百年混凝土桥梁方形带肋钢筋力学性能研究

doi:10.11896/cldb.24090049

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (24842KB)
Export: BibTeX | EndNote (RIS)

Abstract To study the basic mechanical properties of square ribbed steel bars in concrete bridges, 26 pieces of the square ribbed steel bar samples were acquired from a century-old concrete bridge in Suzhou city, and analyses on surface characteristics, element content, mechanical properties of the samples was carried out by means of macro- and micro-morphology observation, chemical composition measurement, and static tensile test. The results showed that the surface characteristics of square ribbed steel bars in the century-old concrete bridge partly meet the current standard specifications. The microstructure of the steel bars consisted mainly of ferrites and pearlites, with a certain amount of inclusions such as sulfides and silicates in which the content of the latter was significantly higher than that in modern steel bars. The carbon content was less than 0.25%, indicating that the square ribbed steel bars were made of low-carbon steel. The contents of Si and Mn elements met the current standard specifications, while the contents of S and P were higher than the upper acceptable limits in the current standard. The century-old steel bars were measured to have yield strength, ultimate tensile strength, percentage elongation after fracture, elastic modulus, and strength-to-yield ratio (all were average values) of 276.40 MPa, 413.43 MPa, 35.49%, 1.92×10⁵ MPa, and 1.49, respectively. The elastic modulus was slightly lower than that of the steel bars used in modern bridges, while the strength-to-yield ratio and the percentage elongation after fracture both met the current standard specifications for steel bars in bridges. The output of this work provides basic mechanical parameters for concrete bridges and historical buildings at the same period, which are of a certain engineering importance for the maintenance and reinforcement of similar concrete structures.

Key words： century-old concrete bridge square ribbed steel bar surface characteristic mechanical property tensile test

Published: 10 March 2025 Online: 2025-03-18

CLC number:	TB31
	U446.1

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	ZHAI Musai
	LIU Kefan
	TAO Yiran
	CHEN Jianbing

Cite this article:

ZHAI Musai,LIU Kefan,TAO Yiran, et al. Study on Mechanical Properties of Square Ribbed Steel Bars in a Century-old Concrete Bridge[J]. Materials Reports, 2025, 39(5): 24090049-6.

URL:

https://www.mater-rep.com/EN/10.11896/cldb.24090049 OR https://www.mater-rep.com/EN/Y2025/V39/I5/24090049

1 Editorial Department of China Journal of Highway and Transport. China Journal Highway and Transport, 2024, 37(12), 1 (in Chinese).
《中国公路学报》编辑部. 中国公路学报, 2024, 37(12), 1.
2 Wang C S, Zhou J, Wu Q Y, et al. China Journal of Highway and Transport, 2012, 25(6), 101 (in Chinese).
王春生, 周江, 吴全有, 等. 中国公路学报, 2012, 25(6), 101.
3 Shao X D, Qiu M H, Yan B F, et al. Materials Reports, 2017, 31(23), 33 (in Chinese).
邵旭东, 邱明红, 晏班夫, 等. 材料导报, 2017, 31(23), 33.
4 Duffó G S, Morris W, Raspini I, et al. Corrosion Science, 2004, 46(9), 2143.
5 Duffó G S, Reinoso M, Ramos C P. et al. Cement and Concrete Research, 2012, 42(1), 111.
6 Lin F, Gu X L, Xiao B H. Structural Engineers, 2010, 26(1), 108 (in Chinese).
林峰, 顾祥林, 肖炳辉. 结构工程师, 2010, 26(1), 108.
7 Chun Q, Wang J G, Feng S H, et al. Journal of Southeast University(Natural Science Edition), 2014, 44(4), 817 (in Chinese).
淳庆, 王建国, 冯世虎, 等. 东南大学学报(自然科学版), 2014, 44(4), 817.
8 Zheng S J, Bai X, Jiang L X. Building Structure, 2022, 52(3), 78 (in Chinese).
郑士举, 白雪, 蒋利学. 建筑结构, 2022, 52(3), 78.
9 Mi Z D, Chun Q, Jin H. Journal of Huaqiao University(Natural Science), 2023, 44(1), 38 (in Chinese).
糜镇东, 淳庆, 金辉. 华侨大学学报(自然科学版), 2023, 44(1), 38.
10 Shi J G, Li G C, Hu M H, et al. Journal of Architecture and Civil Engineering, 2023, 40(6), 10 (in Chinese).
石建光, 李国聪, 胡红梅, 等. 建筑科学与工程学报, 2023, 40(6), 10.
11 Tian Y, Zhang G Y, Ye H L, et al. Construction and Building Materials, 2023, 369, 130504.
12 Zhang J Q, Song Z W, Han B, et al. China Civil Engineering Journal, 2022, 55(12), 65 (in Chinese).
张劲泉, 宋紫薇, 韩冰, 等. 土木工程学报, 2022, 55(12), 65.
13 Ambroziak A, Haustein E, Niedostatkiewicz M. Materials, 2021, 14(1), 20.
14 Paulík P, Bauvík M, Ševík P, et al. Procedia Engineering, 2016, 156, 326.
15 Wolert P J, Kolodziejczyk M, Stallings J M, et al. Frontiers in Built Environment, 2020, 6, 1.
16 Sena-Cruz J, Ferreira R M, Ramos L F, et al. International Journal of Architectural Heritage, 2013, 7(6), 628.
17 Gebauer J, Harnik A B. Cement and Concrete Research, 1975, 5(2), 163.
18 Hellebois A, Launoy A, Pierre C, et al. Construction and Building Materials, 2013, 44, 149.
19 Czaderski C, Motavalli M. Composites Part B Engineering, 2007, 38, 878.
20 Pettigrew C S, Barr P J, Maguire M, et al. Journal of Bridge Engineering, 2016, 21(9), 04016054.
21 Cao J A, Wen Y S. Journal of Changsha Railway University, 1998, 16(4), 15 (in Chinese).
曹建安, 文雨松. 长沙铁道学院学报, 1998, 16(4), 15.
22 Zhang W P, Li S B, Gu X L, et al. China Journal of Highway and Transport. 2009, 22(2), 53 (in Chinese).
张伟平, 李士彬, 顾祥林, 等. 中国公路学报, 2009, 22(2), 53.