高吸水树脂对混凝土水化及强度的影响

doi:10.11896/j.issn.1005-023X.2017.024.009

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (1531KB)
Export: BibTeX | EndNote (RIS)

Abstract Super absorbent polymer (SAP) as a kind of internal curing materials can effectively inhibit the autogenous shrinkage and prevent crack formation. However, it remains to be studied whether SAP has a negative impact on concrete. In this paper, the hydration products of paste incorporated by different content of SAP were studied by XRD and DTA-TG, and mechanical properties were tested after standard curing to the different ages. The influence of SAP on hydration and compressive strength of concrete was studied quantificationally. Results indicated that SAP could delay the early hydration on concrete (0—7 d) and the compressive strength of concrete decreased as well. After 7 days curing, the influence of SAP on hydration and compressive strength of concrete was negligible. When the addition of SAP was 1 kg/m³ (the mass percentage of super absorbent polymer in cementitious material was 0.2%) and 1.5 kg/m³ (the mass percentage of super absorbent polymer in cementitious material was 0.3%), the compressive strength of concrete with SAP was 100% and 96% of the concrete without SAP at the age of 28 days. After 56 days curing, the compressive strength of concrete with SAP was 107% and 96% of the concrete without SAP. For C50 concrete, the recommended content of SAP is 1 kg/m³.

Key words： super-absorbent polymer internal curing concrete hydration compressive strength

Published: 08 May 2018

CLC number:

TU528.31

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	JIANG Yudan
	JIN Zuquan
	CHEN Yongfeng
	FAN Junfeng

Cite this article:

JIANG Yudan,JIN Zuquan,CHEN Yongfeng, et al. Effect of Super-absorbent Polymer on Hydration and Compressive Strength of Concrete[J]. Materials Reports, 2017, 31(24): 40-44.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2017.024.009 OR http://www.mater-rep.com/EN/Y2017/V31/I24/40

1 Mezencevova A, Garas V, Nanko H, et al. Influence of thermomechanical pulp fiber compositions on internal curing of cementitious materials[J]. J Mater Civil Eng, 2012,24(8):970.
2 Hou Dongwei, Zhang Jun, Sun Wei. Determination of concrete setting time based on measurements of deformation[J].J Chin Ceram Soc, 2009,37(7):1079(in Chinese).
侯东伟,张君,孙伟.基于早期变形特征的混凝土凝结时间的确定[J].硅酸盐学报,2009,37(7):1079.
3 Zhao Wenjie, Zhang Huixuan, Zhang Baoyan. Properties of PB-g-PSG latex-modified cement mortars[J]. J Building Mater, 2010,13(4):497(in Chinese).
赵文杰,张会轩,张宝砚.PB-g-PSG胶乳改性水泥砂浆性能[J].建筑材料学报,2010,13(4):497.
4 Ding Hongyan, Zhang Lei, Zhang Puyang. Factors influencing strength of super absorbent polymer(SAP) concrete[J]. Trans Tianjin University, 2017,23(3):245.
5 Brüdern A E, Mechtcherine V. Multifunctional use of SAP in strain-hardening cement-based composites[C]∥RILEM Publications SARL. Denmark, 2010:11.
6 Schrfl C, Mechtcherine V, Gorges M. Relation between the molecular structure and the efficiency of superabsorbent polymers (SAP) as concrete admixture to mitigate autogenous shrinkage[J]. Cem Concr Res, 2012,42(6):865.
7 Yao Y, Zhu Y, Yang Y. Incorporation superabsorbent polymer (SAP) particles as controlling pre-existing flaws to improve the performance of engineered cementitious composites (ECC)[J]. Constr Building Mater, 2012,28(1):139.
8 Dudziak L, Mechtcherine V. Enhancing early-age resistance to cracking in high-strength cement-based materials by means of internal curing using super absorbent polymers[J]. Additions Improving Properties Concr, 2010,77:129.
9 Kim J S, Schlangen E.Super absorbent polymers to simulate self healing in ECC[C]∥van Breugel K,Ye G,Yuan Y.2nd International Symposium on Service Life Design for Infrastructure. Delft, 2010:849.
10Bian Xia, Wang Zhifeng, Ding Guoquan, et al. Compressibility of cemented dredged clay at high water content with super-absorbent polymer[J]. Eng Geol, 2016,208:198.
11Lura P, Durand F, Loukili A, et al. Compressive strength of cement pastes and mortars with superabsorbent polymers[C]∥Proceedings of the International RILEM Conference. Denmark, 2006:117.
12Esteves L P. Internal curing in cement-based materials[D]. Portugal: Aveiro University, 2009.
13Pang Lufeng, Ruan Shiye, Cai Yongtao. Effects of internal curing by super absorbent polymer on shrinkage of concrete[J]. Key Eng Mater, 2011,477:200.
14Gaston Espinoza-Hijazin, Mauricio Lopez. Extending internal curing to concrete mixtures with W/C higher than 0.42[J]. Constr Building Mater,2011,25(3):1236.
15Mehta P K, Monteiro P J M. Concrete: Microstructure,properties and materials[M].3rd ed. Mc Graw-Hill, 2006:105.16Piérard J,Pollet V,Cauberg N. Mitigation of autogenous shrinkage in HPC by internal curing using superabsorbent polymers[C]∥International RILEM Conference Onchanges of Hardening Concrete: Testing & Mitigation. Denmark, 2006.
17Jensen O M,Lura P,Kovler K. Volume changes of hardening concrete: Testing and mitigation[C]∥Proceedings of the International RILEM Conference. Denmark, 2006.
18Ma Xinwei, Li Xueying, Jiao Hejun. Experimental research on utilization of super absorbent polymer in cement mortar and concrete[J]. J Wuhan Univ Tech, 2009,31(2):33(in Chinese).
马新伟,李学英,焦贺军.超强吸水聚合物在砂浆与混凝土中的应用研究[J].武汉理工大学学报,2009,31(2):33.
19Wang Kunyan, Cen Rufeng, Shu Wenwen. Preparation and performance of super-absorbent resin using polyacrylonitrile fiber wastes[J]. Adv Mater Res, 2015,1120:498.
20Li Xiangtao. The release and hydration rules of water in water slurry in high absorbent resin base[J]. China Concr Cem Products, 2017,7:1.