脆性涂层材料断裂韧性和残余应力压痕表征技术综述<sup>*</sup>

doi:10.11896/j.issn.1005-023X.2017.013.001

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (2200KB)
Export: BibTeX | EndNote (RIS)

Abstract The large variety of brittle coating materials have become crucial materials in the fields of aerospace and national defense science and technology, and have played a great role in national economy.Fracture toughness and residual stress are important mechanical criteria of brittle coating materials. Vickers indentation method is one of the effective methods to characterize the mecha-nical properties of brittle coating materials. In this paper, the research progresses in fracture toughness and residual stress of brittle coatings are reviewed from the aspects of coating characteristics, indentation testing methods, mechanical model and experimental equipment. The characteristics and applicability of indentation mechanics models are discussed in detail. The future development direction of Vickers indentation techniques is also pointed out.

Key words： Vickers indentation fracture toughness residual stress brittle coating

Published: 10 July 2017 Online: 2018-05-04

CLC number:

O341

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	MAO Weiguo
	YANG Peng
	DAI Cuiying
	HE Yuanwu
	WAN Jie

Cite this article:

MAO Weiguo,YANG Peng,DAI Cuiying, et al. A Review of Vickers Indentation Measurements for Fracture Toughness and Residual Stress of Brittle Coating Systems[J]. Materials Reports, 2017, 31(13): 1-11.

URL:

https://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2017.013.001 OR https://www.mater-rep.com/EN/Y2017/V31/I13/1

