电弧脉冲对6005A-T6铝合金CMT-P焊接接头组织和性能的影响
朱轩,杨晓益*, 陆鑫*, 杨书汉
昆明理工大学材料科学与工程学院,昆明 650093
Effect of Arc Pulse on Microstructure and Properties of 6005A-T6 Aluminum Alloy CMT-P Welded Joint
ZHU Xuan, YANG Xiaoyi*, LU Xin*, YANG Shuhan
Faculty of Materials Science and Engineering, Kunming University of Science and Technology, Kunming 650093, China
下载:  全 文 ( PDF ) ( 46584KB ) 
输出:  BibTeX | EndNote (RIS)      
摘要 6005A-T6铝合金已被广泛应用于焊接制造,良好的焊接质量是其工业应用的关键。本工作研究了不同电弧脉冲个数下冷金属过渡-脉冲(CMT-P)焊接工艺对6005A-T6铝合金焊接接头宏观形貌、微观组织和力学性能的影响。结果表明,冷金属过渡(CMT)和CMT-P焊接接头力学性能接近,接头硬度分布基本相同。在CMT-P中,随着脉冲个数的增加,焊缝宽度增加,焊缝中心晶粒尺寸增大。当脉冲个数为6时,CMT-P焊接接头的气孔率接近于0%,极限抗拉强度为158 MPa,达到了母材的61.2%,接头延伸率为6.74%。接头拉伸断裂位置均在热影响区,断裂形式为韧性断裂。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
朱轩
杨晓益
陆鑫
杨书汉
关键词:  CMT-P  电弧脉冲  焊缝成形  微观组织  力学性能    
Abstract: 6005A-T6 aluminum alloy has been widely used in welding manufacturing for it's good welding quality. In this work, the effects of cold metal transfer plus pulse (CMT-P) welding process on the macroscopic morphology, microstructure, and mechanical properties of 6005A-T6 aluminum alloy welded joints under different arc pulse numbers were studied. The results show that the mechanical properties of cold metal transfer (CMT) welded joints are close to that of CMT-P, and the hardness distribution of the two kind of joints are almost the same. By CMT-P, as the number of pulses increases, the weld width increases and the grain size in the weld center increases. When the number of pulses is 6, the poro-sity of the CMT-P welded joint is close to 0%, the ultimate tensile strength is 158 MPa, which is 61.2% of the base metal, and the elongation of the joint is 6.74%. The tensile fracture positions of the joints are all in the heat affected zone, and the fracture form is ductile fracture.
Key words:  CMT-P    arc pulse    appearance of welding zone    microstructure    mechanical property
出版日期:  2024-12-10      发布日期:  2024-12-10
ZTFLH:  TG444+.7  
基金资助: 云南省重点研发计划(202103AA080017;202203AE140011);云南省基础研究专项(202201AU070081)
通讯作者:  * 杨晓益,2020年毕业于西南交通大学,获工学博士学位。现为昆明理工大学材料科学与工程学院副教授、硕士研究生导师。主要开展先进电弧与激光焊接、高性能电弧增材制造等方向的研究工作,已发表SCI/EI等科研论文20余篇,获授权国家专利7项。yangxiaoyi@kust.edu.cn
陆鑫,2019年毕业于燕山大学,获工学博士学位。现为昆明理工大学材料科学与工程学院讲师、硕士研究生导师。主要基于激光、电弧及塑性变形加工原理,运用集成计算材料工程(ICME)理念,围绕金属增材制造(3D打印)及表面强化工艺,开展铝合金、钛合金、镍基合金、钢铁等材料的微观组织与性能调控研究。已发表SCI/EI等科研论文20余篇,授权多项国家发明专利及软件著作权。trekin@kust.edu.cn   
作者简介:  朱轩,2022年6月于昆明理工大学获得工学学士学位。昆明理工大学材料科学与工程学院2022级硕士研究生,导师为杨晓益老师。主要研究领域为铝合金焊接、增材制造。在读期间,申请授权一项发明专利。
引用本文:    
朱轩,杨晓益, 陆鑫, 杨书汉. 电弧脉冲对6005A-T6铝合金CMT-P焊接接头组织和性能的影响[J]. 材料导报, 2024, 38(23): 23090035-7.
ZHU Xuan, YANG Xiaoyi, LU Xin, YANG Shuhan. Effect of Arc Pulse on Microstructure and Properties of 6005A-T6 Aluminum Alloy CMT-P Welded Joint. Materials Reports, 2024, 38(23): 23090035-7.
链接本文:  
http://www.mater-rep.com/CN/10.11896/cldb.23090035  或          http://www.mater-rep.com/CN/Y2024/V38/I23/23090035
1 Liu J X, Shen J, Li X W, et al. Materials Reports, 2021, 35(2), 2092 (in Chinese).
刘敬萱, 沈健, 李锡武, 等. 材料导报, 2021, 35(2), 2092.
2 Li S Z, Han X H, Wu L J, et al. Materials Reports, 2022, 36(17), 157 (in Chinese).
李帅贞, 韩晓辉, 吴来军, 等. 材料导报, 2022, 36(17), 157.
3 Peng Z, Yang S, Wang Z, et al. Materials, 2022, 15(13), 4698.
4 Pang J, Hu S, Shen J, et al. Journal of Materials Processing Technology, 2016, 238, 212.
5 Huang H C, Xu L Y, Jin H Y, et al. Transactions of the China Welding Institution, 2019, 40(10), 127 (in Chinese).
黄瀚川, 徐连勇, 荆洪阳, 等. 焊接学报, 2019, 40(10), 127.
