稀土Ce对Fe-Ni-Al马氏体时效钢等温过程显微组织演变的影响

doi:10.11896/cldb.24010236

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (31950KB)
Export: BibTeX | EndNote (RIS)

Abstract The microstructure evolution and mechanical properties of maraging steel were systematically studied by OM, XRD, SEM and TEM, and compared with those of maraging steel with rare earth Ce. The results show that the hardness of two experimental steels increased firstly with the aging time, and then entered a wide hardness plateau. Compared with ordinary maraging steel, the mareging steel with rare earth Ce has finer lath martensite and more uniform martensite laths distribution, but its hardness decreases slightly. After aging at 500 ℃ for 3 h, the elongation of the experimental steel with rare earth Ce increases, and the strength change little, the tensile strength reaches 2 053 MPa. There are two types of precipitation with the aging to the experimental steel. One is NbC precipitated particles with larger size , the other is dispersed B2-NiAl phase with smaller size. After the addition of rare earth Ce, the size of NbC precipitation decreases, and the precipitation of NiAl phase is delayed. The lattice constants of the B2 phase and the matrix were obtained by HRTEM. The B2-NiAl is coherent with the matrix, and the mismatch between the two phases is 0.2%.

Key words： maraging steel rare earth Ce microstructure precipitation

Published: 10 April 2025 Online: 2025-04-10

CLC number:

TG142.1

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	TAN Huijie
	WANG Haiyan
	HUA Liangeng
	GAO Xueyun
	LYU Meng
	YU Dawei
	XING Lei

Cite this article:

TAN Huijie,WANG Haiyan,HUA Liangeng, et al. Effect of Rare Earth Ce on Microstructure Evolution of Fe-Ni-Al Maraging Steel During Isothermal Process[J]. Materials Reports, 2025, 39(7): 24010236-6.

URL:

https://www.mater-rep.com/EN/10.11896/cldb.24010236 OR https://www.mater-rep.com/EN/Y2025/V39/I7/24010236

1 Raabe D, Ponge D, Dmitrieva O. Scripta Materialia, 2009, 60 (12), 1141.
2 Kan L Y, Ye Q B, Tian Y, et al. Iron and Steel, 2021, 56(2), 105 (in Chinese).
阚立烨, 叶其斌, 田勇, 等. 钢铁, 2021, 56(2), 105.
3 Liu Q D, Song H, Zhang J, et al. Materials Characterization, 2021, 171, 110754.
4 Wang X Shen Q, Yan J J, et al. Acta Metallurgica Sinica, 2014, 50 (11), 1305 (in Chinese).
王晓姣, 沈琴, 严菊杰, 等. 金属学报, 2014, 50(11), 1305.
5 Lyu Z P, Jiang S H, He J Y, et al. Acta Metallurgica Sinica, 2016, 52 (10), 1183 (in Chinese).
吕昭平, 蒋虽合, 何骏阳, 等. 金属学报, 2016, 52 (10), 1183.
6 Shen Q. Co-precipitation mechanisms research of Cu-rich and NiAl phases in steel. Ph. D. Thesis, Shanghai University, China, 2018 (in Chinese).
沈琴. 钢中富Cu相和NiAl相复合析出机制的研究. 博士学位论文, 上海大学, 2018.
7 Jiang S H, Wang H, Wu Y, et al. Nature, 2017, 544 (2), 460.
8 Wang L M, Du T, Lu X L, et al. Chinese Rare Earths, 2001, 22 (4), 37 (in Chinese).
王龙妹, 杜挺, 卢先利, 等. 稀土, 2001, 22 (4), 37.
9 Fang M M. Study on mechanical properties and strengthening and toughening mechanism of 18Ni (350) maraging steel. Master's Thesis, Yangzhou University, China, 2014 (in Chinese).
方明敏. 18Ni(350)马氏体时效钢力学性能及强韧化机制的研究. 硕士学位论文, 扬州大学, 2014.
10 Jiang X, Song S H. Materials Science and Engineering:A, 2014, 613, 171.
11 Liu H H, Fu P X, Liu H W, et al. Metals , 2017, 7 (10), 436.
12 Gao X Y, Ren H P, Wang H Y, et al. Materials Science and Technology, 2017, 33 (11), 1366.
13 Gladman T. Materials Science and Technology, 1999, 15 (1), 30.
14 Gao X Y, Wang H Y, Li J, et al. Materials Science and Engineering:A, 2022, 846, 143306.
15 Jiang S H, Xu X Q, Li W, et al. Acta Materialia, 2021, 213, 116984.
16 Ryklina E P, Polyakova K A, Tabachkova N Y, et al. Journal of Alloys and Compounds, 2018, 764, 626.
17 Yeddu H K. Computational Materials Science, 2018, 154, 75.
18 Li Z, Wu R. Materials Reports, 2021, 34(Z2), 412 (in Chinese).
李钊, 吴润. 材料导报, 2021, 34 (Z2), 412.