1 Iscan B. Application of ceramic coating for improving the usage of cottonseed oil in a diesel engine[J]. J Energy Institute,2016,89 (1):150.
2 Zhu C, Jian Hai Y U, Guo Y F, et al. Problems of aircraft engine thermal barrier coating and its developing direction[J]. Surf Tech-nol,2016,45(1):13.
3 Padture N P, Gell M, Jordan E H. Thermal barrier coatings for gas-turbine engine applications[J]. Science,2002,296(5566):280.
4 Sampath S, Schulz U, Jarligo M O, et al. Processing science of advanced thermal-barrier systems[J]. MRS Bull, 2012,37(10):903.
5 Yang Yazheng, Yang Jialing, Fang Daining. Research progress on the thermal protection materials and structures in hypersonic vehicles[J].Appl Math Mech,2008,29(1):47(in Chinese).
杨亚政,杨嘉陵,方岱宁. 高超声速飞行器热防护材料与结构的研究进展[J]. 应用数学和力学,2008,29(1):47.
6 Darolia R. Thermal barrier coatings technology: Critical review, progress update, remaining challenges and prospects[J]. Int Mater Rev,2013,58(6):315.
7 Mumm D, Evans A I S. Characterization of a cyclic displacement instability for a thermally grown oxide in a thermal barrier system[J]. Acta Mater,2001,49(12):2329.
8 Lima Moreira F, Kleinberg M, Nunes C, et al. A novel Vickers hardness measurement technique based on adaptive balloon active contour method[J]. Expert Systems Appl,2016,45(C):294.
9 Ma D J, Wang J L, Sun L, et al. Method for identifying Vickers hardness by instrumented indentation curves with Berkovich/Vickers indenter[J]. Experimental Mech,2016,56(5):891.
10 Qiu Z, Liu C, Wang H, et al. Crack propagation and the material removal mechanism of glass-ceramics by the scratch test[J]. J Mech Behav Biomed Mater,2016,64:75.
11 Hermosilla U, Hyde T, Jones I A. Thermal analysis of electron-beam physical vapour deposited thermal barrier coated super-alloy tensile specimens[J]. Proc Inst Mech Engineers, Part L: J Mater Des Appl,2008,222(2):141.
12 Zhao P, Sun C, Zhu X, et al. Fracture toughness measurements of plasma-sprayed thermal barrier coatings using a modified four-point bending method[J]. Surf Coat Technol,2010,204(24):4066.
13 Liu H, Liang L, Wang Y, et al. Fracture characteristics and damage evolution of coating systems under four-point bending[J]. Int J Appl Ceram Technol,2016,13(6):1043.
14 Li C, Jacques S D M, Chen Y, et al. A synchrotron X-ray diffraction deconvolution method for the measurement of residual stress in thermal barrier coatings as a function of depth[J]. J Appl Crystallography,2016,49(6):1904.
15 Garces H F, Senturk B S, Padture N P. In situ Raman spectroscopy studies of high-temperature degradation of thermal barrier coatings by molten silicate deposits[J]. Scripta Mater,2014,76(76):29.
16 Christensen R, Lipkin D, Clarke D R, et al. Nondestructive evaluation of the oxidation stresses through thermal barrier coatings using Cr³⁺ piezospectroscopy[J]. Appl Phys Lett,1996,69(24):3754.
17 Elizalde M, Sanchez J, Martinez-Esnaola J, et al. Interfacial fracture induced by cross-sectional nanoindentation in metal-ceramic thin film structures[J]. Acta Mater,2003,51(14):4295.
18 Cook R F, Lawn B R, Fairbanks C J. Microstructure-strength pro-perties in ceramics: I. Effect of crack size on toughness[J]. J Am Ceram Soc,1985,68(11):604.
19 Sheity D K, Rosenfield A R, Duckworth W H. Indenter flaw geometry and fracture toughness estimates for a glass-ceramic[J]. J Am Ceram Soc,1985,68(10):C-282.
20 Niihara K, Morena R, Hasselman D P H. Evaluation of KIC of brittle solids by the indentation method with low crack-to-indent ratios[J]. J Mater Sci Lett,1982,1(1):13.
21 Gong J, Wang J, Guan Z. Indentation toughness of ceramics: A modified approach[J]. J Mater Sci, 2002,37(4):865.
22 Zhang T Y, Haasen P. The influence of ionized hydrogen on the brittle-to-ductile transition in silicon[J]. Philosophical Magazine A,1989,60(1):15.
23 Zhang T Y, Chen L Q, Fu R. Measurements of residual stresses in thin films deposited on silicon wafers by indentation fracture[J]. Acta Mater,1999,47(14):3869.
