改性磷石膏对超硫酸盐水泥水化特性的影响

doi:10.11896/cldb.22120115

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (8883KB)
Export: BibTeX | EndNote (RIS)

Abstract The influence of modified phosphogypsumson early hydration heat, compressive strength, pH of the pore, hydration products and microstructure characteristics of supersulfated cement (SSC) were studied. SSC system had lower early hydration rate, lower hydration heat, longer induction period, and delayed second exothermic peak, which showed lower early hydration characteristics comparing with common Portland cement (CPC). Modification methods of phosphogypsum could regulate the early hydration rate and the hydration activity of the system. The main hydration products of SSC were AFt and C-S-H gels, the pH value was stable at 11, and its strength was depended on the characteristic of phosphogypsum. Calcination could improve the strength at the middle and late ages, while lime neutralization could improve the strength through the whole age. After treatment, the activity of phosphogypsum increased, resulting in more AFt and C-S-H gels, which made the structure dense and strength increasing.

Key words： phosphogypsum modification method supersulfated cement early hydration microstructure

Published: 25 July 2024 Online: 2024-08-12

CLC number:

TQ172.78

Fund:National Natural Science Foundation of China (52278273), Application Foundation Frontier Project of Wuhan City (2020010601012200), CRSRI Open Research Program (CKWV20221026/KY).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	WANG Lu
	TU Yongjun
	GAO Fuhao
	LIU Shuhua

Cite this article:

WANG Lu,TU Yongjun,GAO Fuhao, et al. Effect of Modified Phosphogypsum on Hydration Characteristics of Supersulfated Cement[J]. Materials Reports, 2024, 38(14): 22120115-6.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.22120115 OR http://www.mater-rep.com/EN/Y2024/V38/I14/22120115

1 Wu M, Xie S H, Ge G W. Bulletin of the Chinese Ceramic Society, 2021, 40(8), 2640 (in Chinese).
吴旻, 谢胜华, 葛根旺. 硅酸盐通报, 2021, 40(8), 2640.
2 Li Z, Zhao X, He T, et al. Construction and Building Materials, 2017, 155, 126.
3 Liu Z F. China Cement, 2020(5), 50 (in Chinese).
刘志甫. 中国水泥, 2020(5), 50.
4 Bai Y, Collier N C, Milestone N B, Yang C H. Journal of Nuclear Mate-rials, 2011, 413(3), 183.
5 Fang P P, Liu S H. Bulletin of the Chinese Ceramic Society, 2019, 38(8), 2430 (in Chinese).
方佩佩, 刘数华. 硅酸盐通报, 2019, 38(8), 2430.
6 Yang M, Qian J S, Wang Z, et al. Materials Reports, 2007(6), 104 (in Chinese).
杨敏, 钱觉时, 王智, 等. 材料导报, 2007(6), 104.
7 Liu L Z. Effect of the quality of phosphogypsum on phosphogypsu compo-site binder. Master's Thesis, Southweat University of Science and Techno-logy, China, 2015 (in Chinese).
刘路珍. 磷石膏品质对磷石膏复合胶凝材料影响的研究. 硕士学位论文, 西南科技大学, 2015.
8 Andrade Neto J S, Bersch J D, Silva T S M, et al. Construction and Building Materials, 2021, 299, 123935.
9 Sun Z, Nie S, Zhou J, et al. Journal of Cleaner Production, 2022, 333, 130094.
10 Rubert S, Angulski Da Luz C, F. Varela M V, et al. Journal of Thermal Analysis and Calorimetry, 2018, 134, 971.
11 Cabrera-Luna K, Maldonado-Bandala E E, Nieves-Mendoza D, et al. Cement and Concrete Composites, 2021, 124, 104236.
12 Liu S, Ouyang J, Ren J. Construction and Building Materials, 2020, 243, 118226.
13 Liu S, Fang P, Ren J, et al. Journal of Cleaner Production, 2020, 272, 122660.
14 Han F H. Study on hydration characteristics and kinetics of composite binder. Ph.D. Thesis, China University of Mining & Technology, China, 2015 (in Chinese).
韩方晖. 复合胶凝材料水化特性及动力学研究. 博士学位论文, 中国矿业大学, 2015.
15 Ouyang J Y, Liu S H. China Concrete, 2019(9), 60 (in Chinese).
欧阳嘉艺, 刘数华. 混凝土世界, 2019(9), 60.
16 Liu S, Wang L, Yu B. Construction and Building Materials, 2019,214, 9.
17 Hou G H, Zhong B Q, Yang N R. Journal of the Chinese Ceramic Society, 2002(6), 675 (in Chinese).
侯贵华, 钟白茜, 杨南如. 硅酸盐学报, 2002(6), 675.
18 Reardon E J. Cement and Concrete Research, 1990, 20, 175.
19 Liu Z H, Shao W, Lan X H, et al. Journal of Building Materials, 2011, 14(2), 169 (in Chinese).
刘志辉, 邵伟, 兰祥辉, 等. 建筑材料学报, 2011,14(2), 169.
20 Myers R J, L'Hôpital E, Provis J L, et al. Cement and Concrete Research, 2015, 68, 83.