多孔金属材料的化学制备方法及性能研究进展<sup>*</sup>

doi:10.11896/j.issn.1005-023X.2017.021.020

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (1685KB)
Export: BibTeX | EndNote (RIS)

Abstract In order to optimize the preparation method, deeply cognize the properties and extend the application of porous metallic materials, the present paper reviews the preparation methods, properties and applications of porous metallic materials. Preparation methods mainly include the electrodeposition method, dealloying method, solid-state sintering process and liquid solidification. Based on the sound absorption properties, separation performance, thermal and electrical conductivities and catalytic performance of porous metallic materials, the applications of porous metallic materials in automotive industry, aerospace industry and biomedical fields are introduced. The paper ends with a brief description of the future development trend of porous metallic materials,i.e. compositing,introducing gradient and diversifying porous structures.

Key words： porous metallic material chemical preparation method performance

Published: 10 November 2017 Online: 2018-05-08

CLC number:	TB34
	O61

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	CAO Feng
	ZHANG Wenyan
	ZHANG Sisi
	YAN Yangtian
	YANG Ruifeng

Cite this article:

CAO Feng,ZHANG Wenyan,ZHANG Sisi, et al. A Technological and Performance Review of Chemically Prepared Porous Metallic Materials[J]. Materials Reports, 2017, 31(21): 139-145.

URL:

https://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2017.021.020 OR https://www.mater-rep.com/EN/Y2017/V31/I21/139

