for enhancing deformability, whereas excessive SF content can weaken the deflection hardening characteristics and affect flexural performance. Considering strength, deformability, and cost, the SF content should not exceed 0.6%. Based on micro-analysis, a uniaxial tensile/compressive constitutive model for HS-ECC was proposed, and a predictive model for flexural properties was established. This model can effectively predict the flexural properties of PEF-SF hybrid HS-ECC, providing theoretical support for its application in practical engineering.

Key words： high-strength engineered cementitious composite hybrid fiber flexural performance constitutive model prediction model

Published: 10 December 2025 Online: 2025-12-03

CLC number:

TU528.572

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	WAN Siyu
	SU Sanqing
	CAO Zhen
	WANG Zhaoyao

Cite this article:

WAN Siyu,SU Sanqing,CAO Zhen, et al. Flexural Performance and Prediction Model of High-strength ECC with Hybrid Fiber[J]. Materials Reports, 2025, 39(23): 24120022-10.

URL:

https://www.mater-rep.com/EN/10.11896/cldb.24120022 OR https://www.mater-rep.com/EN/Y2025/V39/I23/24120022

1 Zhang T, Li X Q, Zhang L, et al. Materials Reports, 2023, 37(S1), 583(in Chinese).
张田, 李晓琴, 张莉, 等. 材料导报, 2023, 37(S1), 583.
2 Jiang S Y, Gong H W, Yao W L, et al. Materials Reports, 2018, 32(23), 4192(in Chinese).
江世永, 龚宏伟, 姚未来, 等. 材料导报, 2018, 32(23), 4192.
3 Li B, Meng X Z, Zhang C, et al. Materials Research and Application, 2023, 17(1), 158(in Chinese).
李犇, 孟宪忠, 张琛, 等. 材料研究与应用, 2023, 17(1), 158.
4 Zhou J, Pan J, Leung C K Y. Journal of Materials in Civil Engineering, 2015, 27(1), 04014111.
5 Huang B T, Li Q H, Xu S L. Journal of Structural Engineering, 2019, 145(1), 04018234.
6 Zhang D, Yu J, Wu H, et al. Composites Part B:Engineering, 2020, 184, 107741.
7 Zhao J, Yan C, Liu S, et al. Construction and Building Materials, 2021, 268, 121169.
8 Lu C, Pan J, Luo B, et al. Construction and Building Materials, 2022, 331, 127296.
9 Yu K Q, Yu J T, Dai J G, et al. Construction and Building Materials, 2018, 158, 217.
10 Liu D, Yu J, Qin F, et al. Case Studies in Construction Materials, 2023, 18, e01961.
11 Xu L Y, Huang B T, Li V C, et al. Cement and Concrete Composites, 2022, 125, 104296.
12 Huang B T, Zhu J X, Weng K F, et al. Cement and Concrete Composites, 2022, 129, 104464.
13 Wu J D, Guo L P, Cao Y Z, et al. Cement and Concrete Composites, 2022, 126, 104371.
14 Ahmed S F U, Maalej M, Paramasivam P. Construction and Building Materials, 2007, 21(5), 1088.
15 Zhou Y, Xi B, Yu K, et al. Materials, 2018, 11(8), 1448.
16 Tinoco M P, De Andrade S F. Journal of Materials Research and Technology, 2021, 11, 754.
17 Wang Z B, Zhang J. Concrete, 2018(4), 65(in Chinese).
王振波, 张君. 混凝土, 2018(4), 65.
18 Liu Z, Liu S, Takasu K, et al. Construction and Building Materials, 2024, 450, 138674.
19 American Society of Testing Materials. ASTM C 1609 standard test method for flexural performance of fiber-reinforced concrete (using beam with third-point loading), West Conshohocken, ASTM Internation, 2024, pp.5.
20 Baby F, Graybeal B, Marchand P, et al. Materials and Structures, 2013, 46(8), 1337.
21 Han T S, Feenstr P H, Billington S L. ACI Structural Journal, 2003, 100(6), 749.
22 Bai R, Liu S G, Yan C W, et al. Construction and Building Materials, 2020, 247(3), 118110.
23 Meng D, Huang T, Zhang Y X, et al. Construction and Building Materials, 2017, 141(3), 259.
24 Huang H, Gao X, Khayat K H. Cement and Concrete Composites, 2021, 118, 103971.
25 Ministry of Housing and Urban Rural Development of the People’s Republic of China. Standard for design of concrete structures, GB/T 50010-2010, China Architecture and Building Press, China, 2024(in Chinese).
中华人民共和国住房和城乡建设部. 混凝土结构设计标准, GB/T 50010-2010, 中国建筑工业出版社, 2024.
26 Huo L, Bi J, Zhao Y, et al. Construction and Building Materials, 2021, 280, 122423.
27 Li V C, Wang Y, Backer S. Composites Communications, 1990, 21(2), 132.
28 Xu B, Ju J, Shi H. International Journal of Damage Mechanics, 2011, 20(6), 922.
29 Ning X L, Ding Y N, Zhang F S. Construction and Building Materials, 2015, 93, 644.
30 Lin Z, Kanda T, Li V C. Journal of Concrete Science and Engineering, 1999, 1, 173.
31 Liu J P, Tang J H, Han F Y. China Civil Engineering Journal, 2021, 54(10), 47(in Chinese).
刘加平, 汤金辉, 韩方玉. 土木工程学报, 2021, 54(10), 47.
32 Lin Z, Li V C. Journal of the Mechanics and Physics of Solids, 1997, 45(5), 763.
33 Li J, Qiu J, Weng J, et al. Construction and Building Materials, 2023, 362, 605.
34 Zhang Y, Zhang S, Deng M. Case Studies in Construction Materials, 2022, 17, e01573.