| RESEARCH PAPER |
|
|
|
|
|
| Very High Cycle Fatigue Behaviors of Bainite/Martensite Multi-phase Steel and Mechanism of Non-inclusion Induced Crack Initiation |
| GAO Guhui1, CHEN Qianru2,3, GUO Haoran1, CHENG Cheng1, BAI Bingzhe1
|
1 School of Mechanical, Electronic and Control Engineering,Beijing Jiaotong University,Beijing 100044;
2 College of Petroleum Engineering,Xi’an Shiyou University,Xi’an 710065;
3 Well Cementing Compangy,CNPC Chuanqing Drilling Engineering Company Limited,Xi’an 710018 |
|
|
|
|
Abstract In order to improve the fatigue properties of the steel component used in high speed railway and oil exploration, the bainite/martensite (B/M) multiphase high strength steels with excellent fatigue properties have been developed. Many results showed that the very high cycle fatigue (VHCF) property of B/M steels is less sensitive to the inclusion than that of conventional tempered martensite steels. Hence, both non-inclusion and inclusion-induced crack initiations occurred in the B/M steels under VHCF test. The microstructure morphologies, i.e., phase types, microstructure homogeneity and refinement degree,could influence the non-inclusion induced crack initiation. The VHCF crack initiation sites are determined by the competition between the inclusion level and the microstructure morphologies of the B/M steels. Enhanced VHCF properties of B/M steels have been achieved through coordinated adjustment of physical and/or chemical metallurgy treatment (e.g., microstructure optimization and inclusion size reduction). The mechanism of non-inclusion induced crack initiations is also discussed.
|
|
Published: 25 October 2017
Online: 2018-05-05
|
|
|
|
|
1 李鹤林,李平全,冯耀荣. 石油钻柱失效分析及预防 [M]. 北京:石油工业出版社,1999.
2 Macdonald K, Bjune J V. Failure analysis of drill strings[J]. Eng Failure Analysis, 2007,14(8):1641.
3 Li Helin, Ji Lingkang, Xie Lihua. Current situation analysis of oil steel pipe in China [J], J Hebei Univer Sci Technol, 2006,27(1):1(in Chinese).
李鹤林,吉玲康,谢丽华. 中国石油钢管的发展现状分析 [J]. 河北科技大学学报,2006,27(1):1.
4 Zhou Chengen, Xie Jijia, Hong Youshi. Retrospect and prospect of very high cycle fatigue[J]. J Mech Strength, 2004,26(5):526(in Chinese).
周承恩,谢季佳,洪友士. 超高周疲劳研究现状及展望 [J]. 机械强度,2004,26(5):526.
5 Wang Qingyuan, Liu Yongjie. Very high fatigue behaviors of the metal structural materials [J]. Chin J Solid Mech, 2010,31(5):496(in Chinese).
王清远,刘永杰. 结构金属材料超高周疲劳破坏行为 [J]. 固体力学学报,2010,31(5):496.
6 Sakai T. Review and prospects for current studies on very high cycle fatigue of metallic materials for machine structural use [J]. J Solid Mech Mater Eng, 2009,3(3):425.
7 Shiozawa K, Morii Y, Nishino S, et al. Subsurface crack initiation and propagation mechanism in high strength steel in a very high cycle fatigue regime [J]. Int J Fatigue, 2006,28:1521.
8 Murakami Y, Nomoto T, Ueda T. Factors influencing the mechanism of superlong fatigue failure in steels [J]. Fatigue Fract Eng Mater Struct, 1999,22:581.
9 Yu Y, Gu J, Shou F, et al. Competition mechanism between microstructure type and inclusion level in determining VHCF behavior of bainite/martensite dual steels [J]. Int J Fatigue, 2011,33:500.
10Yu Y, Gu J, Xu L, et al. Very high cycle fatigue behaviors of Mn-Si-Cr series bainite/martensite dual phase steels [J]. Mater Des, 2010,31:3067.
11Zhao P, Gao G, Misra R, et al. Effect of microstructure on the very high cycle fatigue behavior of a bainite/martensite multiphase steel [J]. Mater Sci Eng A, 2015,630:1.
12Zhao P, Cheng C, Gao G et al. The potential significance of microalloying with niobium in governing very high cycle fatigue behavior of bainite/martensite multiphase steels [J]. Mater Sci Eng A, 2016,650:438.
13Yang Z, Zhang J, Li S, et al. On the critical inclusion size of high strength steels under ultra-high cycle fatigue [J]. Mater Sci Eng A, 2006,427:167.
14Yu Yang. Study on very high cycle fatigue behaviors and mechanism of Mn-Si-Cr series bainite/martensite duplex-phase high strength steels [D]. Beijing:Tsinghua University, 2010(in Chinese).
于洋. Mn-Si-Cr系贝/马复相高强钢超高周疲劳行为及机理研究 [D]. 北京:清华大学,2010.
15Shiozawa K, Lu L, Ishihara S. S-N curve characteristics and subsurface crack initiation behaviour in ultra-long life fatigue of a high carbon-chromium bearing steel [J]. Fatigue Fract Eng Mater Struct, 2001,24:781.
16Hong Y, Lei Z, Sun C, et al. Propensities of crack interior initiation and early growth for very-high-cycle fatigue of high strength steels [J]. Int J Fatigue, 2014,58:144.
17Chai G. Fatigue behaviour of duplex stainless steels in the very high cycle regime [J]. Int J Fatigue, 2006,28:1611.
18Gao G, Zhang B, Cheng C, et al. Very high cycle fatigue behaviors of bainite/martensite multiphase steel treated by quenching-partitioning-tempering process [J]. Int J Fatigue, 2016,92:203. |
|
|
|
渝公网安备50019002502923号 © Editorial Office of Materials Reports.
2017, Vol. 31 