1 Dvies G J, Zhen S. Metallic foam: their production, properities and applications[J]. J Mater Science, 1983(18): 1899.
2 Kostevsek N, Kristina Z R, Darja P, et al. A comparative study of the electrochemical deposition kinetics of iron-palladium alloys on a flat electrode and in a porous aluminatemplate[J]. Electrochim Acta, 2014, 125:320.
3 Tan K, Tian M B, Cai Q. Effect of bromide ions and polyethylene glycol on morphological contronl of electrodeposited copper foam[J]. Thin Solid Films, 2010, 518:5159.
4 Tian Q H, Guo X Y. Electrodeposition for manufacturing microcellular foamed zinc material with high porosity[J]. Mater Sci Tech-nol, 2010, 18(5):644(in Chinese).
田庆华, 郭学益. 电沉积法制备高孔隙率微孔金属锌泡沫材料[J]. 材料科学与工艺, 2010, 18(5):644.
5 Gao M Y, Yang C, Zhang Q B, et al. Electrochemical fabrication of porous Ni-Cu alloy nanosheets with high catalytic activity for hydrogen evolution[J]. Electrochim Acta, 2016, 215:609.
6 Xiong Q Q, Qin H Y, Chi H Z, et al. Synthesis of porous nickel networks supported metal oxide nanowire arrays as binder-free anode for lithium-ion batteries[J]. J Alloy Compd, 2016, 685:15.
7 Poizot S, Laruelle S, Grugeon S, et al. Nano-sized transition-metal oxides as negativeelectrode materials for lithium-ion batteries[J]. Nature, 2000, 407:496.
8 Xiao A G, Zhou S B, Zuo C G, et al. Electrodeposited porous metal oxide films with interconnectednanoparticles applied as anode of lithium ion battery[J]. Mater Res Bull, 2014, 60:864.
9 Zhang W Y, Xi Z P, Fang M, et al. Research Progress on Metallic Nanoporous Materials[J]. Rare Met Mater Eng, 2008, 37(7):1129(in Chinese).
张文彦, 奚正平, 方明等. 纳米孔结构金属多孔材料研究进展[J]. 稀有金属材料与工程, 2008, 37(7):1129.
10Yu-chen Karen Chen-Wiegart, Steve Wang, Ian McNulty, et al. Effect of Ag-Au composition and acid concentration on dealloying front velocity and cracking during nanoporous gold formation[J]. Acta Mater, 2013, 61(15):5561.
11Chen F, Chen Xi, Zou L J, et al. Fabrication and mechanical beha-vior of bulk nanoporous Cu via chemical dealloying of Cu-Al alloys[J]. Mater Sci Eng A, 2016,660:241.
12Li Y N, Li G Z, Zhang W Y, et al. Nanoporous Ti alloy foam prepared by dealloying[J]. Rare Met Mater Eng, 2013, 42(10):2197(in Chinese).
李亚宁, 李广忠, 张文彦,等. 脱合金法制备纳米多孔泡沫钛合金[J]. 稀有金属材料与工程, 2013, 42(10):2197.
13Sun Y X, Ren Y B, Yang K. New preparation method of micron porous copper through physicalvacuum dealloying of Cu-Zn alloys[J]. Mater Lett, 2016, 165:1.
14Zeng Y Q, Dong X Z, Yang C L, et al. Pd-based multicomponent nanoporous metals with enhanced electrocatalytic performance prepared by dealloying metallic glass[J].Rare Metal Mater Eng, 2015, 44(1):54.
15Wang L C, Personick M L, Karakalos S, et al. Active sites for methanol partial oxidation on nanoporous gold catalysts[J]. J Catal, 2016, 344:778.
16Jiang X L, Cai F, GaoD F, et al. Electrocatalytic reduction of carbon dioxide over reduced nanoporous zinc oxide[J]. Electrochem Commu, 2016, 68:67.
17Zou C M, Zhang E L, Zeng S Y. Porous titanium by fiber sintering and its biomimetic Ca-P coating[J]. Rare Met Mater Eng, 2007, 36(8):1394(in Chinese).
邹鹑鸣, 张二林, 曾松岩. 纤维烧结多孔钛及其表面生长仿生Ca-P涂层[J]. 稀有金属材料与工程, 2007, 36(8):1394.
18Murakami T, Akagi T, Kasai E. Development of porous iron based material by slag foaming and its reduction[J]. Procedia Mater Sci, 2014, 4:27.
19Nilsén F, Lehtonen J, Ge Y L, et al. Highly porous spark plasma sintered Ni-Mn-Ga structures[J]. Scr Mater, 2017, 139:148.
20Feng W, Kong Q Q, Zhu X D. Preparation of porous aluminum bulk material by SPS with sublimate material as pore-forming agent[J]. Powder Metall Ind, 2016, 26(2):38(in Chinese).
冯威, 孔清泉, 朱晓东等. 添加升华性造孔剂的放电等离子法制备多孔铝块体材料[J].粉末冶金工业, 2016, 26(2):38.
21Covaciu M, Walczak M, Ramos-grez J. A method for manufacturing cellular metals with open- and close-type porosities[J]. Mater Lett, 2011, 65:2947.
