硫铝水泥改性固废基胶凝材料性能与水化进程研究

doi:10.11896/cldb.24090006

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (21264KB)
Export: BibTeX | EndNote (RIS)

Abstract The solid waste based cementitious materials was mainly prepared from steel slag, slag and desulphurized gypsum, it has a long setting time and insufficient mechanical properties. In view of these problems, proposed a method that using calcium sulfoaluminate cement (CSA) to improve the properties of solid waste based cementitious materials. By means of heat of hydration, XRD, FTIR, TG-DSC, SEM and MIP, the influence mechanism of CSA on the hydration process, hardened paste composition and microstructure evolution of solid waste based cementitious materials was investigated, and the modification mechanism was further revealed. The results show that when the content of CSA is 5% (mass fraction), the 3-day and 28-day compressive strength of the cementitious materials reaches 17.7 MPa and 31.1 MPa, respectively, it increased by 21.2% and 23.4% respectively compared with the blank group. CSA in highly active mineral form AFt C₄A₃ rapid hydration, significantly shortens the setting time of solid waste based cementitious materials. CSA accelerates the hydration reaction process of the system, greatly advances the hydration induction period and the hydration heat release peak, and increases the total heat release. However, the addition of CSA reduces the initial pH value of the paste and delays the dissociation process of the slag to a certain extent. As the degree of hydration deepens, more AFt, C-S-H gels and other hydration products will be generated in the system, especially the formation of a large number of C-S-H gels in the late stage of the reaction, improving the bound water content and reaction depth of the system. In the system, needle-rod AFt and C-S-H gels interpenetrate and lap with each other, fill the pores, refine the pore size, and form a more dense microstructure, thus greatly improving the mechanical properties of solid waste based cementitious materials.

Key words： calcium sulfoaluminate cement solid waste based cementitious materials compressive strength hydration process microstructure modification mechanism

Published: 25 September 2025 Online: 2025-09-11

CLC number:

TU526

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	REN Caifu
	WANG Dongmin
	FANG Kuizhen
	WANG Jixiang
	LI Xiaohui
	ZHANG Xinlong

Cite this article:

REN Caifu,WANG Dongmin,FANG Kuizhen, et al. Study on Properties and Hydration Process of Solid Waste Based Cementitious Materials Modified by Calcium Sulfoaluminate Cement[J]. Materials Reports, 2025, 39(18): 24090006-8.

URL:

https://www.mater-rep.com/EN/10.11896/cldb.24090006 OR https://www.mater-rep.com/EN/Y2025/V39/I18/24090006

1 Busch P, Kendall A, Murphy C W, et al. Resources, Conservation and Recycling, 2022, 182, 106278.
2 Zhang C, Yu B, Chen J, et al. Resources, Conservation and Recycling, 2021, 166, 105355.
3 Gao T, Shen L, Shen M, et al. Journal of Cleaner Production, 2015, 103, 160.
4 Wu K, Shi H, Guo X. Waste Management, 2011, 31(9-10), 2001.
5 Sethurajan M, van Hullebusch E D, Nancharaiah Y V. Journal of environmental Management, 2018, 211, 138.
6 Guo J, Bao Y, Wang M. Waste Management, 2018, 78, 318.
7 Dhoble Y N, Ahmed S. Journal of Material Cycles and Waste Management, 2018, 20, 1373.
8 Rahou J, Rezqi H, EI Ouahabi M, et al. Construction and Building Materials, 2022, 314, 125663.
9 Gołaszewski J, Klemczak B, Gołaszewska M, et al. Journal of Building Engineering, 2023, 66, 105893.
10 Xu C, Ni W, Li K, et al. Construction and Building Materials, 2021, 288, 123111.
11 Xu D, Ni W, Wang Q, et al. Journal of Cleaner Production, 2021, 307, 127262.
12 Wang X, Ni W, Li J, et al. Cement and Concrete Research, 2019, 125, 105893.
13 Cui X W, Ni W, Ren C. Journal of Materials Research, 2017, 31, 687.
崔孝炜, 倪文, 任超. 材料研究学报, 2017, 31(9), 687.
14 Ma X M, Ni W, Liu X. Materials Reports, 2016, 30(16), 135.
马旭明, 倪文, 刘轩. 材料导报, 2016, 30(16), 135.
15 Ren C, Wang J, Duan K, et al. Materials, 2024, 17, 1999.
16 Liu S, Wang L, Gao Y, et al. Thermochimica Acta, 2015, 605, 37.
17 Liu S, Li L. Journal of Thermal Analysis and Calorimetry, 2014, 117, 629.
18 Gao W, MA X, Wang Z, et al. Colloids and Surfaces A: Physicochemical and Engineering Aspects, 2011, 389, 230.
19 Grounds T, Nowell D, WilburnF. Journal of Thermal Analysis and Calorimetry, 1995, 45, 385.
20 Lan M Z, Zhao X D, Chen Z F, et al. Bulletin of Silicate, 2017, 36(9), 2958
兰明章, 赵旭东, 陈智丰, 等. 硅酸盐通报, 2017, 36(9), 2958.
21 Sun Z N, Zhou J, Mu R, et al. Bulletin of Silicate, 2019, 38, 2362.
孙正宁, 周健, 慕儒, 等. 硅酸盐通报, 2019, 38(8), 2362.
22 Chen P, Ma B, Tan H, et al. Construction and Building Materials, 2023, 377, 131034.
23 Sun Z, Nie S, Zhou J, et al. Journal of Cleaner Production, 2022, 333, 130094.
24 Idrissi M, Diouri, A, Damidot D, et al. Cement and Concrete Research, 2010, 40, 1314.
25 Matschei T, Bellmann F, Stark J. Advances in Cement Research, 2005, 17, 167.
26 Huang B Y, Cui S P, Wang Y L, et al. Bulletin of Silicate, 2023, 42, 56.
黄炳银, 崔素萍, 王亚丽, 等. 硅酸盐通报, 2023, 42(5).
27 Wang Q, Yan P, Han S. Science China Technological Sciences, 2011, 54, 388
28 Wang Q, Yan P. Construction and Building Materials, 2010, 24, 1134.
29 Gruskovnjak A, Lothenbach B, Winnefeld F, et al. Cement and Concrete Research, 2008, 38, 983.
30 Moghaddam S E, Hejazi V, Hwang S H, et al. Journal of Materials Chemistry A, 2017, 5, 3798.
31 Zhou Y, Hou D, Jiang J, et al. Construction and Building Materials, 2016, 126, 991.
32 Matschei T, Bellmann F, Stark J. Advances in Cement Research, 2005, 17, 167.
33 Erdem E, Ölmez H. Cement and Concrete Research, 1993, 23, 115.
34 Chen Z X, Chu S H, Lee Y S, et al. Journal of Cleaner Production, 2020, 262, 121385.
35 Kazanskaya L F, Smirnova O M, Palomo A, et al. Materials, 202, 14, 403.
36 Hegazy A A, Khalil A A, El-Alfi, E A, et al. Egyptian Journal of Chemistry, 2019, 62, 1145.
37 Sun R, Wang D, Fang Z, et al. Cement and Concrete Composites, 2022, 131, 104588.
38 Wang Q, Yan P, Han S. Science China Technological Sciences, 2011, 54, 388.
39 Hu Y, Ren X, Ye J, et al. Construction and Building Materials, 2022, 346, 128471.