钛合金压印接头疲劳性能与微观分析

doi:10.11896/j.issn.1005-023X.2017.06.017

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (1632KB)
Export: BibTeX | EndNote (RIS)

Abstract Mechanical clinching is a widely used connection technology in different industrial fields. Because it has several advantages such as simple operating process, high efficiency and so forth. Fatigue damage is a main failure mode of the metal mechanical part. In this paper, tensile-shear tests and fatigue test were carried out to characterize the mechanical properties of the clinched joints of titanium alloy. The tensile-shear strength of the clinched joint of titanium alloy was about 36.7% of that of the material itself with equal size. The fatigue strength for titanium alloy sheets joined by clinching was about 46% of that of titanium alloy and about the average load was about 42% of the static strength of clinched joints. Microscopic characteristics showed that the fracture was brittle fatigue fracture. Fatigue abrasive dust with high hardness was produced due to the fretting wear and oxidation which acted as micro abrasive in the process of fretting wear. In this way, it accelerated the abrasion and crack propagation and eventually leaded to fatigue failure.

Key words： titanium alloy mechanical clinching fatigue property fretting wear

Published: 25 March 2017 Online: 2018-05-02

CLC number:

TG3

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	ZHANG Yue
	HE Xiaocong
	ZHANG Long
	ZHANG Xianlian

Cite this article:

ZHANG Yue,HE Xiaocong,ZHANG Long, et al. Fatigue Property and Microanalysis of Clinched Joints of Titanium Alloy[J]. Materials Reports, 2017, 31(6): 81-85.

URL:

https://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2017.06.017 OR https://www.mater-rep.com/EN/Y2017/V31/I6/81

1 Xu T C, Peng X D, Jiang J W, et al. Study on application of new technology of dissimilar materials of titanium alloy connection [J]. Rare Met,2014(4):711(in Chinese).
许天才,彭晓东,姜军伟,等.钛合金连接异种材料新技术的研究应用[J].稀有金属,2014(4):711.
2 李亚江,王娟,刘强.有色金属焊接及应用[M]. 北京:化学工业出版社,2006.
3 He X C, Gu F S, Ball A. Fatigue behavior of fastening joints of sheet materials and finite element analysis[C]//International Conference on Solid State and Materials.Losangeles,2013.
4 Mucha J. The analysis of lock forming mechanism in the clinching joint [J]. Mater Des,2011,32(10):4943.
5 Luo X Y, Zhao R G,He W, et al. Analysis on low cycle fatigue properties and fractography of TC25 titanium alloy [J]. Acta Mech Solida Sin,2011(1):145(in Chinese).
罗希延,赵荣国,何伟,等.TC25钛合金低周疲劳特性与断口分析[J].固体力学学报,2011(1):145.
6 Lambiase F. Mechanical behavior of polymer-metal hybrid joints produced by clinching using different tools [J]. Mater Des,2015,87:606.
7 Lee C J, Kim J Y, Lee S K, et al. Parametric study on mechanical clinching process for joining aluminum alloy and high-strength steel sheets [J]. J Mater Process Technol,2010,24:123.
8 He X C, Zhao L, Yang H Y, et al. Investigations of strength and energy absorption of clinched joints[J]. Comput Mater Sci,2014,94:58.
9 He X C, Liu F L, Xing B Y, et al. Numerical and experimental investigations of extensible die clinching [J]. Int J Adv Manuf Tech-nol,2014,74:1229.
10 He X C, Zhang Y, Xing B Y, et al. Mechanical properties of extensible die clinched joints in titanium sheet materials [J]. Mater Des,2015,71:26.
11 Lambiase F. Damage analysis in mechanical clinching: Experimental and numerical study [J]. J Mater Process Technol,2016,230:109.
12 Eshtayeh M M, Hrairi M, Mohiuddin A K M. Clinching process for joining dissimilar materials: State of the art [J]. Int J Adv Manuf Technol,2016,82:179.
13 Mori K, Abe Y, Kato T. Mechanism of superiority of fatigue strength for aluminum alloy sheets joined by mechanical clinching and self-pierce riveting [J]. J Mater Process Technol,2012,212:1900.
14 Carboni M, Beretta S, Monno M. Fatigue behavior of tensile-shear loaded clinched joints [J]. Eng Fracture Mech,2006,73:178.
15 Abe Y, Kato T, Mori K. Mechanical clinching of ultra-high strength steel sheets and strength of joints [J]. J Mater Process Technol,2014,214:2112.
16 Yang H Y, He X C, Wang Y Q, et al. Tensile-shear and fatigue properties of clinched joint in cold rolled mild steel sheets [J]. Mech Des,2013,30(9):78(in Chinese).
杨慧艳,何晓聪,丁燕芳,等. 冷轧钢压印接头拉伸-剪切和疲劳性能研究[J].机械设计,2013,30(9):78.
17 Li H M, Song G, Liu Y Z. Estimating formula of fatigue limits for metallic materials [J].J Zhengzhou University: Eng Sci,2002(4):26(in Chinese).
李海梅,宋刚,刘永志.金属材料疲劳极限的估算[J].郑州大学学报:工学版,2002(4):26.
18 Ding S D, Yang G Z. Estimation of unsymmetrical cycle fatigue li-mits for titanium alloy smooth specimens [J]. J Mech Strength,2001(3):371(in Chinese).
丁遂栋,杨国战.钛合金光滑试样非对称循环疲劳极限的估算[J].机械强度,2001(3):371.
19 钟群鹏,赵子华.断口学[M].北京:高等教育出版社,2006:349.
20 何明鉴.机械构件的微动疲劳[M].北京:国防工业出版社,1994:225.