温度对含模拟α-高放核废液的磷酸镁水泥固化体性能的影响

doi:10.11896/j.issn.1005-023X.2017.024.017

Abstract
Figure/Table
References
Related Citation (6)

Download:

Full Text ( PDF ) (680KB)
Export: BibTeX | EndNote (RIS)

Abstract The magnesium potassium phosphate cement (MPC) were used for immobilization of liquid acidic α-high-level radioactive waste (HLW). This work focused on the impact of heat-treatment temperature on mechanical property, phase, microstructure and Cs⁺ leaching rate of the solidified MPC. BET, XRD, SEM and AAS results showed that the ambient temperature reaction of MgO, KH₂PO₄ and HLW could form a dense structure, several kinds of phosphate was interspersed in the structure. The solidified MPC dehydrated with the increase of heat-treatment temperature, and obtained more pore structure, large average pore size, lower compressive strength and high Cs⁺leaching rate after sintering at 400℃. As the temperature continued to rise, the solidified MPC was sintered and formed ceramic while the average pore diameter decreased and the compressive strength increased. The solidified MPC turned into ceramic structure after sintering at 900 ℃. Crystal grains melt down completely. The 28 d leaching rate of Cs⁺ in the solidified MPC was 7.21×10^-6 g/(cm²·d). The leaching rate of Cs⁺ could reach the performance requirements of the vitrification form agent of the MPC solidified liquid with HLW at different heat-treatment temperatures, which showed obvious advantages of MPC in solidifying the HLW.

Key words： high-level radioactive waste immobilization MPC

Published: 08 May 2018

CLC number:

TU526

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	FU Mingjiao
	YANG Hailin
	WU Chuanming
	ZHANG Ying
	YOU Chao
	QIAN Jueshi

Cite this article:

FU Mingjiao,YANG Hailin,WU Chuanming, et al. Effects of Temperature on the Properties of α-High-level Radioactive Waste Immobilized, Hardened Magnesium Phosphate Cement[J]. Materials Reports, 2017, 31(24): 86-90.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2017.024.017 OR http://www.mater-rep.com/EN/Y2017/V31/I24/86

1 Wen Juan. The ion irradiation effects on δ-phase and nanocrystalline pyrochlore[D]. Lanzhou: Lanzhou University, 2016(in Chinese).
温娟. δ相及纳米烧绿石氧化物的离子束辐照效应研究[D]. 兰州:兰州大学, 2016.
2 Lv Yanjie. Study on monazite phosphate glass-ceramics as wasteform for simulated α-HLLW[D]. Wuhan: China University of Geoscie-nces, 2008(in Chinese).
吕彦杰. 模拟α-高放废液独居石磷酸盐玻璃陶瓷固化体的研究[D]. 武汉: 中国地质大学, 2008.
3 Zhang Ruizhu, Zhao Junhua, et al. Synthesis of SrTiO₃ by double-SHS for immobilization of high level radioactive waste[J]. Chin J Raremet, 2009,33(1):66(in Chinese).
张瑞珠, 赵军华, 郭志猛. 二次自蔓延高温合成SrTiO₃固化高放废物[J]. 稀有金属, 2009,33(1):66.
4 He Yong. Properties of mineral hosts for high-level nuclear waste(HLW)[J]. Geological Sci Technol Inf, 2006,19(3):73(in Chinese).
何涌. 高放射性废物矿物固化体的特性[J]. 地质科技情报, 2006,19(3):73.
5 罗上庚. 放射性废物处置预处理[M]. 北京:中国环境科学出版社, 2007.
6 Ke Changfeng. Fundamental research on vetrification of simulated radioactive waste with Pu[D]. Hefei: National University of Defense Technology, 2006(in Chinese).
柯昌凤. 模拟含Pu放射性废物玻璃固化的基础研究[D]. 合肥:国防科技大学, 2006.
7 Liao Changzhong, Shi Minkai. Immobilization of zironolite-based glass-ceramics and investigation on analogue of actinides[J]. World Nuclear Geoscience, 2014,33(1):65(in Chinese).
廖长忠, 施凯闵. 钙钛锆石基玻璃陶瓷固化锕系核素模拟物的研究[J]. 世界核地质科学, 2014,33(1):65.
8 Jae Han Cho, Yujin Eom,et al. Stablization/solidification of mercury-contaminated waste ash using calcium sodium phosphate (CNP) and magnesium potassium phosphate (MKP) processes[J]. J Hazard Mater, 2014,278:474.
9 Daniel Véras Ribeiro, Marcio Raymundo Morelli. Influence of the addition of grinding dust to a magnesium phosphate cement matrix[J]. Constr Build Mater, 2009,23:3094.
10Irene Buj, Josep Torras, et al. Leaching behaviour of magnesium phosphate cements containing high quantities of heavy metals[J]. J Hazard Mater, 2010,175:789.
11Covill A, Hyatt N C, et al. Development of magnesium phosphate cements for encapsulation of radioactive waste[J]. Adv Appl Ceram, 2011,3:111.
12Singh D, Mandalika V R.Magnesium potassium phosphate ceramic for ⁹⁹Tc immpbilization[J]. J Nucl Mater, 2006,348:272.
13Ma Baoguo, Wang Jingran, et al. Effect of heavy metals and leaching toxicity of magnesium potassium phosphate cement[J]. Appl Mech Mater, 2011,117:1080.
14 Vinokurov S E, Kulyako Y M, et al. Low-temperature immobilization of actinides and other components of high-level waste in magnesium potassium phosphate matrices[J]. J Nuc Mater, 2009,385:189.
15Rehab O. Abdel Rahman. Ravil Z. Rakhimov. Cementitious materials for nuclear waste immobilization[M]. Pondicherry: Spi Publis-her Services, 2014.
16Li Pingguang. Study on solidification technology of simulated radioa-ctive nuclide in borosilicate glass and glass-ceramic systems[D]. Hangzhou: Zhejiang University, 2013(in Chinese).
李平广. 模拟核素的硼硅酸盐玻璃及玻璃陶瓷固化技术研究[D]. 杭州:浙江大学, 2013.
17Lai Zhenyu, Qian Jueshi, et al. Effects of different temperature treatments to properties of magnesium phosphate cement[J]. J Funct Mater, 2015,15(43):2065(in Chinese).
赖振宇, 钱觉时,等. 不同温度处理对磷酸镁水泥性能的影响[J]. 功能材料, 2015,15(43):2065.
18Lai Zhenyu. Immobilization of medium and low level radioactive wastes by magnesium phosphate cement[D]. Chongqing: Chongqing University, 2012(in Chinese).
赖振宇. 磷酸镁水泥固化中低放射性废物研究[D]. 重庆:重庆大学, 2012.
19Huang Chencheng. Solidfication simulated high Level liquid waste by magnesium phosphate cement[D]. Mianyang: Southwest University of Science and Technology, 2016(in Chinese).
黄陈程. 磷酸镁水泥固化模拟高放废液[D]. 绵阳:西南科技大学, 2016.