加热模式对Cu-Al微电阻点焊过程中电极烧损行为的影响

doi:10.11896/cldb.23100261

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (84276KB)
Export: BibTeX | EndNote (RIS)

Abstract Full life cycle continuous welding and phased welding experiments were carried out on micro-resistance spot welding electrodes under unipolar and bipolar heating modes, respectively, in order to elucidate the effect of heating mode on the burning behavior of electrodes and the performance of welding joints in the Cu-Al wire bonding process of microelectronic packaging. The burning loss law of the electrodes under different heating modes during the continuous welding process was elaborated based on the electrical, thermal, and geometric physical properties of the electrodes during the experimental process, as well as the morphology and tensile shear force of the welded joints. It was studied how the performance of the welded joints under different heating modes was affected by electrode burning loss. Analyses were conducted on the electrode failure mechanisms under different heating conditions. The results demonstrate that the bipolar heating mode can effectively prolong increase the electrode service life and tensile share strength, surface quality, of welded joints. The electrode shows three distinct phases of continuous burning loss over the course of its life cycle under both heating modes: initial, stable, and severe burning loss. In comparison to unipolar heating mode, bipolar heating mode reduces the degree of electrode burning loss during each welding stage. The primary forms of electrode failure in both heating modes include fatigue cracks, surface peeling, droplet sputtering, recrystallization, grain development, and melting. The primary causes of electrode failure are high temperature oxidation, thermal stress cycling, and transient thermal shock.

Key words： micro-resistance spot welding electrode heating mode burning law failure mechanism joint performance

Published: 25 February 2025 Online: 2025-02-18

CLC number:

TG438.2

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	ZHANG Zhichun
	WANG Xiaoqing
	WU Minghai
	YANG Kai

Cite this article:

ZHANG Zhichun,WANG Xiaoqing,WU Minghai, et al. Effect of Heating Mode on Electrode Burning Behavior During Cu-Al Micro-resistance Spot Welding Process[J]. Materials Reports, 2025, 39(4): 23100261-9.

URL:

https://www.mater-rep.com/EN/10.11896/cldb.23100261 OR https://www.mater-rep.com/EN/Y2025/V39/I4/23100261

1 Cecil J, Kumar M, Lu Y, et al. International Journal of Advanced Manufacturing Technology, 2016, 83(9), 1569.
2 Li X, Wang M, Hua X M, et al. Welding & Joining, 2020 (7), 1 (in Chinese).
李旬, 王敏, 华学明, 等. 焊接, 2020(7), 1.
3 Kumar N, Ramakrishnan M S, Panchapakesan K, et al. International Journal of Advanced Manufacturing Technology, 2022, 121(9), 6581.
4 Guo Z G, Ma T J, Yang X W, et al. Materials Science and Engineering A-Structural Materials Properties Microstructure and Processing, 2023, 872, 144991.
5 Zeng J Q, Cao B, Yang K, et al. Journal of South China University of Technology: Natural Science Edition, 2019, 47(12), 32 (in Chinese).
曾家铨, 曹彪, 杨凯, 等. 华南理工大学学报(自然科学版), 2019, 47(12), 32.
6 Panza L, De-Maddis M, Spena P R. Journal of Manufacturing Processes, 2022, 76, 93.
7 Shuai G W, Fang P, Guo Z H, et al. Hot Working Technology, 2009, 38(13), 122 (in Chinese).
帅歌旺, 方平, 郭正华, 等. 热加工工艺, 2009, 38(13), 122.
8 Kim J W, Murugan S P, Kang N H, et al. Korean Journal of Metals and Materials, 2019, 57(11), 715.
9 Zheng L H, Zhang C Q, Zhang Q X, et al. Chian Mechanical Engineering, 2020, 31(21), 2632 (in Chinese).
郑立好, 张超群, 张庆鑫, 等. 中国机械工程, 2020, 31(21), 2632.
10 Xiao Y, Li Z, Qin F C, et al. Surface Technology, 2018, 47(1), 142 (in Chinese).
肖瑶, 李智, 覃富城, 等. 表面技术, 2018, 47(1), 142.
11 Li M F, Wang Y J, Yang S L, et, al. Journal of Manufacturing Processes, 2021, 64, 948.
12 Kawashiro F, Takao K, Kobayashi T, et, al. Microelectronics Reliability, 2019, 99, 168.
13 Wang X Q, Yang K, Li H D, et al. Transactions of the China Welding Institution, 2023, 44(1), 63 (in Chinese).
王晓庆, 杨凯, 李浩东, 等. 焊接学报, 2023, 44(1), 63.
14 Qi Y F, Wang B, Zhou J Y, et al. Rare Metal Materials and Engineering, 2018, 47(6), 1945 (in Chinese).
齐艳飞, 王波, 周景一, 等. 稀有金属材料与工程, 2018, 47(6), 1945.
15 Zhang X X, Yan Q Z. Journal of Nuclear Materials, 2014, 444(1), 428.
16 Kurishita H, Matsuo S, Arakawa H, et al. Journal of Nuclear Materials, 2009, 386, 579.
17 Chen L, Liu X, Lian Y Y. Nuclear Fusion and Plasma Physics, 2014, 34(1), 53 (in Chinese).
陈蕾, 刘翔, 练友运. 核聚变与等离子体物理, 2014, 34(1), 53.