| INORGANIC MATERIALS AND CERAMIC MATRIX COMPOSITES |
|
|
|
|
|
Microcapsules for Realizing Delayed Release of Early Strength Agent in Repair
Mortar and Their Property Analysis |
| YANG Liukun, PAN Zhihua, XU Saisai, LIU Jingsong
|
| College of Materials Science and Engineering,Nanjing Tech University,Nanjing 210009 |
|
|
|
|
Abstract Aiming at preparing a kind of repair mortar with proper setting time and higher early strength, anhydrous sodium sulfate was microencapsulated and incorporated into the repair mortar. Then the effects of the microcapsules on setting time, compressive strength, development of hydration process, hydration product and the growth rate of ettringite in early hydration of the repair mortar were investigated in depth. The results showed that the setting process of paste was substantially prolonged, the interval of initial and final setting time was shortened, while no obviously variation of compressive strength was found after the anhydrous sodium sulfate microcapsules were incorporated in the repair mortar. Thanks to the addition of the microcapsules, the hydration rate of the paste maintained at a low level in the first 3 h of hydration, then the hydration rate increased obviously, and finally the paste reached the similar hydration degree with the repair mortar adding the same amount of anhydrous sodium sulfate. Besides, the repair mortar with microcapsules exhibited a high growth rate of ettringite in early hydration, and its hydration product could obtain a similar densification with that of the repair mortar adding the same amount of anhydrous sodium sulfate after hydration for 4 h.
|
|
Published: 31 January 2019
|
|
|
| Fund:This work was financially supported by the Priority Academic Program Development of Jiangsu Higher Education Institutions. |
| About author:: Liukun Yang received his M.S. degrees in June 2018 from Nanjing Tech University in engineering, focusing on the research of inorganic and nonmetallic material.Zhihua Pan is the corresponding author. He is a professor who has long been engaged in research on new types of cementitious materials, ecological environment materials, cement concrete chemistry, cement production technology, special concrete preparation and application technology. |
|
|
1 White S R, Sottos N R, Geubelle P H, et al. Nature,2001,409(6822),794.
2 Šavija Branko, Zhang Hongzhi, Schlangen Erik. Materials,2017,10,863.
3 Perez G, Gaitero J J, Erkizia E, et al. Cement and Concrete Composites,2015,60,55.
4 Giannaros P, Kanellopoulos A, Al-Tabbaa A. Smart Materials and Structures,2016,25(8),084005.
5 Choi Y C, Cho Y K, Shin K J, et al. KSCE Journal of Civil Enginee-ring,2016,20(1),282.
6 Dong B, Wang Y, Ding W, et al. Construction and Building Materials,2014,56(3),1.
7 Wang Y, Fang G, Ding W, et al. Scientific Reports,2015,5,18484.
8 Dong B, Wang Y, Fang G, et al. Cement and Concrete Composites,2015,56,46.
9 Wang Y, Ding W, Fang G, et al. Construction and Building Materials,2016,125,742.
10 He Yan, Zhang Xiong, Zhang Yongjuan, et al. Journal of Building Materials,2015,18(3),433(in Chinese).
何燕,张雄,张永娟,等.建筑材料学报,2015,18(3),433.
11 Hu Ting, Yao Xiao, Zhu Huajun. Polymer Materials Science and Engineering,2012,28(8),148(in Chinese).
胡婷,姚晓,诸华军.高分子材料科学与工程,2012,28(8),148.
12 Jambor J. Cement and Concrete Research,1990,20(6),948.
13 Wang Peiming, Feng Shuxia, Liu Xianping. Journal of Building Mate-rials,2005,8(6),646(in Chinese).
王培铭,丰曙霞,刘贤萍.建筑材料学报,2005,8(6),646.
14 Shen Wei. Cement Technology, Wuhan University of Technology Press, China,1991(in Chinese).
沈威.水泥工艺学,武汉理工大学出版社,1991.
15 Yang Jiujun, Guan Zongfu, Yu Haiyan, et al. Journal of the Chinese Ceramic Society,1997(4),470(in Chinese).
杨久俊,管宗甫,余海燕,等.硅酸盐学报,1997(4),470.
16 Yan Lili, Zhou Wen, You Qian, et al. New Building Materials,2015,42(2),41(in Chinese).
颜哩哩,周文,尤迁,等.新型建筑材料,2015,42(2),41. |
|
|
|
渝公网安备50019002502923号 © Editorial Office of Materials Reports.
2019, Vol. 33 