24 Vandermeulen W, Bosch R W, Snijkers F. The effect of Vickers hardness indentations on the fracture mode in 8mol% yttria-stabilised zirconia[J]. J Mater Sci,2015,50(7):2932.
25 Faisal N H, Ahmed R, Prathuru A K, et al. An improved Vickers indentation fracture toughness model to assess the quality of thermally sprayed coatings[J]. Eng Fracture Mech,2014,128:189.
26 Hong C H, Rickhey F, Jin H L, et al. Characteristics of indentation cracking using cohesive zone finite element techniques for pyramidal indenters[J]. Int J Solids Struct,2014,51(25):4327.
27 Hervas I, Montagne A, Gorp A V, et al. Fracture toughness of glasses and hydroxyapatite: A comparative study of 7 methods by using Vickers indenter[J]. Ceram Int,2016,42(11):12740.
28 Tanaka C B, Harisha H, Baldassarri M, et al. Experimental and finite element study of residual thermal stresses in veneered Y-TZP structures[J]. Ceram Int,2016,42(7):9214.
29 Song K, Xu Y, Zhao N, et al. Evaluation of fracture toughness of tantalum carbide ceramic layer: A vickers indentation method[J]. J Mater Eng Perform,2016,25(7):1.
30 Marshall D, Lawn B. An indentation technique for measuring stresses in tempered glass surfaces[J]. J Am Ceram Soc,1977,60(1-2):86.
31 Lawn B R, Evans A, Marshall D. Elastic/plastic indentation damage in ceramics: The median/radial crack system[J]. J Am Ceram Soc,1980,63(9-10):574.
32 Evans A G, Hutchinson J W. On the mechanics of delamination and spalling in compressed films[J]. Int J Solids Struct,1984,20(5):455.
33 Chicot D, Démarécaux P, Lesage J. Apparent interface toughness of substrate and coating couples from indentation tests[J]. Thin Solid Films,1996,283(1):151.
34 Abbas S Z, Khalid F A, Zaigham H. Indentation fracture toughness behavior of FeCo-based bulk metallic glass intrinsic composites[J]. J Non-Crystalline Solids,2017,457:86.
35 Fakolujo O, Merati A, Bielawski M, et al. Influence of mechanical surface treatments on the indentation fracture toughness of glass infiltrated zirconia toughened alumina "GI-ZTA" disks[J]. Matéria,2016,12(12):420.
36 Chiang S S, Marshall D B, Evans A G. The response of solids to elastic/plastic indentation. I. Stresses and residual stresses[J]. J Appl Phys,1982,53(1):298.
37 Lawn B R, Fuller E R. Equilibrium penny-like cracks in indentation fracture [J]. J Mater Sci,1975,10(12):2016.
38 龚江宏. 陶瓷材料断裂力学[M]. 北京:清华大学出版社,2001:101.
39 Yoffe E H. Elastic stress fields caused by indenting brittle materials[J]. Philosophical Magazine A,1982,46(4):617.
40 Anstis G R, Chantikul P, Lawn B R, et al. A critical evaluation of indentation techniques for measuring fracture toughness: I. Direct crack measurements[J]. J Am Ceram Soc,1981,64(9):533.
41 Ponton C B, Rawlings R D. Vickers indentation fracture toughness test Part 1 Review of literature and formulation of standardised indentation toughness equations[J]. Mater Sci Technol,1989,5(9):865.
42 Rios C T, Coelho A A, Batista W W, et al. ISE and fracture toughness evaluation by Vickers hardness testing of an Al₃Nb-Nb₂Al-AlNbNi in situ composite[J]. J Alloys Compd,2009,472(1-2):65.
43 Chicot D, Duarte G, Tricoteaux A, et al. Vickers indentation fracture (VIF) modeling to analyze multi-cracking toughness of titania, alumina and zirconia plasma sprayed coatings[J]. Mater Sci Eng A,2009,527(1-2):65.
44 Lube T. Indentation crack profiles in silicon nitride[J]. J Eur Ceram Soc,2001,21(2):211.
45 Houdková Š, Kaš parová M. Experimental study of indentation fracture toughness in HVOF sprayed hardmetal coatings[J]. Eng Fracture Mech,2013,110:468.
46 Lawn B, Swain M. Microfracture beneath point indentations in brittle solids[J]. J Mater Sci,1975,10(1):113.
47 Laugier M. New formula for indentation toughness in ceramics[J]. J Mater Sci Lett,1987,6(3):355.
48 Evans A G, Charles E A. Fracture toughness determinations by indentation[J]. J Am Ceram Soc,1976,59(7-8):371.
49 Lankford J. Indentation microfracture in the Palmqvist crack regime: Implications for fracture toughness evaluation by the indentation method[J]. J Mater Sci Lett,1982,1(11):493.
