剥离涂层下含缺陷管道腐蚀规律的瞬态数值模拟研究

doi:10.11896/cldb.23010094

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (15902KB)
Export: BibTeX | EndNote (RIS)

Abstract To study the crevice corrosion of metal pipes with defects under disbonded coatings, a two-dimensional mathematical model was established, which fully considered the effects of mass transfer process of solution in the crevice, potential gradient change and the principle of electric neutrality. The influence of cathodic protection on the corrosion behavior of metal pipelines containing defects was studied by numerical simulation, and the evolution of dissolved oxygen concentration, ion concentration and conductivity of solution in defects with time under transient conditions were analyzed. The numerical simulation results show that the cathodic protection potential could not completely protect the defects in the crevice before 35 h, the potential difference at the defects gradually decreased with the increase of the distance from the crevice;in the defect area, due to the influence of electromigration mass transfer and solution concentration gradient on the diffusion of ions, cations move towards the defect interior and anions towards the defect exterior;the reduction reaction causes the conductivity of the solution to increase with time, but to decrease with the increase of the crevice depth. The conductivity at the bottom of the defect is slightly higher than that at the defect mouth.

Key words： crevice corrosion cathodic protection defect transient numerical simulation

Published: 10 March 2025 Online: 2025-03-18

CLC number:

TE832

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	LI Lei
	SUN Dongxu
	CHAI Yuying
	XIE Fei
	WU Ming

Cite this article:

LI Lei,SUN Dongxu,CHAI Yuying, et al. Transient Numerical Simulation Study on Corrosion Law of Defective Pipelines Under Disbonded Coating[J]. Materials Reports, 2025, 39(5): 23010094-9.

URL:

https://www.mater-rep.com/EN/10.11896/cldb.23010094 OR https://www.mater-rep.com/EN/Y2025/V39/I5/23010094

1 Kuang D, Cheng Y F. Corrosion Science, 2015, 99, 249.
2 Allahar K N, Orazem M E. Corrosion Science, 2009, 51(5), 962.
3 Adewale G A, Joshua O I. Recent Innovations in Chemical Engineering, 2020, 13, 379.
4 Wang Z, Huang Y, Wang X, et al. Corrosion Science, 2022, 207, 110580.
5 Duan T, Peng W, Ding K, et al. Journal of Materials Research and Technology, 2022, 20, 4597.
6 Wu C, Wang Z, Zhang Z, et al. Corrosion Communications, 2021, 4, 33.
7 Zhong C, Tang X, Cheng Y F. Electrochimica Acta, 2008, 53, 4740.
8 Wei B X, Xu J, Gao L Q, et al. Surface Technology, 2021, 50(3), 30 (in Chinese).
韦博鑫, 许进, 高立群, 等. 表面技术, 2021, 50(3), 30.
9 Yan M C, Wang J Q, Han E H, et al. Acta Metallurgica Sinica, 2014(9), 1137 (in Chinese).
闫茂成, 王俭秋, 韩恩厚, 等. 金属学报, 2014(9), 1137.
10 Su W, Liu Z. Materials, 2022, 15, 2329.
11 Ding J, He W, Liu Y, et al. Coatings, 2022, 12, 592.
12 Kennell G F, Evitts R W, Heppner K L. Corrosion Science, 2008, 50, 1716.
13 Xiao Z H, Hu S Y, Luo J L, et al. Computational Materials Science, 2018, 149, 37.
14 Chen X, Li X, Du C, et al. Corrosion Science, 2009, 51(9), 2242.
15 Saleem B, Ahmed F, Rafiq M A, et al. Engineering Failure Analysis, 2014, 46, 157.
16 Bueno A, Moreira E D, Gomes J. Engineering Failure Analysis, 2014, 36, 423.
17 Wang C. International Journal of Electrochemical Science, 2020, 15, 4988.
18 Newman J S, Thomas-Alyea K E. Electrochemical systems, 3rd edition, John Wiley & Sons, Inc. , Hoboken, New Jersey, 2004, pp.271.
19 Kennell G F, Evitts R W. Electrochimica Acta, 2009, 54, 4696.
20 Song F M. Corrosion Science, 2012, 57, 279.
21 Cui, C, Chen A R, Pan Z C, et al. Construction and Building Materials, 2019, 206, 683.
22 Xu F, Qiu Y P. Materials and Design, 2016, 89, 1048.
23 Li Y, Mu J, Cui Z, et al. Materials and Corrosion, 2021, 73, 281.
24 Chin D T, Sabde G M. Corrosion-Houston Tx, 2006, 56(8), 783.