温度、浓度对水/乙醇混合溶剂中壳聚糖溶液黏度的影响

doi:10.11896/j.issn.1005-023X.2017.024.022

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (652KB)
Export: BibTeX | EndNote (RIS)

Abstract The change low of viscosity of chitosan solution in water/ethanol mixed solvent with the temperature and concentration was investigated. Water with 1% (volume) acetic acid added was used as the good solvent. Ethanol, an organic solvent, was the poor solvent. Different proportion of ethanol volume mixed with water solution was acted as poor solvents which could provide solubility of regular difference, respectively. Ubbelohde viscometer was used as the viscosity measuring instrument. And the change low of viscosity of chitosan solution with temperature and concentration was measured. The experimental results showed that the viscosity of chitosan solution reduced with the increasing of temperature. And it would be increased with the increasing of concentration, following the constant temperature. When chitosan solution was in good solvent, the change rate of specific viscosity was higher than that in poor solvent. With the increasing of concentration, the change rate of specific viscosity was increased correspondingly. In the extremely dilute concentration, the(η_sp/C)/C curve of chitosan solution would appear abnormal phenomenon where the viscosity of chitosan solution increased sharply with the decreasing of concentration.

Key words： chitosan temperature concentration ethanol-water mixed solvent viscosity

Published: 25 December 2017 Online: 2018-05-08

CLC number:

TB324

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	YANG Shuai
	ZHANG Keke
	CUI Jing
	ZHANG Dawei

Cite this article:

YANG Shuai,ZHANG Keke,CUI Jing, et al. Effect of Temperature and Concentration on the Viscosity of Chitosan Solution in Water/Ethanol Mixed Solvent[J]. Materials Reports, 2017, 31(24): 109-113.

URL:

https://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2017.024.022 OR https://www.mater-rep.com/EN/Y2017/V31/I24/109

1 Croisier F, Jérme C. Chitosan-based biomaterials for tissue engineering[J]. Eur Polym J, 2013,49(4):780.
2 LogithKumar R, KeshavNarayan A, Dhivya S, et al. A review of chitosan and its derivatives in bone tissue engineering[J]. Carbohyd Polym, 2016,151:172.
3 Islam A, Yasin T, Bano I, et al. Controlled release of aspirin from pH sensitive chitosan/poly (vinyl alcohol) hydrogel[J]. J Appl Polym Sci, 2012,124(5):4184.
4 Dutta P K, Khatua M K, Dutta J, et al. Use of Chitosan-DMAc/LiCl gel as drug carriers[J]. J Chem Sci, 2003,1:93.
5 Usman A, Zia K M, Zuber M, et al. Chitin and chitosan based polyurethanes: A review of recent advances and prospective biomedical applications[J]. Int J Biol Macromol, 2016,86:630.
6 Rafique A, Zia K M, Zuber M, et al. Chitosan functionalized poly(vinyl alcohol) for prospects biomedical and industrial applications: A review[J]. Int J Biol Macromol, 2016,87:142.
7 Tsaih M L, Chen R H. Effect of ionic strength and pH on the diffusion coefficients and conformation of chitosans molecule in solution[J]. J Appl Polym Sci, 2015,73(10):2042.
8 EI-hefian E A, Yahaya A H. Rheological study of chitosan and its blends: An overview[J]. Maejo Int J Sci Technol,2010,4(2):210.
9 Luo Y J, Cheng R S, Tan H M. Relationship between viscosity and concentration of nitrocellulose[J]. Chin J Expl Propell, 1999,18(2):42(in Chinese).
罗运军, 程镕时, 谭惠民. 硝化纤维素在稀溶液中的黏度与浓度的依赖关系[J]. 火炸药学报, 1999,18(2):42.
10Dondos A, Skondras P, Pierri E. Hydrodynamic crossover in two polymer mixtures from viscosity measurements[J]. Makromolekulare Chemie, 1983,184(10):2153.
11De Gennes P G. Scaling concepts in polymer physics[M]. Lthaca: Cornell University Press, 1979.
12钱人元, 曹娣. 用分子间激基缔合物荧光研究聚苯乙烯良溶剂溶液——从稀区到亚浓区和浓区的转变[J]. 中国科学(化学), 1983,13(12):1080.
13Wang W. Dilute solution properties of chitosan[J]. Acta Polymerica Sinica, 1992,1(2):202.
王伟. 壳聚糖稀溶液性质的研究[J]. 高分子学报, 1992,1(2):202.