新型Mg-8Li-5Al-5Ca合金的微观组织、力学及耐腐蚀性能<sup>*</sup>

doi:10.11896/j.issn.1005-023X.2017.018.014

Abstract
Figure/Table
References
Related Citation (15)

Download:

Full Text ( PDF ) (2798KB)
Export: BibTeX | EndNote (RIS)

Abstract Mg-8Li-5Al-5Ca with high ratio of calcium and aluminum was designed. Its mechanical properties at room temperature and corrosion resistance were studied by the room temperature tensile test, weight loss method, pH tests and electrochemical tests. Also, microstructure and corrosion morphology of the alloy were analyzed by scanning electron microscopy (SEM) and X-ray diffraction (XRD). The results showed that a structure of double matrix (α-Mg+β-Li) surrounded with Al₂Ca phases was formed in the Mg-8Li-5Al-5Ca alloy, and both the matrix and the second phases were obviously refined after hot extrusion. The corrosion resistance was improved compared with that of the common Mg-Li alloys. Coordinating the excellent plasticity of Mg-Li alloys and high strength of the magnesium alloys with high ratio of calcium and aluminum, the Mg-8Li-5Al-5Ca alloy had high tensile strength (222 MPa) and elongation (8.3%).

Key words： Mg-Li alloy hot extrusion mechanical property corrosion resistance Al₂Ca

Published: 08 May 2018

CLC number:

TG146.2+2

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	DONG Peng
	CHEN Ding
	CHEN Zhenhua
	ZHANG Kai

Cite this article:

DONG Peng,CHEN Ding,CHEN Zhenhua, et al. Microstructure, Mechanical Properties and Corrosion Resistance of a Novel Mg-8Li-5Al-5Ca Alloy[J]. Materials Reports, 2017, 31(18): 64-71.

URL:

http://www.mater-rep.com/EN/10.11896/j.issn.1005-023X.2017.018.014 OR http://www.mater-rep.com/EN/Y2017/V31/I18/64