6 Huang P C, Wei X, Wang X N, et al. Materials Letters, 2021, 301, 130311.
7 Liu Y, Liu Z, Chen Y, et al. Materials, 2022, 15(17), 5880.
8 Chinnasamy R, Chelladurai S J S, Sonar T. Advances in Materials Science and Engineering, DOI: 10.1155/2021/8163164.
9 Li J, Shen J, Hu S, et al. Journal of Materials Processing Technology, 2019, 264, 134.
10 Liu Z Q, Zhang P L, Li S W, et al. Metallurgy and Materials, 2020, 27, 783.
11 Wang D, Lu J, Tang S, et al. Materials, 2018, 11(8), 1344.
12 Zhou S, Xie H, Ni J, et al. Journal of Manufacturing Processes, 2022, 82, 159.
13 Huang P C, Wang X N, Zhang Q Y, et al. Journal of Materials Research and Technology, 2022, 17, 159.
14 Wang Y C, Li M N, Yang X Y, et al. Materials Science and Technology, DOI: 10.1080/02670836.2023.2191091
15 Frostevarg J, Kaplan A F H, Lamas J. Welding in the World, 2014, 58(5), 649.
16 Xiong S, Tang X, Wang C X, et al. Materials Reports, 2019, 33(16), 2720 (in Chinese).
熊斯, 唐鑫, 王春霞, 等. 材料导报, 2019, 33(16), 2720.
17 Schempp P, Rethmeier M. Welding in the World, 2015, 59, 767.
18 Gao S K, Zhou L, Zhang X M, et al. Transactions of the China Welding Institution, 2022, 43(6), 35 (in Chinese).
高士康, 周利, 张欣盟, 等. 焊接学报, 2022, 43(6), 35.
[1] 王子健, 孙舒蕾, 肖寒, 冉旭东, 陈强, 黄树海, 赵耀邦, 周利, 黄永宪. 搅拌摩擦固相沉积增材制造研究现状[J]. 材料导报, 2024, 38(9): 22100039-16.
[2] 白云官, 吉小超, 李海庆, 魏敏, 于鹤龙, 张伟. 原位合成的钛合金@CNTs粉体SPS制备TiC/Ti复合材料的微结构与性能[J]. 材料导报, 2024, 38(9): 22120175-7.
[3] 邝亚飞, 李永斌, 张艳, 陈峰华, 孙志刚, 胡季帆. SPS烧结Ni-Mn-In合金的马氏体相变和力学性能研究[J]. 材料导报, 2024, 38(9): 23110107-6.
[4] 王艳, 高腾翔, 张少辉, 李文俊, 牛荻涛. 不同形态回收碳纤维水泥基材料的力学与导电性能[J]. 材料导报, 2024, 38(9): 23010043-9.
[5] 常川川, 李菊, 李晓红, 金俊龙, 张传臣, 季亚娟. 热处理对同质异态TC17钛合金线性摩擦焊接头的影响[J]. 材料导报, 2024, 38(8): 22080152-5.
[6] 左志东, 刘先斌, 刘吉波, 汪小锋, 陈剑斌. 汽车用2024-T351铝合金的动态力学行为各向异性[J]. 材料导报, 2024, 38(8): 22080196-9.
[7] 郑思铭, 李蔚, 杨函瑞, 陈松, 魏取福. 3D打印聚乳酸的改性研究与应用进展[J]. 材料导报, 2024, 38(8): 22100107-10.
[8] 郑琨鹏, 葛好升, 李正川, 刘贵应, 田光文, 王万值, 徐国华, 孙振平. 河砂与石英砂对蒸养超高性能混凝土(UHPC)性能的影响及机理[J]. 材料导报, 2024, 38(7): 22040216-6.
[9] 吕晶, 赵欢, 张金翼, 席培峰. 冻融循环作用下不同含水率灰土的细微观结构与宏观力学性能[J]. 材料导报, 2024, 38(7): 22110321-7.
[10] 刘斌, 索超, 李忠华, 蒯泽宙, 陈彦磊, 唐秀. 选区激光熔化成形铜合金研究进展[J]. 材料导报, 2024, 38(7): 22080129-11.
[11] 孙华键, 郭德林, 李如庆, 侯良朋, 杨明辉, 孙金钊, 殷凤仕. 改性MCrAlY涂层的研究进展[J]. 材料导报, 2024, 38(7): 22120155-10.
[12] 凌子涵, 王利卿, 张震, 赵占勇, 白培康. 镁合金电弧增材技术基本工艺及工艺因素影响综述[J]. 材料导报, 2024, 38(7): 22090013-9.
[13] 张明玉, 运新兵, 伏洪旺. BASCA热处理对TC10钛合金组织与断裂韧性的影响[J]. 材料导报, 2024, 38(7): 22080020-6.
[14] 杨佳琛, 江海涛, 田世伟, 陈飞达. 基于电子结构理论的微合金Q355B热轧钢力学性能预测[J]. 材料导报, 2024, 38(7): 22090319-5.
[15] 田浩正, 乔宏霞, 冯琼, 韩文文. 石粉替代率对聚合物机制砂粘结砂浆性能及微细观结构的影响[J]. 材料导报, 2024, 38(6): 22050194-7.
No Suggested Reading articles found!
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed