| INORGANIC MATERIALS AND CERAMIC MATRIX COMPOSITES |
|
|
|
|
|
| Performance and Hydration of One-part Geopolymer Activated with NaAlO2 |
| TANG Ning1, WANG Yanjun1, ZHAO Mingyu1, SUN Yihan2, WANG Qing1,*
|
1 School of Materials Science and Engineering, Shenyang Jianzhu University, Shenyang 110168, China
2 Zhejiang Scientific Research Institute of Transport, Hangzhou 310023, China |
|
|
|
|
Abstract Geopolymer is a new type of cementitious material. Compared with ordinary Portland cement, it has many technical advantages such as green environmental protection, energy saving and low carbon, and excellent performance. At present, geopolymeris manufactured with two-parts materials including alumina-silicate materials and aqueous alkali, which leads to harsh transportation conditions, and difficult to control construction in site. Therefore, it is difficult to apply in civil engineering on a large scale. In view of this, the present work aims to study the performance regulation and hydration mechanism of NaAlO2 on one-part geopolymer. In the raw materials of geopolymer, the alkali solution was changed to a solid alkali activator, and NaAlO2 with 2% of raw material powder was employed to improve its workability. The results reveal that NaAlO2 has a fast hydrolysis rate, and it is easy to generate an Al-rich reaction environment in the early stage of the reaction, and quickly form hydrated calcium aluminosilicate, so that the one-part geopolymer can prolong the setting time without changing the compressive strength, and the microstructure also tends to gel and densify. Hence, the adding of a small amount of NaAlO2 is conducive to breaking through the technical bottleneck of the current application of two-parts geopolymer and promoting the large-scale application of geopolymer in engineering.
|
|
Published: 25 April 2024
Online: 2024-04-28
|
|
|
| Fund:National Natural Science Foundation of China (52278453, 52278266), Natural Science Foundation of Liaoning (2021-MS-245), and Liaoning Revitalization Talents Program (XLYC2007176). |
|
|
1 Li D,Zheng W,Liu Y W.Chinese Cement,2022(5),82(in Chinese).
李丹,郑伟,刘彦伟.中国水泥,2022(5),82.
2 Davidovits J.Journal of Thermal Analysis,1991,37(8),1633.
3 Davidovits J.Journal of Thermal Analysis,1989,35(2),429.
4 Hajimohammadi A,Provis J L,Van Deventer J S J.Industrial & Enginee-ring Chemistry Research,2008,47(23),9396.
5 Ma C,Zhao B,Guo S,et al.Journal of Cleaner Production,2019,220,188.
6 Hajimohammadi A,van Deventer J S J.Waste and Biomass Valorization,2017,8(1),225.
7 Ma C,Long G,Shi Y,et al.Journal of Cleaner Production,2018,201,636.
8 Dong M,Elchalakani M,Karrech A.Construction and Building Materials,2020,236,117611.
9 Zhang H Y,Liu J C,Wu B.Construction and Building Materials,2021,273,121973.
10 Nematollahi B,Sanjayan J,Shaikh F U A.Ceramics International,2015,41(4),5696.
11 Wang Y S,Alrefaei Y,Dai J G.Construction and Building Materials,2021,306,124880.
12 Ooi W N,Liew Y M,Heah C Y,et al.Journal of Materials Research and Technology,2021,15,3850.
13 Li H C,Fu B.Handbook of practical chemistry,Chemical Industry Press,China,2007,pp.267(in Chinese).
李华昌,符斌.实用化学手册,化学工业出版社,2007,pp.267.
14 Wang Q,Kang S R,Wu L M,et al.Journal of Building Materials,2020,23(1),184(in Chinese).
王晴,康升荣,吴丽梅,等.建筑材料学报,2020,23(1),184.
15 Wang Q,Kang S R,Wu L M,et al.Materials Reports,2020,34(4),4056(in Chinese).
王晴,康升荣,吴丽梅,等.材料导报,2020,34(4),4056. |
|
|
|
渝公网安备50019002502923号 © Editorial Office of Materials Reports.
2024, Vol. 38 