| RESEARCH PAPER |
|
|
|
|
|
| Preparation of Closed Pore Foamed Ceramics Through Complex Foaming Method by Using Porcelain Tile Residues |
| YANG Zanzhong1,2, WANG Han1, WANG Yongzai3, LIU Min1, DING Qi1, LI Chengfeng1, YUE Hongzhi1,2, WEI Chuncheng1,2
|
1 School of Materials Science and Engineering, Shandong University of Technology, Zibo 255049;
2 Shandong Engineering Research Demonstration Center of Ceramic-matrix Composites, Zibo 255049;
3 Analysis and Testing Center, Shandong University of Technology, Zibo 255049 |
|
|
|
Abstract The foamed ceramics was prepared by complex foaming process using porcelain tile residues as the raw material. The mass ratio of complex agents was determined by the orthogonal test, and the complex foaming mechanism and the firing system were investigated. It was shown that the temperature range of pore-forming was broadened when the complex agent foaming acted mutually, and that the homogeneous pore structure could be formed. Samples in investigation were prepared by adding complex foaming agents in accordance with the mass fraction (%) of carbon∶calcium carbonate∶iron(Ⅲ) oxide∶silicon carbide=1∶3∶1.5∶1, and being calcined at 1 160 ℃ for 100 min. The closed porosity of the foamed ceramics is 62.94%, and its pore diameters are 1.2—1.9 mm. The volume density, water absorption, and thermal conductivity of the resultant are 369 kg/m3, 0.44%, and 0.079 W/(m·K) respectively.
|
|
Published: 25 October 2017
Online: 2018-05-05
|
|
|
|
|
1 Cai Zuguang. The processing of ceramic industrial waste slag [J]. Foshan Ceram, 2002,12(3):11(in Chinese).
蔡祖光. 陶瓷工业废料废渣的处理 [J]. 佛山陶瓷,2002,12(3):11.
2 Miao Songlan, Ma Guanghua, Li Qingtao, et al. Research on the preparation of light-weight ceramic material with the slag polished from building ceramics [J]. J Ceram, 2005,6(2):71(in Chinese).
缪松兰,马光华,李清涛,等. 建筑陶瓷抛光废渣制备轻质陶瓷材料的研究 [J].陶瓷学报,2005,6(2):71.
3 Amoros J L,Orts M J,Garca-Ten J. Effect of the green porous texture on porcelain tile properties [J]. J Am Chem Soc, 2007,27(5):2295.
4 Xia Guanghua, Zhao Xiaodong, Xie Sui, et al. The current situation in utilization of solid waste resource of ceramic industry [J]. Environ Eng, 2012(S2):302(in Chinese).
夏光华,赵晓东,谢穗,等. 陶瓷工业固体废物资源化利用现状 [J]. 环境工程,2012(S2):302.
5 Xi Xiuan, Shui Anze. Effects of magnesium oxychloride and silicon carbide additives on the foaming property during firing for porcelain ceramics and their microstructure [J]. J Eur Chem Soc, 2012,32(12):3035.
6 Zhou Mingkai, Peng Lifen, Wang Huaide, et al. Influence of iron oxide and foaming agent on the performance of coal gangue closed porosity ceramics [J]. China Ceram, 2015,51(2):77(in Chinese).
周明凯,彭丽芬,王怀德,等. 氧化铁和发泡剂对煤矸石闭孔发泡陶瓷的性能影响 [J].中国陶瓷,2015,51(2):77.
7 Wu Zhimin, Xu Jinfeng, Zhang Haixia, et al. Application research on thermal insulating board and fire barrier in building [J]. New Build Mater, 2010(10):1(in Chinese).
吴志敏,许锦峰,张海遐,等. 发泡陶瓷保温板保温系统及防火隔离带建筑应用研究 [J].新型建筑材料,2010(10):1.
8 Liu Bin, Liu Hui, Zhang Chunyan. Application of foamed ceramic thermal insulating board in roof engineering [J]. Chin Overseas Arch, 2012(11):102(in Chinese).
刘彬,刘辉,张春艳. 发泡陶瓷保温板在屋面工程中的应用 [J].中外建筑,2012(11):102.
9 Chi Yuezhang, Yu Aimin, Shen Guangyin, et al. The influence of forming pressure and firing temperature on producing closed porosity ceramics using solid residue and tailings [J]. China Ceram, 2009,45(10):69(in Chinese).
池跃章,余爱民,沈光银,等. 成型压力和烧成温度对利用废渣和尾矿制备闭孔发泡陶瓷的影响 [J].中国陶瓷,2009,45(10):69.
10Yu Kaiming, Jiang Chao, Yu Shaohua. The preparation of alumina foaming porous ceramics [J]. China Ceram, 2014,50(2):51(in Chinese).
余开明,江超,余少华. 氧化铝泡沫多孔陶瓷的制备 [J].中国陶瓷,2014,50(2):51.
11Li Yang, Gong Yingfang, Wang Lin. The preparation of alumina foaming porous ceramics [J]. Bull Chin Ceram Soc, 2014,33(7):1636(in Chinese).
黎阳,宫营方,汪林. 化学结合法低温制备氧化铝泡沫陶瓷的研究 [J].硅酸盐通报,2014,33(7):1636.
12García-Ten J, Saburit A, Bernardo E, et al. Development of light weight porcelain stoneware tiles using foaming agents [J]. J Am Chem Soc, 2012,32:745.
13Bernardin A M, Silva M J, Riella H G. Characterization of cellular ceramics made by porcelain tile residues [J]. Mater Sci Eng A, 2006,437(2):222.
14Shui Anze, Xia Haibin, Zeng Lingke, et al. Preparation of porous thermal insulation building material with tile polished waste[J]. Bull Chin Ceram Soc, 2008,27(1):191(in Chinese).
税安泽,夏海斌,曾令可,等. 利用抛光砖废料制备多孔保温建筑材料 [J].硅酸盐通报,2008,27(1):191.
15Huang Jian, Bao Qifu, Dong Weixia, et al. Research on foam ceramics with silicate waste [J]. China Ceram, 2014,50(12):78(in Chinese).
黄健,包启富,董伟霞,等. 用硅酸盐废弃物制备泡沫陶瓷的研究 [J]. 中国陶瓷,2014,50(12):78.
16Fernández-Jiménez A, De La Torre A G, Palomoa A, et al. Quantitative determination of phases in the alkali activation of fly ash. Part I. Potential ash reactivity [J]. Fuel, 2006,85(5):625.
17Liu Qiuxia, Han Qingrong. Mathematical analyses of factors affec-ting the bubble diameter of foam glass [J]. Bull Chin Ceram Soc, 1999(5):63(in Chinese).
刘秋霞,韩庆荣. 影响泡沫玻璃泡径因素的数学分析 [J]. 硅酸盐通报,1999(5):63.
18Shui Anze, Xi Xiuan, Wang Yanming, et al. Effect of silicon carbide additive on microstructure and properties of porcelain ceramics [J]. Ceram Int, 2010,37(5):1557.
19浙江大学,武汉工业大学,上海化工学院,等. 硅酸盐物理化学 [M]. 中国建筑工业出版社,1987:236.
20Jacobson N S. Kinetics and mechanism of corrosion of SiC by molten salts [J]. J Am Ceram Soc,1986,69:74.
21Gary R,Sun T W,Brown J R. High temperature alkali corrosion of SiC and S3N4[J]. Fuel Process Technol, 1995,44:213. |
| No related articles found! |
|
|
|
|
渝公网安备50019002502923号 © Editorial Office of Materials Reports.
2017, Vol. 31 