Abstract The microstructures and mechanical properties of high-frequency induction welded joints of thin-walled H65 brass pipe were studied. The results show that high frequency induction welding technology used to weld H65 brass pipe can obtain well-formed welds on the surface and achieve high-quality welding. The fusion zone and heat affected zone of the welded joint are shaped like a waist drum, which with a narrow waist. The width of the welded joint and the fusion zone is about 173 μm and 15 μm, respectively. The microstructure of the fusion zone is composed of numerous small equiaxed grains and a small amount of strip grains. The grains in the fusion zone and heat affected zone are refined compared with the base metal. The tensile strength of the welded joint is 400 MPa, which is 97.6% of the tensile strength of the base metal. The increase of the strength of the welded joint is due to the dislocation deformation hindered by the refinement of grains and the interaction of dislocations promoted by the phase orientation difference between grains in the process of tensile deformation. The fracture of welded joint occurs in the heat affected zone due to the offset between work hardening during welding and anneal softening after welding, and the fracture mode of welded joint is mainly ductile fracture. The microhardness of the welded joint shows a ‘ʌ’ shape distribution. The average hardness values of the fusion zone, the heat affected zone and the base metal is 145HV, 137HV and 129HV, respectively. The hardness of the fusion zone is increased by 16% compared with that of the base metal. The increase of the strength of the fusion zone is caused by the work hardening generated during welding.

Key words： H65 brass high frequency welding microstructure mechanical property

Published: 25 July 2024 Online: 2024-08-12

CLC number:

TG456.9

Fund:National Natural Science Foundation of China (51771071),Hubei International Science and Technology Cooperation Project (2022EHB020), and Independent Innovation Projects of the Hubei Longzhong Laboratory(2022ZZ-17).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	CAI Yan
	ZHOU Lei
	YE Feng
	ZHANG Yanyu
	XIE Zhixiong
	DONG Shijie
	TAN Fenfang
	XIE Jianying

Cite this article:

CAI Yan,ZHOU Lei,YE Feng, et al. Microstructure and Mechanical Properties of Thin-walled H65 Brass Pipe Welded Joint by High Frequency Induction[J]. Materials Reports, 2024, 38(14): 23030122-6.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.23030122 OR http://www.mater-rep.com/EN/Y2024/V38/I14/23030122

1 Zhou S P, Liu H S. Journal of Plasticity Engineering, 2021, 28(12), 63 (in Chinese).
周树平, 刘红生. 塑性工程学报, 2021, 28(12), 63.
2 Heidarzadeh A, Saeid T. Rare Metals, 2018, 37, 388.
3 Wang W, Wang K S, Wu J L, et al. Ordnance Material Science and Engineering, 2008, 231(6), 12 (in Chinese).
王文, 王快社, 武佳蕾, 等. 兵器材料科学与工程, 2008, 231(6), 12.
4 Zhang L. Automatic TIG welding processes and microstructure & mechanical properties of copper tube joints. Master's Thesis, Shandong University, China, 2018 (in Chinese).
张亮. 典型铜管件自动TIG焊接工艺及接头组织性能分析. 硕士学位论文, 山东大学, 2018.
5 Qiu J F. Special Casting & Nonferrous Alloys, 2012, 32(10), 973 (in Chinese).
邱葭菲. 特色铸造及有色金属, 2012, 32(10), 973.
6 Zhao K L. The effect of induction heating process parameters of copper and brass inserts on microstructure and properties of brazed joints. Master's Thesis, China University of Petroleum (East China), China, 2019 (in Chinese).
赵凯磊. 紫铜与黄铜插套接头感应加热工艺参数对钎焊接头组织与性能的影响. 硕士学位论文, 中国石油大学(华东), 2019.
7 Zhang C, Qin Z, Rong C, et al. Materials, 2020, 13, 2401.
8 Moghaddam M S, Parvizi R, Haddad-Sabzevar M, et al. Materials & Design, 2011, 32, 2749.
9 Xiao S G, Xie Z X, Xu Z H, et al. Welding Technology, 2020, 49(12), 1 (in Chinese).
肖述广, 谢志雄, 许章华, 等. 焊接技术, 2020, 49(12), 1.
10 Kang C, Shi C, Liu Z, et al. Journal of Manufacturing Processes, 2020, 59, 772.
11 Egger C, Kroll M, Kern K, et al. Materials, 2022, 15, 3615.
12 Egger C, Marco.Lüchinger, Schreiner M, et al. Materials (Basel, Swit-zerland), 2022, 15,1270.
13 Zhang W D, Zhao G Q, Fu Q J. Materials Science & Engineering, A, 2018, 736, 276.
14 Chen Q, Xiao S G, Wang C, et al. Transactions of Materials and Heat Treatment, 2022, 43(6), 175 (in Chinese).
陈琪, 肖述广, 王超, 等. 材料热处理学报, 2022, 43(6), 175.
15 Xiao S G, Xie Z X, Chen Z, et al. Materials Reports, 2023, 37(1), 194 (in Chinese).
肖述广, 谢志雄, 陈卓, 等. 材料导报, 2023, 37(1), 194.
16 Hu S L. Welded Pipe and Tube, 2017, 40(6), 61 (in Chinese).
胡松林. 焊管, 2017, 40(6), 61.
17 Sabzi M, Kianpour-Barjoie A, Ghobeiti-Hasab M, et al. Archives of Me-tallurgy & Materials, 2018, 63, 1693.
18 Goto S, Nakata H, Toyoda S, et al. Metallurgical & Materials Transactions A, 2017, 48, 5075.
19 Zaffaroni G G B, Mishin O V, Ciucani U M, et al. Materials Characte-rization, 2021, 173, 110939.
20 Zhang H J, Cao C P, Shan Q Q, et al. Electric Welding Machine, 2021, 51(7), 37 (in Chinese).
张海军, 曹春鹏, 单清群, 等. 电焊机, 2021, 51(7), 37.
21 Sui X, Song B W, Li B, et al. The Chinese Journal of Nonferrous Metals, 2009, 19(6), 1049 (in Chinese).
隋贤, 宋宝韫, 李冰, 等. 中国有色金属学报, 2009, 19(6), 1049.
22 Wang X J, Da C B, Li J, et al. The Chinese Journal of Nonferrous Me-tals, 2006, 16(5), 775 (in Chinese).
王希靖, 达朝炳, 李晶, 等. 中国有色金属学报, 2006, 16(5), 775.
23 Zhang C Q, Qin Z, Rong C, et al. Journal of Mechanical Engineering, 2020, 56(12), 65 (in Chinese).
张昌青, 秦卓, 荣琛, 等. 机械工程学报, 2020, 56(12), 65.
24 Li Y, Zhang X K, He K J, et al. The Chinese Journal of Nonferrous Me-tals, 2016, 26(1), 66 (in Chinese).
李祎, 张祥凯, 何克坚, 等. 中国有色金属学报, 2016, 26(1), 66.
25 Guo X N, Huang H Q, Gong D Y, et al. Transactions of Matterials and Heat Treatment, 2017, 38(10), 23 (in Chinese).
郭晓妮, 黄慧强, 龚殿尧, 等. 材料热处理学报, 2017, 38(10), 23.
26 Wu X W. Influence of alloying on microstructure and properties of H62 brass. Master's Thesis, University of Jinan, China, 2017 (in Chinese).
武祥为. 合金化对H62黄铜组织和性能影响. 硕士学位论文, 济南大学, 2017.