海泡石纤维增强二氧化硅气凝胶的制备及性能

doi:10.11896/cldb.23030233

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (49408KB)
Export: BibTeX | EndNote (RIS)

Abstract The efficiency and performance of silica (SiO₂) aerogel prepared by sol-gel method under atmospheric pressure are insufficient, which limits its industrial scale application. In this work, sepiolite nanofibers were used as enhancement, tetraethyl orthosilicate was used as silicon source precursor, and trimethylchlorosilane was used as modifier. Sepiolite fiber/silica aerogel bulk materials were prepared by sol-gel method and atmospheric drying. The mechanical properties, thermal properties and fire safety properties were tested, and the pore structure, infrared spectrum and micro-morphology were analyzed and characterized. The fiber skeleton of sepiolite can inhibit the shrinkage and cracking of aerogel block. Fibers have heterogeneous nucleation in the sol formation stage, which refines the particles, increases the specific surface area of aerogels and changes the pore structure. The introduction of fiber improves the mechanical properties, high temperature and ablation stability and fire safety properties, and reduces the thermal conductivity. The thermal conductivity of mass sepiolite fiber/silica aerogel can reach 0.012 8 W/(m·K), the compressive strength is 1.20 MPa, the flame retardancy is V-0, the shape remains stable after ablation at 1 300 ℃, and the comprehensive performance is excellent.

Key words： silica aerogel sepiolite nanofibers mechanical property thermal property fire safety property

Published: 10 October 2024 Online: 2024-10-23

CLC number:

TB332

Fund:National Natural Science Foundation of China (51778096), Cooperation Project Between Universities in Chongqing and Affiliated Institutes of Chinese Academy of Sciences (HZ2021009).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	LI Siying
	ZHOU Chao

Cite this article:

LI Siying,ZHOU Chao. Preparation and Properties of Sepiolite Fiber Enhanced Silica Aerogel[J]. Materials Reports, 2024, 38(19): 23030233-9.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.23030233 OR http://www.mater-rep.com/EN/Y2024/V38/I19/23030233

1 Kistler S S. Nature, 1931, 127(3211), 741.
2 Rashid A B, Shishir S I, Mahfuz M A, et al. Particle & Particle Systems Characterization, 2023, 40(6), 2200186.
3 Chen K. Preparation and properties of boehmite fiber-doped silica aerogels. Master's Thesis, University of Chinese Academy of Sciences (Ningbo Institute of Materials Technology and Engineering, China Academy of Sciences), China, 2019(in Chinese).
陈凯. 勃姆石纤维掺杂二氧化硅气凝胶的制备与性能研究. 硕士学位论文, 中国科学院大学(中国科学院宁波材料技术与工程研究所), 2019.
4 Li S Y, Zhou C, Li C Q, et al. Applied Chemical Industry, 2023, 52(3), 726(in Chinese).
李思盈, 周超, 李传强, 等. 应用化工, 2023, 52(3), 726.
5 Zhang J, Yin B, Liu W X, et al. Chemical Journal of Chinese Universities, 2022, 43(11), 108(in Chinese).
张洁, 银波, 刘玮欣, 等. 高等学校化学学报, 2022, 43(11), 108.
6 Iswar S, Malfait W J, Balog S, et al. Microporous and Mesoporous Materials, 2017, 241, 293.
7 Li X, Wang Q, Li H, et al. Journal of Sol-Gel Science and Technology, 2013, 67, 646.
8 Wang H, Yan X, Jin X, et al. Composites Communications, 2022, 35, 101285.
9 Lyu J, Liu Z, Wu X, et al. ACS Nano, 2019, 13(2), 2236.
10 Modest M F. Radiative heat transfer, Academic Press, San Diego, CA, 2003, pp.465.
11 Wang J, Kuhn J, Lu X. Journal of Non-crystalline Solids, 1995, 186, 296.
12 Jennings S G. Journal of Aerosol Science, 1988, 19(2), 159.
13 Schwarzenbach R P, Gschwend P M, Imboden D M. Environmental organic chemistry, John Wiley & Sons, 2016.
14 Ding S H. Preparation of silica aerogels and study on their heat transfer models. Master's Thesis, Changsha University of Science and Technology, China, 2018(in Chinese).
丁舒怀. 二氧化硅气凝胶的制备及其传热模型的研究. 硕士学位论文, 长沙理工大学, 2018.
15 He Y L, Xie T. Applied Thermal Engineering, 2015, 81, 28.
16 Zimmermann M V G, Zattera A J. Journal of Porous Materials, 2021, 28(5), 1325.
17 Okkerse C, Linsen B G. Ertl G, 1970, 142, 107.
18 Zhuravlev L T. Colloids and Surfaces A: Physicochemical and Engineering Aspects, 2000, 173(1-3), 1.
19 Huang Y, He S, Chen G, et al. Journal of Sol-Gel Science and Technology, 2018, 88, 129.
20 Yan M, Fu Y, Pan Y, et al. Composites Part B: Engineering, 2022, 230, 109496.
21 Farooq M, Sipponen M H, Seppálá A, et al. ACS Applied Materials & Interfaces, 2018, 10(32), 27407.
22 Yang J Y, Xia Y, Zhao J, et al. Chinese Journal of Polymer Science, 2020, 38, 1294.
23 Yin R, Cheng H, Hong C, et al. Composites Part A: Applied Science and Manufacturing, 2017, 101, 500.
24 Liu F, Jiang Y, Peng F, et al. Chemical Engineering Journal, 2023, 461, 141721.