50 Blendell J E. The origins of internal stresses in polycrystalline Al₂O₃ and their effects on mechanical properties[J]. Massachusetts Institute of Technology,1979,123(1):617.
51 Sakardeliormanli A, Güden M. Microhardness and fracture toughness of dental materials by indentation method[J]. J Biomed Mater Res Part B:Appl Biomater,2006,76(2):257.
52 Faisal N H, Reuben R L, Ahmed R. An improved measurement of Vickers indentation behaviour through enhanced instrumentation[J]. Measurement Sci Technol,2011,22(1):015703.
53 Marshall D, Lawn B. Residual stress effects in sharp contact crac-king[J]. J Mater Sci,1979,14(8):2001.
54 Marshall D, Lawn B R, Chantikul P. Residual stress effects in sharp contact cracking. II Strength degradation[J]. J Mater Sci,1979,14:2225.
55 Hivart P, Crampon J. Interfacial indentation test and adhesive fracture characteristics of plasma sprayed cermet Cr₃C₂/Ni-Cr coatings[J]. Mech Mater,2007,39(11):998.
56 He Yuanwu. A modified indentation method and characterization of thermal barrier coatings under high-temperature by Vickers indentation[D].Xiangtan:Xiangtan University, 2016(in Chinese).
何远武. 热障涂层体系压痕断裂力学模型及高温压痕测试分析[D]. 湘潭: 湘潭大学,2016.
57 Wan J, Zhou M, Yang X S, et al. Fracture characteristics of freestanding 8wt% Y₂O₃-ZrO₂ coatings by single edge notched beam and Vickers indentation tests[J]. Mater Sci Eng A,2013,581:140.
58 Jordan D, Faber K. X-ray residual stress analysis of a ceramic thermal barrier coating undergoing thermal cycling[J]. Thin Solid Films,1993,235(1):137.
59 Chen Q, Mao W G, Zhou Y C, et al. Effect of Young′s modulus evolution on residual stress measurement of thermal barrier coatings by X-ray diffraction[J]. Appl Surf Sci,2010,256(23):7311.
60 Mao W, Wan J, Dai C, et al. Evaluation of microhardness, fracture toughness and residual stress in a thermal barrier coating system: A modified Vickers indentation technique[J]. Surf Coat Technol,2012,206(21):4455.
61 Lesage J, Chicot D. Role of residual stresses on interface toughness of thermally sprayed coatings[J]. Thin Solid Films,2002,415(1):143.
62 Kim S S, Chae Y H, Choi S Y. Characteristics evaluation of plasma sprayed ceramic coatings by nano/micro-indentation test[J]. Tribo-logy Lett,2004,17(3):663.
63 Mao W, Wu D, Yao W, et al. Multiscale monitoring of interface failure of brittle coating/ductile substrate systems: A non-destructive evaluation method combined digital image correlation with acoustic emission[J]. J Appl Phys,2011, 110(8):084903.
64 Mao W, Shen Y, Lu C. Deformation behavior and mechanical pro-perties of polycrystalline and single crystal alumina during nanoindentation[J]. Scripta Mater,2011,65(2):127.
65 毛卫国, 万杰, 陈强, 等. 压痕法测试脆性材料的硬度、断裂韧性和残余应力的装置: 中国, CN102393341A[P]. 2012-03-28.
66 毛卫国, 戴翠英, 何远武, 等. 脆性材料断裂韧性和残余应力原位同步测试方法及装置: 中国, CN104075941A[P]. 2014-10-01.
67 Araujo P, Chicot D, Staia M, et al. Residual stresses and adhesion of thermal spray coatings[J]. Surf Eng,2005,21(1): 35.
68 Chicot D, Marot G, Araujo P, et al. Effect of some thermal treatments on interface adhesion toughness of various thick thermal spray coatings[J]. Surf Eng,2006,22(5):390.
69 Chicot D, Araujo P, Horny N, et al. Application of the interfacial indentation test for adhesion toughness determination[J]. Surf Coat Technol,2005,200(1-4):174.
70 Liang K M, Orange G, Fantozzi G. Evaluation by indentation of fracture toughness of ceramic materials[J]. J Mater Sci,1989,25(1):207.
71 Marot G, Lesage J, Démarécaux P, et al. Interfacial indentation and shear tests to determine the adhesion of thermal spray coatings[J]. Surf Coat Technol,2006,201(5):2080.
72 Marot G, Démarécaux P, Lesage J, et al. The interfacial indentation test to determine adhesion and residual stresses in NiCr VPS coatings[J]. Surf Coat Technol,2008,202(18):4411.
73 Khan A N, Lu J, Liao H. Effect of residual stresses on air plasma sprayed thermal barrier coatings[J]. Surf Coat Technol,2003,168(2-3):291.