高性能内燃机用滤纸的制备及其对性能的影响

doi:10.11896/cldb.22050334

Abstract
Figure/Table
References
Related Citation (7)

Download:

Full Text ( PDF ) (6780KB)
Export: BibTeX | EndNote (RIS)

Abstract In order to prepare filter paper with high mechanical properties, good hydrophobicity and proper air permeability for internal combustion engine, the mixture of high strength and high modulus polyethylene (UHMWPE) fiber and softwood pulp was used. The effects of base paper preparation, resin impregnation and hot pressing on the properties of filter paper were discussed, the mechanical properties, thermal stability, pore size and hydrophobicity of the filter paper were characterized. The results showed that when the mass ratio of UHMWPE fiber to softwood pulp was 8∶2 and the beating degree of softwood pulp was 22 °SR, the mass fraction of dispersant PEO and reinforcing agent CPAM were 0.5% and 0.1%, respectively, and the hot pressing temperature was 140 ℃, the hot pressing time was 15 min, and the hot pressing pressure was 10 MPa, the filter paper made by UHMWPE for internal combustion engine has the best performance, in which the tensile index of the filter paper was 50.28 N·m/g, the bursting strength was 503.55 kPa, the contact angle was 123.52° and the filter paper was impervious within 1 min, and the melting point was raised to 155 ℃.

Key words： UHMWPE fiber phenol formaldehyde resin hot pressing burst strength filter paper

Published: 25 March 2024 Online: 2024-04-07

CLC number:

TS77

Corresponding Authors: ^*longzhu@jiangnan.edu.cn

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	MA Rui
	JIN Shengnan
	LONG Zhu
	ZHU Ruifeng
	SUN Chang

Cite this article:

MA Rui,JIN Shengnan,LONG Zhu, et al. Preparation of Filter Paper for High Performance Internal Combustion Engine and Its Influence on Performance[J]. Materials Reports, 2024, 38(6): 22050334-6.

URL:

https://www.mater-rep.com/EN/10.11896/cldb.22050334 OR https://www.mater-rep.com/EN/Y2024/V38/I6/22050334

1 Jiang B Y, Zhao Y, Ding M T, et al. Papermaking Equipment & Mate-rials, 2021, 50(1), 3(in Chinese).
蒋宝永, 赵云, 丁明太, 等. 造纸装备及材料, 2021, 50(1), 3.
2 杭州特种纸业有限公司. 中国专利, CN201710439552.6, 2017.
3 Sun S Y. Factors affecting the production and quality of filter paper in the automotiveind-ustry. Master's Thesis, Zhejiang Sci-Tech University, China, 2019(in Chinese).
孙诗尧. 影响汽车工业滤纸生产及质量的因素. 硕士学位论文, 浙江理工大学, 2019.
4 Zhang B Y, Li Z F, Cui Z H, et al. China Pulp & Paper Industry, 2019, 40(24), 17(in Chinese).
张宝印, 李枝芳, 崔中华, 等. 中华纸业, 2019, 40(24), 17.
5 Yao C D, Bai W F, Tang M, et al. Paper Science & Technology, 2015, 34(4), 20(in Chinese).
要长东, 白伟锋, 唐敏, 等. 造纸科学与技术, 2015, 34(4), 20.
6 Sun Z, Hui L F, Zhao G D, et al. Tianjin Paper Making, 2021, 43(1), 39(in Chinese).
孙哲, 惠岚峰, 赵国栋, 等. 天津造纸, 2021, 43(1), 39.
7 Zhao D J. Textile Science Research, 2017(5), 70(in Chinese).
赵东瑾. 纺织科学研究, 2017(5), 70.
8 Han L, Cai H, Chen X, et al. Polymers, 2020, 12(3), 521.
9 Chhwtri S, Bougherara H. Composites: Part A, Applied Science & Manufacturing, 2021, 140, 106146.
10 Wang G J, Guo Y J, Xu M X. Journal of Functional Materials, 2009, 40(1), 130(in Chinese).
王广健, 郭亚杰, 徐明霞. 功能材料, 2009, 40(1), 130.
11 Zhang M Y, Dong H B, Wang J. China Pulp & Paper, 2011, 30(1), 1(in Chinese).
张美云, 董和滨, 王建. 中国造纸, 2011, 30(1), 1.
12 Li H B, Fang G G, Han S M, et al. Journal of Functional Materials, 2020, 51(1), 1165(in Chinese).
李红斌, 房桂干, 韩善明, 等. 功能材料, 2020, 51(1), 1165.
13 Lu Z Q, Chen J, Zhang D K. China Pulp & Paper, 2013(2), 22(in Chinese).
陆赵情, 陈杰, 张大坤. 中国造纸, 2013(2), 22.
14 Liu Y B, Li X R, Shen Y D, et al. China Pulp & Paper, 2021, 40(9), 29(in Chinese).
刘勇兵, 李小瑞, 沈一丁, 等. 中国造纸, 2021, 40(9), 29.
15 Long A Y, Zhao C S, Jiang Y F, et al. China Pulp & Paper, 2015, 34(6), 28(in Chinese).
龙爱云, 赵传山, 姜亦飞, 等. 中国造纸, 2015, 34(6), 28.
16 Zherebtsov D, Chukov D, Torokhov D, et al. Journal of Materials Engineering and Performance, 2020, 29(3), 1522.
17 Xie M Q, Wang L G, Luo Y Q, et al. Materials Science and Engineering of Powder Metallurgy, 2021, 26(2), 182(in Chinese).
谢茂青, 王雷刚, 罗怡沁, 等. 粉末冶金材料科学与工程, 2021, 26(2), 182.
18 Ren W H, Zhang D, Wang G, et al. Journal of Northeast Forestry University, 2014(8), 90(in Chinese).
任文涵, 张丹, 王戈, 等. 东北林业大学学报, 2014(8), 90.
19 Li C S, Liu Z, Hui L F, et al. China Pulp & Paper, 2021, 40(12), 9(in Chinese).
李昌胜, 刘忠, 惠岚峰, 等. 中国造纸, 2021, 40(12), 9.
20 Wang C H. Study on preparation and properties of high strength and high modulus polyethylene fiber paper. Master's Thesis, Jiangnan University, China, 2017(in Chinese).
王长红. 高强高模聚乙烯纤维纸的制备及性能研究. 硕士学位论文, 江南大学, 2017.