22Wang H, Zhou X Y, Long B, et al. Sound absorption properties of open-cells aluminum foams prepared by infiltration casting methods[J].Chin J Nonferr Met, 2013, 23(4):1034.
王辉, 周向阳, 龙波等. 渗流铸造法制备的开孔泡沫铝的声学性能[J]. 中国有色金属学报, 2013, 23(4):1034.
23Zhu J L, Sun J, Tang H P, et al. Gradient-structural optimization of metal fiber porous materials for sound adsorption[J]. Powder Technol, 2016, 301:1235.
24Liu P S, Qing H B, Hou H L. Primary investigation on sound absorption performance of highly porous titanium foams[J]. Mater Des, 2015, 85:275.
25Lu M, Meng B N, Liu P S, et al. Effect of perforated panel combination on sound absorption performance of nickel foam[J]. Rare Met Mater Eng, 2015,44(12):3083(in Chinese).
卢淼, 孟泊宁, 刘培生等. 穿孔板组合对电沉积泡沫镍吸声性能的影响[J]. 稀有金属材料与工程,2015, 44(12):3083.
26Dong L F. The filtration accuracy of sintered metal porous materials[J]. J Filtr Sep, 2016, 26(2):31(in Chinese).
董领峰. 烧结金属多孔材料的过滤精度[J]. 过滤与分离, 2016, 26(2):31.
27Liu P S, Liang K M,Gu S R, et al. Substrate materials of porous metal electrode[J]. Chin J Rare Met, 2000, 24(6):440(in Chinese).
刘培生, 梁开明, 顾守仁等. 多孔金属电极基体材料[J]. 稀有金属, 2000, 24(6):440.
28Li X D, Wu G X, Liu X, et al. Orderly integration of porous TiO₂(B) nanosheets into bunchy hierarchical structure for high-rate and ultralong-lifespan lithium-ion batteries[J]. Nano Energy, 2017, 31:1.
29Zhao D D, Ru Q, Guo L Y, et al. ZnCo₂O₄ nanoflake arrays grown on Ni foam as anode material[J]. Battery Bimonthly, 2016, 46(2):61(in Chinese).
赵豆豆, 汝强, 郭凌云等. 泡沫镍上生长纳米片ZnCo₂O₄负极材料[J]. 电池, 2016,46(2):61.
30Ji Y W, Qiu S, Li G M, et al. Degradation of RhB by ultrasound combined with foamy copper[J]. Technol Water Treat, 2016, 42(5):51(in Chinese).
冀雅婉, 邱珊, 李光明等. 超声-泡沫铜耦合降解罗丹明B[J]. 水处理技术, 2016, 42(5):51.
31Liu Y X, Deng J G, Xie S H, et al. Catalytic removal of volatile organic compounds using ordered porous transition metal oxide and supported noble metal catalysts[J]. Chin J Catal, 2016, 37(8):1193.
32赵文浩. 列车用泡沫铝复合地板制造工艺[J]. 冷热工艺, 2016, (2):25.
33Zhao L C, Zhang Z, Song Y T, et al. Mechanical properties and in vitro biodegradation of newly developed porous Zn scaffolds for biomedical applications[J]. Mater Des, 2016, 108:136.
34Wang D P, Li Q J, Wang Z Q. Properties and application of medical porous tantalum in knee joint injury[J]. J Clin Rehabil Tissue Eng Res, 2011, 29(15):5463(in Chinese).
王大鹏, 李琪佳, 王志强. 医用多孔钽的性能及其在膝关节损伤中的应用[J]. 中国组织工程研究与临床康复, 2011, 29(15):5463.
35Yue X J, Zhang T, Yang D Y, et al. The synthesis of hierarchical porous Al₂O₃/acrylic resin composites as durable, effcient and recyclable absorbents for oil/water separation[J]. Chem Eng J, 2017, 309:522.
36Karen I, Yazici M, Shukla A. Designing foam filled sandwich panels for blast mitigation using a hybrid evolutionary optimization algorithm[J]. Compos Struct, 2016, 158:72.
37Li Z B, Chen X G, Jiang B H, et al. Local indentation of aluminum foam core sandwich beams at elevated temperatures[J]. Compos Struct, 2016, 145:142.
38刘培生. 沸石球复合金属多孔材料: 中国, CN 103131884A[P].2013-03-06.
39Cheng J, Zou Y J, Xiang C L, et al. Preparation of nanoporous Co-Ni-B/Cu-BTC composites and its application for catalyzing the hydrolysis of NH₃BH₃[J]. J Funct Mater, 2016, 47(6):06152(in Chinese).
程军, 邹勇进, 向翠丽,等. 纳米多孔Co-Ni-B/Cu-BTC复合材料的制备及其催化水解氨硼烷的研究[J]. 功能材料, 2016, 47(6):06152.
40Wang Q B, Tang H P, Yang B J. Research on the Continuously Graded Porous Metal Materials[J]. Mater China, 2016, 35(2):136(in Chinese).
汪强兵, 汤慧萍, 杨保军. 连续梯度金属多孔材料的研究[J]. 中国材料进展, 2016,35(2):136.
41Dong X H. Review of fabrication of graded porous metal matrix composites[J].Met World, 2017, 2:20.
董旭辉. 梯度多孔金属基复合材料的制备综述[J]. 金属世界, 2017, (2):20.
42Wu L, He Y H, Jiang Y, et al. Effect of pore structures on corrosion resistance of porous Ni₃Al intermetallics[J]. Trans Nonferr Met Soc, 2014, 24(11):3509.
43Tang H P, Wang J Z, Ao Q B, et al. Effect of pore structure on performance of porous metal fiber materials[J]. Rare Met Mater Eng, 2015, 44(8):1821.