低碳贝氏体钢等温淬火变体选择与特殊晶面定量化表征

doi:10.11896/cldb.22100050

Abstract
Figure/Table
References
Related Citation (4)

Download:

Full Text ( PDF ) (12936KB)
Export: BibTeX | EndNote (RIS)

Abstract In order to analyze the influence of variant selection and special crystal plane misorientation distribution of low carbon bainite steel (15Cr12CuSiMoMn) on its mechanical properties, and the correlation between variant selection and crystal plane misorientation, the experimental steel was subjected to isothermal quenching heat treatment at a specified temperature after fully austenitizing, and then the evolution law of variant selection and the distribution law of special crystallographic plane misorientation during isothermal transition were analyzed and characterized. The results show that the {100} standard polar diagram is basically consistent with the {100} polar diagram of the experimental steel. The orientation relationship between the bainite variant and the parent austenite conforms to the K-S relationship. With the increase of isothermal quenching temperature, the bainite transformation rate is accelerated, and the ability of variant selection is reduced. At the same time, the content of HAGBs (45—65°) and LAGBs (2—15°) is decreased. After isothermal quenching for 60 min, it is found that the number of variant pairs V1/V2, V1/V3, V1/V5 in the same CP group increases by 2.4%, 15%, 1.1% in 320 ℃ compared with 340 ℃, and the bainite variant in the same CP group can increase the LAGBs. After isothermal quenching at 320 ℃, the experimental steel has large overall interfacial misorientation, cleavage plane (100) misorientation and slip plane (110) misorientation. The misorientation of the overall plane ranges from 3.2°to 62.5°, the misorientation of the cleavage plane (100) ranges from 6.9° to 47.8°, and the misorientation of the slip plane (110) ranges from 1° to 29.2°. By controlling the distribution and content of bainite variants, which affects the distribution range of the effective cleavage surface orientation difference (100) and the slip surface orientation difference (110), increasing the range of special crystal plane orientation difference is conducive to optimizing the bainite structure.

Key words： bainite steel orientation distribution variant selection orientation difference

Published: 10 May 2024 Online: 2024-05-13

CLC number:

TG142.1

Fund:National Natural Science Foundation of China (51764047).

	Service
	E-mail this article
	Add to my bookshelf
	Add to citation manager
	E-mail Alert
	RSS
	Articles by authors
	YANG Jie
	REN Huiping
	WANG Haiyan
	GAO Xueyun
	LIU Zongchang

Cite this article:

YANG Jie,REN Huiping,WANG Haiyan, et al. Selection of Isothermal Quenching Variants and Quantitative Characterization of Special Crystal Faces of Low Carbon Bainite Steels[J]. Materials Reports, 2024, 38(9): 22100050-8.

URL:

http://www.mater-rep.com/EN/10.11896/cldb.22100050 OR http://www.mater-rep.com/EN/Y2024/V38/I9/22100050

1 Furuhara T, Kawata H, Morito S, et al. Metallurgical and Materials Transactions, 2008, 39(5), 1003.
2 Kim M C, Yong J O, Hong J H. Scripta Materialia, 2000, 43(3), 205.
3 Hwang B, Yang G K, Lee S, et al. Metallurgical & Materials Transactions A, 2005, 36(8), 2107.
4 Lambert A, Garat X, Sturel T, et al. Scripta Materialia, 2000, 43(2), 161.
5 You Y, Shang C, Nie W, et al. Materials Science & Engineering A, 2012, 558(15), 692.
6 Li X, Ma X, Subramanian S V, et al. Materials Science and Engineering A, 2014, 36(8), 2107.
7 Flower H M, Lindley T C. Metal Science Journal, 2000, 16(1), 26.
8 Morris J W, Lee C S, Guo Z. Transactions of the Iron & Steel Institute of Japan, 2007, 43(3), 410.
9 Terentyev D, Gao F. Materials Science and Engineering A, 2013, 12(3), 125.
10 Hiromoto, Kitahara. Acta Materialia, 2006, 54(5), 1279.
11 Kurdjumow G V, Sachs G. Zeitschrift für Physik A Hadrons and Nuclei, 1930, 64(5), 325.
12 Luo C P, Weatherly G C, Liu Z Y. Metallurgical Transactions A, 1992, 43(3), 410.
13 Furuhara N. Acta Materialia, 2012, 53(5), 1279.
14 Stormvinter A, Miyamoto G, Furuhara T, et al. Acta Materialia, 2012, 60(20), 7265.
15 Titahara R. Acta Materialia, 2005, 34(4), 179.
16 Terentyev D. Acta Materialia, 2012, 43(3), 409.
17 Guo Z, Lee C S, Morris J W. Acta Materialia, 2004, 52(19), 5511.
18 Kaneshita T, Miyamoto G, Furuhara T. Acta Materialia, 2017, 27(11), 368.
19 Liu S, Li X, Guo H, et al. Philosophical Magazine, 2018, 22(15), 25.
20 Li X C, Sun M Y, Zhao J X, et al. Acta Metallurgica Sinica, 2020, 56(4), 8 (in Chinese).
李秀程, 孙明煜, 赵靖霄, 等. 金属学报, 2020, 56(4), 8.
21 Guo H, Gao X, Bai Y, et al. Materials Characterization, 2012, 67, 34.
22 Wu J, Zhang W Z. Acta Metallurgica Sinica, 2009, 45(8), 9 (in Chinese).
吴静, 张文征. 金属学报, 2009, 45(8), 9.
23 Kamaya M, Joao Q, Li L M, et al. Applied Mechanics & Materials, 2012, 7(8), 173.
24 Fu W, Song X, Long L, et al. Acta Metallurgica Sinica, 2016, 22(15), 25.
25 Yuan J H, Zhang Q H, Wang J L, et al. Acta Metallurgica Sinica, 2020, 58(12), 15 (in Chinese).
原家华, 张秋红, 王金亮, 等. 金属学报, 2020, 58(12), 15.
26 Gao D, Zhou Y, Yu Z, et al. Acta Metallurgica Sinica, 2022, 58(9), 141 (in Chinese).
高栋, 周宇, 于泽,等. 金属学报, 2022, 58(9), 141.