1 Chang T C, Wang J Y, Chu C L, et al. Mechanical properties and microstructures of various Mg-Li alloys[J]. Mater Lett, 2006,60(27):3272.
2 Froes F H, Eliezer D, Aghion E. The science, technology, and applications of magnesium[J]. J Met, 1998,50(9):30.
3 Biatobrzeski A, Saja K, Hubner K. Ultralight magnesium-lithium alloys[J]. Arch Foundry Eng, 2007,7(3):11.
4 Muga C O, Zhang Z W. Strengthening mechanisms of magnesium-lithium based alloys and composites[J]. Adv Mater Sci Eng, 2016,2016:1.
5 Jiang B, Qiu D, Zhang M X, et al. A new approach to grain refinement of an Mg-Li-Al cast alloy[J]. J Alloys Compd, 2010,492(1-2):95.
6 Wu H Y, Lin J Y, Gao Z W, et al. Effects of age heat treatment and thermomechanical processing on microstructure and mechanical behavior of LAZ1010 Mg alloy[J]. Mater Sci Eng A, 2009,523(1-2):7.
7 Saito N, Mabuchi M, Nakanishi M, et al. The aging behavior and the mechanical properties of the Mg-Li-Al-Cu alloy[J]. Scr Mater, 1997,36(5):551.
8 Zhou Y, Bian L, Chen G, et al. Influence of Ca addition on microstructural evolution and mechanical properties of near-eutectic Mg-Li alloys by copper-mold suction casting[J]. J Alloys Compd, 2016,664:85.
9 Ramesh C, Sakai T, Kamado S, et al. Semi-solid forming of Mg-Li-Al-Ca light metal alloys[J]. J Jpn Inst Light Met, 1998,48(1):13.
10Wang T, Wu R, Zhang M, et al. Effects of calcium on the microstructures and tensile properties of Mg-5Li-3Al alloys[J]. Mater Sci Eng A, 2011,528(18):5678.
11Sakamoto M, Akiyama S, Ogi K. Suppression of ignition and bur-ning of molten Mg alloys by Ca bearingstable oxide film[J]. J Mater Sci Lett, 1997,16(12):1048.
12Zeng R, Qi W, Zhang F, et al. In vitro corrosion of Mg-1.21Li-1.12Ca-1Y alloy[J]. Prog Nat Sci: Mater Int, 2014,24(5):492.
13Song G S, Staiger M, Kral M. Some new characteristics of the strengthening phase in β-phase magnesium-lithium alloys containing aluminum and beryllium[J]. Mater Sci Eng A, 2004,371(1-2):371.
14Zeng R C, Sun L, Zheng Y F, et al. Corrosion and characterisation of dual phase Mg-Li-Ca alloy in Hank’s solution: The influence of microstructural features[J]. Corros Sci, 2014,79:69.
15Yang Y, Peng X, Wen H, et al. Microstructure and mechanical behavior of Mg-10Li-3Al-2.5Sr alloy[J]. Mater Sci Eng A, 2014,611:1.
16Phasha M J, Ngoepe P E, Chauke H R, et al. Link between structural and mechanical stability of fcc- and bcc-based ordered Mg-Li alloys[J]. Intermetallics, 2010,18(11):2083.
17Zhou W R, Zheng Y F, Leeflang M A, et al. Mechanical property, biocorrosion and in vitro biocompatibility evaluations of Mg-Li-(Al)-(RE) alloys for future cardiovascular stent application[J]. Acta Biomater, 2013,9(10):8488.
18Zhang L, Deng K K, Nie K B, et al. Microstructures and mechanical properties of Mg-Al-Ca alloys affected by Ca/Al ratio[J]. Mater Sci Eng A, 2015,636:279.
19Yu W Y, Wang N, Xiao X B, et al. First-principles investigation of the binary AB2 type laves phase in Mg-Al-Ca alloy: Electronic structure and elastic properties[J]. Solid State Sci, 2009,11(8):1400.
20Aljarrah M, Medraj M, Wang X, et al. Experimental investigation of the MgAlCa system[J]. J Alloys Compd, 2007,436(1-2):131.
21Hai Binji, Guang Chunyao, Hong Binli. Microstructure, coldro-lling, heat treatment, and mechanical properties of Mg-Li alloys[J]. J Miner Metall Mater, 2008,15(4):440.
22Liu T, Wu S D, Li S X, et al. Microstructure evolution of Mg-14% Li-1% Al alloy during the process of equal channel angular pressing[J]. Mater Sci Eng A, 2007,460-461:499.
23Zhang Y, Zhang J, Wu G, et al. Microstructure and tensile properties of as-extruded Mg-Li-Zn-Gd alloys reinforced with icosahedral quasicrystal phase[J]. Mater Des, 2015,66:162.
24Zhang J, Zhang Y, Wu G, et al. Microstructure and mechanical properties of as-cast and extruded Mg-8Li-3Al-2Zn-0.5Nd alloy[J]. Mater Sci Eng A, 2015,621:198.
25Xiao D, Chen Z, Wang X, et al. Microstructure, mechanical and creep properties of high Ca/Al ratio Mg-Al-Ca alloy[J]. Mater Sci Eng A, 2016,660:166.
26Dong H, Pan F, Jiang B, et al. Evolution of microstructure and mechanical properties of a duplex Mg-Li alloy under extrusion with an increasing ratio[J]. Mater Des, 2014,57:121.
27Gao L, Zhang C, Zhang M, et al. The corrosion of a novel Mg-11Li-3Al-0.5RE alloy in alkaline NaCl solution[J]. J Alloys Compd, 2009,468(1-2):285.
28Brett C M A, Dias L, Trindade B, et al. Characterisation by EIS of ternary Mg alloys synthesised by mechanical alloying[J]. Electrochim Acta, 2006,51(8-9):1752.
29Aung N N, Zhou W. Effect of grain size and twins on corrosion behaviour of AZ31B magnesium alloy[J]. Corros Sci, 2010,52(2):589.
30Song Y, Shan D, Chen R, et al. Corrosion characterization of Mg-8Li alloy in NaCl solution[J]. Corros Sci, 2009,51(5):1087.