AC-HVAF非晶和金属陶瓷涂层在压裂液中空蚀行为研究<sup>*</sup>

doi:10.11896/j.issn.1005-023X.2017.016.018

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (1456KB)
Export: BibTeX | EndNote (RIS)

Abstract The cavitation-erosion rules and synergistic mechanism of the AC-HVAF sprayed Fe-based amorphous metallic and WC-10Co-4Cr metallic cermet coatings in hydraulic fracturing fluid were studied by means of the ultrasonic cavitation and electrochemical testing methods. The leading role of the corrosion resistance and hardness during the cavitation was determined. The results showed that the existing of KCl in the fracturing fluid had a significant impact on the cavitation behavior of the coatings, especially for the lower corrosion resistance of metallic cermet coating. The cavitation performance of coatings in fracturing fluid was a double variable function of corrosion resistance and hardness. Mechanical damage of cavitation had a significant effect on cavitation erosion process of high hardness coating. The cavitation-erosion resistance of coatings was mainly dependent to hardness, and the high hardness of WC metallic cermet coating exhibited excellent cavitation-erosion resistance. The cavitation-erosion damage of coatings originated from the pores and defect areas, the hard phases striped off the surface and thus led to the damage of the hard metals and coa-tings. Reducing porosity and improving bonding strength were helpful to improve the corrosion resistance of coatings in fracturing fluid.

Key words： amorphous metallic coating cermet coating hydraulic fracturing fluid cavitation synergistic effect

Published: 25 August 2017 Online: 2018-05-07

CLC number:

TG174

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	SUN Lili
	WANG Zunce
	WANG Yong

Cite this article:

SUN Lili,WANG Zunce,WANG Yong. Cavitation Corrosion Mechanism of AC-HVAF Sprayed Amorphous Metallic Coatings and Cermet Coatings in the Hydraulic Fracturing Fluid[J]. Materials Reports, 2017, 31(16): 89-93.

URL:

https://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2017.016.018 OR https://www.mater-rep.com/EN/Y2017/V31/I16/89

1 Chen Z, Wang Z D, Zeng H G. Status quo and prospect of staged fracturing technique in horizontal wells [J]. Nat Gas Ind,2007,22(9):78(in Chinese).
陈作,王振铎,曾华国.水平井分段压裂工艺技术现状及展望[J].天然气工业,2007,22(9):78.
2 Zhang X Y. Study on erosion wear mechanism of tool materials and surface coatings in the condition of fracturing [D]. Daqing: Northeast Petroleum University,2013(in Chinese).
张旭昀.压裂工况下工具材料及表面涂层冲刷磨损机理研究[D].大庆:东北石油大学,2013.
3 Sun L L. Cavitation-abrasion behavior and damage mechanisms of typical materials in hydrajet fracturing [D]. Daqing: Northeast Petroleum University,2015(in Chinese).
孙丽丽.水力压裂工况下典型材质损伤行为及机理研究[D].大庆:东北石油大学,2015.
4 Jacek Ryl, Joanna Wysocka, Pawel Slepski, et al.Instantaneous impedance monitoring of synergistic effect between cavitation erosion and corrosion processes[J].Electrochim Acta,2016,203(10):388.
5 Farmer J C, et al. Corrosion resistance of thermally sprayed high-boron iron-based amorphous-metal coatings: Fe_49.7Cr_17.7Mn_1.9Mo_7.4W_1.6B_15.2C_3.8Si_2.4[J]. J Mater Res,2007,22:2297.
6 Wang Y, ZhengY G, Ke W, et al.Slurry erosion-corrosion beha-viour of high-velocity oxy-fuel (HVOF) sprayed Fe-based amorphous metallic coatings for marine pump in sand-containing NaCl solutions[J]. Corros Sci,2011,53:3177.
7 Wang Y, Xing Z Z, Luo Q, et al. Corrosion and erosion-corrosion behaviour of activated combustion high-velocity air fuel sprayed Fe-based amorphous coatings in chloride-containing solutions[J]. Corros Sci,2015,98(6):339.
8 Chen B Q, Yun C H, Zou H L,et al. An overview on the corrosion resistance of amorphous and nonocrystalline soft magnetic material [J]. Mater Rev,2006,20(12):113(in Chinese).
陈伯渠,云翠华,邹洪流,等.非晶及纳米晶软磁材料耐腐蚀性能的研究现状[J].材料导报,2006,20(12):113.
9 Liu C L, Lin Y Y, Wang Y Q,et al. Progress in coatings on the surface of metals for anti-cavitation corrosion [J]. Mater Rev:Rev,2011,25(1):127(in Chinese).
刘成龙,林英英,王玥霁,等.金属材料表面抗空蚀涂层的研究进展[J].材料导报:综述篇,2011,25(1):127.
10 Liu W, Zheng Y G, Yao Z M, et al. Research progress on cavitation erosion of metallic materials[J]. J Chin Soc Corros Protection,2001,21(4):250(in Chinese).
柳伟, 郑玉贵, 姚治铭, 等. 金属材料的空蚀研究进展[J]. 中国腐蚀与防护学报,2001,21(4):250.
11 Zheng Y G, Yao Z M, Wei X Y, et al. The synergistic effect between erosion and corrosion in acidic slurry medium[J]. Wear,1995,186-187:555.
12 Zhao K, Gu C Q, Shen F S, et al. Study on mechanism of combined action of abrasion and cavitation erosion on some engineering steels[J]. Wear,1993,162-164:811.
13 John R Blak, Giles S Keen, Robert P Tong. Acoustic cavitation: The fluid dynamics of non-spherical bubbles [J]. Philosophical Trans A,1999,357(2):251.
14 Zhao M, Wang S L, Jiang N. Effect of microstructure of TiN layer on wear resistance of CVD TiC-TiCN-TiN multilayer coating [J]. Mater Rev:Res,2016,30(5):51(in Chinese).
赵嫚,王少龙,江南.TiN层微观结构对CVD TiC-TiCN-TiN多层涂层耐磨性能的影响[J].材料导报:研究篇,2016,30(5):51.